- W4285604367 abstract "Biochar (BC) is a good adsorbent with high porosity, high specific surface area, and abundant functional groups. However, it exhibits poor phosphate (P) adsorption due to its negative surface charge. Metal (hydr)oxide modification is an effective approach to promote P sorption on biochar. Hence, Ca/Zn composite (CaCO3/ZnO) loaded biochar ([email protected]+Zn) derived from orange peel was prepared through precipitation of Zn2+/Ca2+ on the surface of orange peel followed by carbonization at 700 °C. SEM-EDS, FTIR, XRD, BET, and XPS were used to characterize the biochar before and after modification. The results demonstrated that CaCO3/ZnO were uniformly loaded on the surface of biochar. More reactive sites and oxygen-containing groups were observed on biochar after decoration, which significantly enhanced P sorption. An optimal adsorption capacity was achieved with a metal loading of 3 mM/g. [email protected]+Zn exhibited the best P adsorption efficiency compared to [email protected] and [email protected] The maximum adsorption capacity of [email protected]+Zn was 52.96 mg/g, which was 8-fold higher compared with raw BC. The adsorption kinetics and isotherm were fitted better with the pseudo-second-order and Langmuir isotherm models, respectively. The effect of coexisting anions (Cl-, NO3-, SO42-) on P sorption by [email protected]+Zn was negligible, whereas humic acid significantly inhibited P adsorption. Phosphate was adsorbed by carbonyl, hydroxyl, and other oxygen-containing functional groups on the surface of [email protected]+Zn. This study suggests that Ca/Zn modified biochar can effectively improve the P adsorption capacity for potential applications." @default.
- W4285604367 created "2022-07-16" @default.
- W4285604367 creator A5001206877 @default.
- W4285604367 creator A5013895300 @default.
- W4285604367 creator A5015399496 @default.
- W4285604367 creator A5026660382 @default.
- W4285604367 creator A5036822304 @default.
- W4285604367 creator A5046289405 @default.
- W4285604367 creator A5087990397 @default.
- W4285604367 date "2022-10-01" @default.
- W4285604367 modified "2023-10-16" @default.
- W4285604367 title "Enhanced adsorption of phosphate on orange peel-based biochar activated by Ca/Zn composite: Adsorption efficiency and mechanisms" @default.
- W4285604367 cites W1960263738 @default.
- W4285604367 cites W1983646727 @default.
- W4285604367 cites W1995157209 @default.
- W4285604367 cites W2011141753 @default.
- W4285604367 cites W2025515113 @default.
- W4285604367 cites W2040152771 @default.
- W4285604367 cites W2052476780 @default.
- W4285604367 cites W2079647236 @default.
- W4285604367 cites W2082689761 @default.
- W4285604367 cites W2086047095 @default.
- W4285604367 cites W2110081460 @default.
- W4285604367 cites W2125672123 @default.
- W4285604367 cites W2301299565 @default.
- W4285604367 cites W2463156617 @default.
- W4285604367 cites W2501691238 @default.
- W4285604367 cites W2569659974 @default.
- W4285604367 cites W2574098941 @default.
- W4285604367 cites W2625410841 @default.
- W4285604367 cites W2740235545 @default.
- W4285604367 cites W2757188414 @default.
- W4285604367 cites W2762845959 @default.
- W4285604367 cites W2767966419 @default.
- W4285604367 cites W2768319605 @default.
- W4285604367 cites W2779670937 @default.
- W4285604367 cites W2780096618 @default.
- W4285604367 cites W2789181942 @default.
- W4285604367 cites W2789940574 @default.
- W4285604367 cites W2791222045 @default.
- W4285604367 cites W2799542964 @default.
- W4285604367 cites W2801239808 @default.
- W4285604367 cites W2801717853 @default.
- W4285604367 cites W2892796381 @default.
- W4285604367 cites W2900936310 @default.
- W4285604367 cites W2902587499 @default.
- W4285604367 cites W2910096196 @default.
- W4285604367 cites W2945083327 @default.
- W4285604367 cites W2963970157 @default.
- W4285604367 cites W2965820903 @default.
- W4285604367 cites W2969908860 @default.
- W4285604367 cites W2980663784 @default.
- W4285604367 cites W3002221073 @default.
- W4285604367 cites W3007325236 @default.
- W4285604367 cites W3010549838 @default.
- W4285604367 cites W3016532478 @default.
- W4285604367 cites W3019788844 @default.
- W4285604367 cites W3024790350 @default.
- W4285604367 cites W3084840984 @default.
- W4285604367 cites W3094132164 @default.
- W4285604367 cites W3113448160 @default.
- W4285604367 cites W3129900048 @default.
- W4285604367 cites W3132886849 @default.
- W4285604367 cites W3133553859 @default.
- W4285604367 cites W3141319804 @default.
- W4285604367 cites W3174561846 @default.
- W4285604367 cites W3178591551 @default.
- W4285604367 cites W3182462941 @default.
- W4285604367 cites W3191497863 @default.
- W4285604367 cites W3197782128 @default.
- W4285604367 cites W3202160534 @default.
- W4285604367 cites W4211212668 @default.
- W4285604367 doi "https://doi.org/10.1016/j.colsurfa.2022.129728" @default.
- W4285604367 hasPublicationYear "2022" @default.
- W4285604367 type Work @default.
- W4285604367 citedByCount "15" @default.
- W4285604367 countsByYear W42856043672022 @default.
- W4285604367 countsByYear W42856043672023 @default.
- W4285604367 crossrefType "journal-article" @default.
- W4285604367 hasAuthorship W4285604367A5001206877 @default.
- W4285604367 hasAuthorship W4285604367A5013895300 @default.
- W4285604367 hasAuthorship W4285604367A5015399496 @default.
- W4285604367 hasAuthorship W4285604367A5026660382 @default.
- W4285604367 hasAuthorship W4285604367A5036822304 @default.
- W4285604367 hasAuthorship W4285604367A5046289405 @default.
- W4285604367 hasAuthorship W4285604367A5087990397 @default.
- W4285604367 hasConcept C12143843 @default.
- W4285604367 hasConcept C127413603 @default.
- W4285604367 hasConcept C13965031 @default.
- W4285604367 hasConcept C150394285 @default.
- W4285604367 hasConcept C150581940 @default.
- W4285604367 hasConcept C154877778 @default.
- W4285604367 hasConcept C160892712 @default.
- W4285604367 hasConcept C161790260 @default.
- W4285604367 hasConcept C178790620 @default.
- W4285604367 hasConcept C179104552 @default.
- W4285604367 hasConcept C185592680 @default.
- W4285604367 hasConcept C2777132085 @default.