- W4289779189 abstract "The MgAl2O4 transparent ceramic was firstly flash joined in 3 min at 1500 °C by applying direct current (DC) electric field. Three-point flexural strength of the joints reached approximately 256.0 MPa, which was even 114.7% of that of the parent material. Compared with parent transparent ceramics, transmittance loss of the MgAl2O4/MgAl2O4 joints in band of visual light and mid-infrared was only 1.5% and 4.5%, respectively. A possible mechanism of flash joining was proposed. The applied DC electric field induces numerous charged defects in the sample and superplastic deformation of the ceramic. The defects generated at the pores of the joining interface migrate directionally under the action of the DC electric field, which accelerates the diffusion rate of substances and enables the samples to be quickly jointed at a lower temperature." @default.
- W4289779189 created "2022-08-04" @default.
- W4289779189 creator A5002301863 @default.
- W4289779189 creator A5007152038 @default.
- W4289779189 creator A5016473049 @default.
- W4289779189 creator A5021293751 @default.
- W4289779189 creator A5038032242 @default.
- W4289779189 creator A5054395471 @default.
- W4289779189 creator A5055532979 @default.
- W4289779189 creator A5055623794 @default.
- W4289779189 date "2022-11-01" @default.
- W4289779189 modified "2023-10-16" @default.
- W4289779189 title "High-performance flash joining of MgAl2O4 transparent ceramics" @default.
- W4289779189 cites W1969820107 @default.
- W4289779189 cites W1982908692 @default.
- W4289779189 cites W1999371203 @default.
- W4289779189 cites W2002585311 @default.
- W4289779189 cites W2008386626 @default.
- W4289779189 cites W2019796639 @default.
- W4289779189 cites W2032414716 @default.
- W4289779189 cites W2048901051 @default.
- W4289779189 cites W2063377576 @default.
- W4289779189 cites W2106402228 @default.
- W4289779189 cites W2109436818 @default.
- W4289779189 cites W2111274076 @default.
- W4289779189 cites W2130830226 @default.
- W4289779189 cites W2147386419 @default.
- W4289779189 cites W2221308948 @default.
- W4289779189 cites W2591656073 @default.
- W4289779189 cites W2804564253 @default.
- W4289779189 cites W2898327466 @default.
- W4289779189 cites W2913759429 @default.
- W4289779189 cites W2940302851 @default.
- W4289779189 cites W2962944812 @default.
- W4289779189 cites W2997353656 @default.
- W4289779189 cites W3104440326 @default.
- W4289779189 cites W3178469447 @default.
- W4289779189 cites W3183188187 @default.
- W4289779189 cites W3194274509 @default.
- W4289779189 cites W3195927161 @default.
- W4289779189 cites W4206137169 @default.
- W4289779189 cites W4210283517 @default.
- W4289779189 cites W4213457737 @default.
- W4289779189 cites W4233086737 @default.
- W4289779189 doi "https://doi.org/10.1016/j.ceramint.2022.07.336" @default.
- W4289779189 hasPublicationYear "2022" @default.
- W4289779189 type Work @default.
- W4289779189 citedByCount "4" @default.
- W4289779189 countsByYear W42897791892023 @default.
- W4289779189 crossrefType "journal-article" @default.
- W4289779189 hasAuthorship W4289779189A5002301863 @default.
- W4289779189 hasAuthorship W4289779189A5007152038 @default.
- W4289779189 hasAuthorship W4289779189A5016473049 @default.
- W4289779189 hasAuthorship W4289779189A5021293751 @default.
- W4289779189 hasAuthorship W4289779189A5038032242 @default.
- W4289779189 hasAuthorship W4289779189A5054395471 @default.
- W4289779189 hasAuthorship W4289779189A5055532979 @default.
- W4289779189 hasAuthorship W4289779189A5055623794 @default.
- W4289779189 hasConcept C120665830 @default.
- W4289779189 hasConcept C121332964 @default.
- W4289779189 hasConcept C134132462 @default.
- W4289779189 hasConcept C150493377 @default.
- W4289779189 hasConcept C159985019 @default.
- W4289779189 hasConcept C175997439 @default.
- W4289779189 hasConcept C178405089 @default.
- W4289779189 hasConcept C192562407 @default.
- W4289779189 hasConcept C2777526259 @default.
- W4289779189 hasConcept C49040817 @default.
- W4289779189 hasConcept C60799052 @default.
- W4289779189 hasConcept C62520636 @default.
- W4289779189 hasConcept C87976508 @default.
- W4289779189 hasConceptScore W4289779189C120665830 @default.
- W4289779189 hasConceptScore W4289779189C121332964 @default.
- W4289779189 hasConceptScore W4289779189C134132462 @default.
- W4289779189 hasConceptScore W4289779189C150493377 @default.
- W4289779189 hasConceptScore W4289779189C159985019 @default.
- W4289779189 hasConceptScore W4289779189C175997439 @default.
- W4289779189 hasConceptScore W4289779189C178405089 @default.
- W4289779189 hasConceptScore W4289779189C192562407 @default.
- W4289779189 hasConceptScore W4289779189C2777526259 @default.
- W4289779189 hasConceptScore W4289779189C49040817 @default.
- W4289779189 hasConceptScore W4289779189C60799052 @default.
- W4289779189 hasConceptScore W4289779189C62520636 @default.
- W4289779189 hasConceptScore W4289779189C87976508 @default.
- W4289779189 hasFunder F4320321001 @default.
- W4289779189 hasIssue "21" @default.
- W4289779189 hasLocation W42897791891 @default.
- W4289779189 hasOpenAccess W4289779189 @default.
- W4289779189 hasPrimaryLocation W42897791891 @default.
- W4289779189 hasRelatedWork W1541487397 @default.
- W4289779189 hasRelatedWork W1569674102 @default.
- W4289779189 hasRelatedWork W1998055541 @default.
- W4289779189 hasRelatedWork W2048627952 @default.
- W4289779189 hasRelatedWork W2233763142 @default.
- W4289779189 hasRelatedWork W2240769545 @default.
- W4289779189 hasRelatedWork W2273114028 @default.
- W4289779189 hasRelatedWork W2363521449 @default.
- W4289779189 hasRelatedWork W2380600486 @default.