- W4291474953 abstract "This paper investigates the long-term bond-slip behavior of GFRP (glass fiber reinforced polymer)-RC (reinforced concrete) beams. The specimens used in the bond test have been exposed to alkaline accelerated corrosion solution for eight years. In order to more accurately explore the long-term degradation law of the GFRP-RC beam, the factors of sustained load, pre-crack, and specimen form are also considered in this test. The experimental results show that the long-term degradation efficiency of specimens with pre-cracks increases significantly. The interfacial fracture energy and maximum bond strength at fracture failure are reduced by 16% and 23%, respectively. Although the overall bond performance of GFRP-RC beams will deteriorate with service time, the structure usually enters the slow degradation stage. However, the pre-cracks inhibit the arrival of this stage so that the structure will suffer more damage. In order to more intuitively evaluate the safety level of the residual bond performance of the structure in the current state, the long-term degradation prediction model of the GFRP-RC beam is established." @default.
- W4291474953 created "2022-08-15" @default.
- W4291474953 creator A5013209253 @default.
- W4291474953 creator A5075774517 @default.
- W4291474953 creator A5077173966 @default.
- W4291474953 creator A5082205190 @default.
- W4291474953 creator A5086628488 @default.
- W4291474953 date "2022-11-01" @default.
- W4291474953 modified "2023-10-15" @default.
- W4291474953 title "Long-term bond degradation of GFRP-RC beams in the complex alkaline environment for eight years" @default.
- W4291474953 cites W1974168070 @default.
- W4291474953 cites W1983588933 @default.
- W4291474953 cites W1994997039 @default.
- W4291474953 cites W2000338009 @default.
- W4291474953 cites W2009907171 @default.
- W4291474953 cites W2012869039 @default.
- W4291474953 cites W2030856138 @default.
- W4291474953 cites W2034795003 @default.
- W4291474953 cites W2035193434 @default.
- W4291474953 cites W2045419286 @default.
- W4291474953 cites W2045576355 @default.
- W4291474953 cites W2080961374 @default.
- W4291474953 cites W2128922706 @default.
- W4291474953 cites W2133748244 @default.
- W4291474953 cites W2138492593 @default.
- W4291474953 cites W2155282489 @default.
- W4291474953 cites W2170752975 @default.
- W4291474953 cites W2188785641 @default.
- W4291474953 cites W2199135787 @default.
- W4291474953 cites W2520070600 @default.
- W4291474953 cites W2548259308 @default.
- W4291474953 cites W2549286995 @default.
- W4291474953 cites W2550873431 @default.
- W4291474953 cites W2556012586 @default.
- W4291474953 cites W2557319389 @default.
- W4291474953 cites W2592517399 @default.
- W4291474953 cites W2593991188 @default.
- W4291474953 cites W2613584371 @default.
- W4291474953 cites W2729651844 @default.
- W4291474953 cites W2759989277 @default.
- W4291474953 cites W2799944608 @default.
- W4291474953 cites W3005478118 @default.
- W4291474953 cites W3011738532 @default.
- W4291474953 cites W3025984476 @default.
- W4291474953 cites W3044181836 @default.
- W4291474953 cites W3046730783 @default.
- W4291474953 cites W3174104068 @default.
- W4291474953 cites W3174749079 @default.
- W4291474953 cites W3213967961 @default.
- W4291474953 cites W4205901864 @default.
- W4291474953 doi "https://doi.org/10.1016/j.compstruct.2022.116093" @default.
- W4291474953 hasPublicationYear "2022" @default.
- W4291474953 type Work @default.
- W4291474953 citedByCount "5" @default.
- W4291474953 countsByYear W42914749532023 @default.
- W4291474953 crossrefType "journal-article" @default.
- W4291474953 hasAuthorship W4291474953A5013209253 @default.
- W4291474953 hasAuthorship W4291474953A5075774517 @default.
- W4291474953 hasAuthorship W4291474953A5077173966 @default.
- W4291474953 hasAuthorship W4291474953A5082205190 @default.
- W4291474953 hasAuthorship W4291474953A5086628488 @default.
- W4291474953 hasConcept C127413603 @default.
- W4291474953 hasConcept C159096172 @default.
- W4291474953 hasConcept C159985019 @default.
- W4291474953 hasConcept C168834538 @default.
- W4291474953 hasConcept C192562407 @default.
- W4291474953 hasConcept C20625102 @default.
- W4291474953 hasConcept C24326235 @default.
- W4291474953 hasConcept C2779227376 @default.
- W4291474953 hasConcept C2779679103 @default.
- W4291474953 hasConcept C2988805333 @default.
- W4291474953 hasConcept C66938386 @default.
- W4291474953 hasConcept C68928338 @default.
- W4291474953 hasConcept C76344452 @default.
- W4291474953 hasConceptScore W4291474953C127413603 @default.
- W4291474953 hasConceptScore W4291474953C159096172 @default.
- W4291474953 hasConceptScore W4291474953C159985019 @default.
- W4291474953 hasConceptScore W4291474953C168834538 @default.
- W4291474953 hasConceptScore W4291474953C192562407 @default.
- W4291474953 hasConceptScore W4291474953C20625102 @default.
- W4291474953 hasConceptScore W4291474953C24326235 @default.
- W4291474953 hasConceptScore W4291474953C2779227376 @default.
- W4291474953 hasConceptScore W4291474953C2779679103 @default.
- W4291474953 hasConceptScore W4291474953C2988805333 @default.
- W4291474953 hasConceptScore W4291474953C66938386 @default.
- W4291474953 hasConceptScore W4291474953C68928338 @default.
- W4291474953 hasConceptScore W4291474953C76344452 @default.
- W4291474953 hasLocation W42914749531 @default.
- W4291474953 hasOpenAccess W4291474953 @default.
- W4291474953 hasPrimaryLocation W42914749531 @default.
- W4291474953 hasRelatedWork W105740944 @default.
- W4291474953 hasRelatedWork W1660000150 @default.
- W4291474953 hasRelatedWork W2011905704 @default.
- W4291474953 hasRelatedWork W2036435068 @default.
- W4291474953 hasRelatedWork W2210605124 @default.
- W4291474953 hasRelatedWork W2212956779 @default.
- W4291474953 hasRelatedWork W2891205209 @default.
- W4291474953 hasRelatedWork W3141684830 @default.