• W4294190369 abstract "The photoelectrochemical cathodic characteristics of amorphous and nanorod ZnO thin-film coatings on stainless steel AISI 304 (SS304) substrates were investigated. An amorphous ZnO thin film was coated on a SS304 substrate at 200 °C using the spray pyrolysis technique. A nanorod ZnO thin film was coated on a SS304 substrate by spraying seed layers at 400 °C and growing the nanorod structures with a hydrothermal process. The results from x-ray diffractometry and energy dispersive x-ray spectroscopy confirmed amorphous and nanorod ZnO coatings. The ZnO-coated SS304 samples were subjected to the potentiostatic polarization testing under dark and UV conditions, with the ZnO-coated sides of SS304 immersed in a 0.1 M Na 2 S + 0.2 M NaOH solution and the opposite bare sides in a 3 wt% NaCl solution. For both amorphous and nanorod ZnO coatings, the current densities (i corr ) were increased while the voltages (V corr ) were decreased with the UV light exposure. The photoelecrochemical cathodic mechanism has been explained with the photogenerated electron-hole pairs in ZnO, the hole consumption by the S/S −2 redox reaction, and the electron transfer to SS304. The microstructure analyses showed that the pitted areas resulting from the polarization test under UV light were clearly smaller than those from the polarization test under dark condition. • Amorphous and nanorod ZnO films were coated SS304 by spray pyrolysis and hydrothermal. • The photocathodic protection (PCP) of direct ZnO coatings on SS304 was demonstrated. • The UV illumination reduced V corr (cathodic shift) and increased I corr of the ZnO-coated SS304. • The amorphous ZnO exhibited better PCP performance than the nanorod ZnO one. • The PCP is explained with the photogenerated electron-hole pairs and the EHP separation." @default.
• W4294190369 created "2022-09-02" @default.
• W4294190369 creator A5007622168 @default.
• W4294190369 creator A5052638799 @default.
• W4294190369 creator A5057428285 @default.
• W4294190369 creator A5057511320 @default.
• W4294190369 creator A5063785832 @default.
• W4294190369 date "2022-11-01" @default.
• W4294190369 modified "2023-09-24" @default.
• W4294190369 title "Photocathodic protection of amorphous and nanorod zinc oxide thin-film coatings on stainless steel AISI 304 fabricated by spray pyrolysis and hydrothermal technique" @default.
• W4294190369 cites W1507245776 @default.
• W4294190369 cites W1523850894 @default.
• W4294190369 cites W1963946054 @default.
• W4294190369 cites W1976383708 @default.
• W4294190369 cites W1988324782 @default.
• W4294190369 cites W1988371753 @default.
• W4294190369 cites W1991172431 @default.
• W4294190369 cites W1992040550 @default.
• W4294190369 cites W1997907374 @default.
• W4294190369 cites W2028092571 @default.
• W4294190369 cites W2042160287 @default.
• W4294190369 cites W2042688094 @default.
• W4294190369 cites W2045327192 @default.
• W4294190369 cites W2055702303 @default.
• W4294190369 cites W2063735659 @default.
• W4294190369 cites W2064549946 @default.
• W4294190369 cites W2067333026 @default.
• W4294190369 cites W2076086760 @default.
• W4294190369 cites W2076175532 @default.
• W4294190369 cites W2079407258 @default.
• W4294190369 cites W2082086005 @default.
• W4294190369 cites W2084863137 @default.
• W4294190369 cites W2086658033 @default.
• W4294190369 cites W2091255461 @default.
• W4294190369 cites W2099818819 @default.
• W4294190369 cites W2162521739 @default.
• W4294190369 cites W2199359916 @default.
• W4294190369 cites W2332687001 @default.
• W4294190369 cites W2492301684 @default.
• W4294190369 cites W2580111607 @default.
• W4294190369 cites W2587864500 @default.
• W4294190369 cites W2700981144 @default.
• W4294190369 cites W2738396933 @default.
• W4294190369 cites W2780231153 @default.
• W4294190369 cites W2799895411 @default.
• W4294190369 cites W2905530700 @default.
• W4294190369 cites W2951323691 @default.
• W4294190369 cites W3035011355 @default.
• W4294190369 cites W3040807314 @default.
• W4294190369 cites W648618641 @default.
• W4294190369 cites W900225628 @default.
• W4294190369 cites W991368043 @default.
• W4294190369 doi "https://doi.org/10.1016/j.matchemphys.2022.126714" @default.
• W4294190369 hasPublicationYear "2022" @default.
• W4294190369 type Work @default.
• W4294190369 citedByCount "0" @default.
• W4294190369 crossrefType "journal-article" @default.
• W4294190369 hasAuthorship W4294190369A5007622168 @default.
• W4294190369 hasAuthorship W4294190369A5052638799 @default.
• W4294190369 hasAuthorship W4294190369A5057428285 @default.
• W4294190369 hasAuthorship W4294190369A5057511320 @default.
• W4294190369 hasAuthorship W4294190369A5063785832 @default.
• W4294190369 hasConcept C126201875 @default.
• W4294190369 hasConcept C127413603 @default.
• W4294190369 hasConcept C156622251 @default.
• W4294190369 hasConcept C171250308 @default.
• W4294190369 hasConcept C178790620 @default.
• W4294190369 hasConcept C185592680 @default.
• W4294190369 hasConcept C19067145 @default.
• W4294190369 hasConcept C191897082 @default.
• W4294190369 hasConcept C192562407 @default.
• W4294190369 hasConcept C2779851234 @default.
• W4294190369 hasConcept C2988664670 @default.
• W4294190369 hasConcept C36759035 @default.
• W4294190369 hasConcept C42360764 @default.
• W4294190369 hasConcept C535196362 @default.
• W4294190369 hasConcept C56052488 @default.
• W4294190369 hasConceptScore W4294190369C126201875 @default.
• W4294190369 hasConceptScore W4294190369C127413603 @default.
• W4294190369 hasConceptScore W4294190369C156622251 @default.
• W4294190369 hasConceptScore W4294190369C171250308 @default.
• W4294190369 hasConceptScore W4294190369C178790620 @default.
• W4294190369 hasConceptScore W4294190369C185592680 @default.
• W4294190369 hasConceptScore W4294190369C19067145 @default.
• W4294190369 hasConceptScore W4294190369C191897082 @default.
• W4294190369 hasConceptScore W4294190369C192562407 @default.
• W4294190369 hasConceptScore W4294190369C2779851234 @default.
• W4294190369 hasConceptScore W4294190369C2988664670 @default.
• W4294190369 hasConceptScore W4294190369C36759035 @default.
• W4294190369 hasConceptScore W4294190369C42360764 @default.
• W4294190369 hasConceptScore W4294190369C535196362 @default.
• W4294190369 hasConceptScore W4294190369C56052488 @default.
• W4294190369 hasFunder F4320322722 @default.
• W4294190369 hasFunder F4320335038 @default.
• W4294190369 hasLocation W42941903691 @default.
• W4294190369 hasOpenAccess W4294190369 @default.
• W4294190369 hasPrimaryLocation W42941903691 @default.
• W4294190369 hasRelatedWork W2008147986 @default.

• next