- W4290791563 abstract "A gradient microstructure was successfully fabricated by high-frequency induction quenching treatment (HFIQT) to improve the mechanical behavior of Ti-6Al-4V alloy in this work. Microstructural evolution was systematically characterized by electron backscattered diffraction and transmission electron microscopy. The results showed that the gradient microstructure of the alloy after HFIQT and aging varied from a fine αs lamellae decomposed from α′-martensite at the surface layer to a bimodal microstructure at the center. Moreover, the alloy with gradient microstructure presents an optimal strength-ductility synergy. The tensile test results showed that a best strength plastic product UT of 12433.1 MPa·%, an ultimate strength of 1231 MPa and an elongation of 10.1 % were obtained after HFIQT for 5.2 s and aging at 400 °C for 6 h. The tensile strength of the alloy aged at 400 °C markedly increased with the increase in soaking time from 5.1 to 5.3 s during HFIQT. Meanwhile, the tensile strength of the alloy slightly increased with the decrease in aging temperature from 550 to 400 °C during HFIQT. Surprisingly, the elongation of the alloy also increased with decreasing aging temperature. The effects of the gradient microstructure characteristic on strength and ductility of the Ti-6Al-4V alloy were discussed." @default.
- W4290791563 created "2022-08-09" @default.
- W4290791563 creator A5006012404 @default.
- W4290791563 creator A5006714730 @default.
- W4290791563 creator A5046348806 @default.
- W4290791563 creator A5054204107 @default.
- W4290791563 creator A5061194150 @default.
- W4290791563 creator A5072075595 @default.
- W4290791563 creator A5075824768 @default.
- W4290791563 creator A5087925835 @default.
- W4290791563 date "2022-10-01" @default.
- W4290791563 modified "2023-10-18" @default.
- W4290791563 title "Gradient microstructure and mechanical properties of Ti-6Al-4V titanium alloy fabricated by high-frequency induction quenching treatment" @default.
- W4290791563 cites W1021166515 @default.
- W4290791563 cites W1176749318 @default.
- W4290791563 cites W1967368658 @default.
- W4290791563 cites W1970117376 @default.
- W4290791563 cites W1987738131 @default.
- W4290791563 cites W1998012323 @default.
- W4290791563 cites W2009393552 @default.
- W4290791563 cites W2009691576 @default.
- W4290791563 cites W2023758491 @default.
- W4290791563 cites W2023930568 @default.
- W4290791563 cites W2029031285 @default.
- W4290791563 cites W2037086916 @default.
- W4290791563 cites W2047660260 @default.
- W4290791563 cites W2053015403 @default.
- W4290791563 cites W2065589878 @default.
- W4290791563 cites W2073420256 @default.
- W4290791563 cites W2077229196 @default.
- W4290791563 cites W2086879456 @default.
- W4290791563 cites W2207044233 @default.
- W4290791563 cites W2239749925 @default.
- W4290791563 cites W2321217820 @default.
- W4290791563 cites W2342354447 @default.
- W4290791563 cites W2398544446 @default.
- W4290791563 cites W2511884523 @default.
- W4290791563 cites W2521248220 @default.
- W4290791563 cites W2601358472 @default.
- W4290791563 cites W2604290490 @default.
- W4290791563 cites W2775739240 @default.
- W4290791563 cites W2789536787 @default.
- W4290791563 cites W2801816695 @default.
- W4290791563 cites W2805223791 @default.
- W4290791563 cites W285475345 @default.
- W4290791563 cites W2887014377 @default.
- W4290791563 cites W2889279091 @default.
- W4290791563 cites W2897833039 @default.
- W4290791563 cites W2898115957 @default.
- W4290791563 cites W2899449085 @default.
- W4290791563 cites W2955469632 @default.
- W4290791563 cites W2966699005 @default.
- W4290791563 cites W3003730102 @default.
- W4290791563 cites W3008921653 @default.
- W4290791563 cites W3011038397 @default.
- W4290791563 cites W3152706570 @default.
- W4290791563 cites W3156556109 @default.
- W4290791563 cites W3188827976 @default.
- W4290791563 cites W3211478594 @default.
- W4290791563 cites W772773729 @default.
- W4290791563 doi "https://doi.org/10.1016/j.matdes.2022.111031" @default.
- W4290791563 hasPublicationYear "2022" @default.
- W4290791563 type Work @default.
- W4290791563 citedByCount "13" @default.
- W4290791563 countsByYear W42907915632023 @default.
- W4290791563 crossrefType "journal-article" @default.
- W4290791563 hasAuthorship W4290791563A5006012404 @default.
- W4290791563 hasAuthorship W4290791563A5006714730 @default.
- W4290791563 hasAuthorship W4290791563A5046348806 @default.
- W4290791563 hasAuthorship W4290791563A5054204107 @default.
- W4290791563 hasAuthorship W4290791563A5061194150 @default.
- W4290791563 hasAuthorship W4290791563A5072075595 @default.
- W4290791563 hasAuthorship W4290791563A5075824768 @default.
- W4290791563 hasAuthorship W4290791563A5087925835 @default.
- W4290791563 hasBestOaLocation W42907915631 @default.
- W4290791563 hasConcept C112950240 @default.
- W4290791563 hasConcept C120665830 @default.
- W4290791563 hasConcept C121332964 @default.
- W4290791563 hasConcept C121745418 @default.
- W4290791563 hasConcept C149912024 @default.
- W4290791563 hasConcept C159985019 @default.
- W4290791563 hasConcept C182508753 @default.
- W4290791563 hasConcept C18747287 @default.
- W4290791563 hasConcept C191897082 @default.
- W4290791563 hasConcept C192562407 @default.
- W4290791563 hasConcept C2776512210 @default.
- W4290791563 hasConcept C2780026712 @default.
- W4290791563 hasConcept C33947775 @default.
- W4290791563 hasConcept C87976508 @default.
- W4290791563 hasConcept C8953137 @default.
- W4290791563 hasConcept C91881484 @default.
- W4290791563 hasConceptScore W4290791563C112950240 @default.
- W4290791563 hasConceptScore W4290791563C120665830 @default.
- W4290791563 hasConceptScore W4290791563C121332964 @default.
- W4290791563 hasConceptScore W4290791563C121745418 @default.
- W4290791563 hasConceptScore W4290791563C149912024 @default.
- W4290791563 hasConceptScore W4290791563C159985019 @default.
- W4290791563 hasConceptScore W4290791563C182508753 @default.