- W4304943312 abstract "Cr/Cr Al N films were chosen as an interlayer to deposit an adherent diamond film on stainless steels by using hot filament chemical vapor deposition (HFCVD). The results show that diamond film with good adhesion is successfully deposited on 3Cr13 stainless steel when the interlayer with Al content from 0 to 18 at.%, which is ascribed to high chemical adhesion by a certain amount of chromium carbide . When Al content in the interlayer further increases, an excessive Al 2 O 3 is formed on the surface of the interlayer, carbon supersaturation is easily arrived, so that the amount of the carbide at the diamond/interlayer interface decreases evidently. This decreases the strength of the covalent bonding from the carbide, producing poor adhesion. Moreover, with the raise of Al content in the interlayer, the hardness of the multilayer coated stainless steel increases due to the increase of the interlayer's hardness and the slight increase of the diamond content in the film. • An adherent diamond film was prepared on stainless steel using Cr/Cr Al N interlayer. • Diamond film becomes thick with interlayer's Al content increasing. • The adhesion becomes poor when applying Cr Al N interlayer with high Al content." @default.
- W4304943312 created "2022-10-13" @default.
- W4304943312 creator A5017700164 @default.
- W4304943312 creator A5018959128 @default.
- W4304943312 creator A5035330500 @default.
- W4304943312 creator A5035339773 @default.
- W4304943312 creator A5036699072 @default.
- W4304943312 creator A5039268297 @default.
- W4304943312 creator A5045392886 @default.
- W4304943312 creator A5065228157 @default.
- W4304943312 creator A5081272438 @default.
- W4304943312 creator A5081449417 @default.
- W4304943312 date "2022-11-01" @default.
- W4304943312 modified "2023-09-23" @default.
- W4304943312 title "Deposition of an adherent diamond film on stainless steel using Cr/Cr Al N as an interlayer" @default.
- W4304943312 cites W1683671757 @default.
- W4304943312 cites W1825395731 @default.
- W4304943312 cites W1973149517 @default.
- W4304943312 cites W1985646677 @default.
- W4304943312 cites W2000160195 @default.
- W4304943312 cites W2006272081 @default.
- W4304943312 cites W2010444884 @default.
- W4304943312 cites W2015434186 @default.
- W4304943312 cites W2015872531 @default.
- W4304943312 cites W2020732688 @default.
- W4304943312 cites W2021899098 @default.
- W4304943312 cites W2026733239 @default.
- W4304943312 cites W2029757758 @default.
- W4304943312 cites W2034384380 @default.
- W4304943312 cites W2056581802 @default.
- W4304943312 cites W2060888994 @default.
- W4304943312 cites W2060921503 @default.
- W4304943312 cites W2061704947 @default.
- W4304943312 cites W2063158878 @default.
- W4304943312 cites W2070499049 @default.
- W4304943312 cites W2073663005 @default.
- W4304943312 cites W2087343132 @default.
- W4304943312 cites W2091975258 @default.
- W4304943312 cites W2093336032 @default.
- W4304943312 cites W2097332735 @default.
- W4304943312 cites W2148288756 @default.
- W4304943312 cites W2170912302 @default.
- W4304943312 cites W2171898868 @default.
- W4304943312 cites W2298220592 @default.
- W4304943312 cites W2322338229 @default.
- W4304943312 cites W2344897459 @default.
- W4304943312 cites W2505430104 @default.
- W4304943312 cites W2547434574 @default.
- W4304943312 cites W2600078708 @default.
- W4304943312 cites W2761702354 @default.
- W4304943312 cites W2775474373 @default.
- W4304943312 cites W2789687069 @default.
- W4304943312 cites W2891612503 @default.
- W4304943312 cites W2894458603 @default.
- W4304943312 cites W2944434922 @default.
- W4304943312 cites W2973202965 @default.
- W4304943312 cites W3046488048 @default.
- W4304943312 cites W3108783460 @default.
- W4304943312 cites W3127031773 @default.
- W4304943312 doi "https://doi.org/10.1016/j.surfcoat.2022.128960" @default.
- W4304943312 hasPublicationYear "2022" @default.
- W4304943312 type Work @default.
- W4304943312 citedByCount "3" @default.
- W4304943312 countsByYear W43049433122023 @default.
- W4304943312 crossrefType "journal-article" @default.
- W4304943312 hasAuthorship W4304943312A5017700164 @default.
- W4304943312 hasAuthorship W4304943312A5018959128 @default.
- W4304943312 hasAuthorship W4304943312A5035330500 @default.
- W4304943312 hasAuthorship W4304943312A5035339773 @default.
- W4304943312 hasAuthorship W4304943312A5036699072 @default.
- W4304943312 hasAuthorship W4304943312A5039268297 @default.
- W4304943312 hasAuthorship W4304943312A5045392886 @default.
- W4304943312 hasAuthorship W4304943312A5065228157 @default.
- W4304943312 hasAuthorship W4304943312A5081272438 @default.
- W4304943312 hasAuthorship W4304943312A5081449417 @default.
- W4304943312 hasConcept C151730666 @default.
- W4304943312 hasConcept C159985019 @default.
- W4304943312 hasConcept C191897082 @default.
- W4304943312 hasConcept C192562407 @default.
- W4304943312 hasConcept C2776921476 @default.
- W4304943312 hasConcept C2816523 @default.
- W4304943312 hasConcept C64297162 @default.
- W4304943312 hasConcept C86803240 @default.
- W4304943312 hasConceptScore W4304943312C151730666 @default.
- W4304943312 hasConceptScore W4304943312C159985019 @default.
- W4304943312 hasConceptScore W4304943312C191897082 @default.
- W4304943312 hasConceptScore W4304943312C192562407 @default.
- W4304943312 hasConceptScore W4304943312C2776921476 @default.
- W4304943312 hasConceptScore W4304943312C2816523 @default.
- W4304943312 hasConceptScore W4304943312C64297162 @default.
- W4304943312 hasConceptScore W4304943312C86803240 @default.
- W4304943312 hasLocation W43049433121 @default.
- W4304943312 hasOpenAccess W4304943312 @default.
- W4304943312 hasPrimaryLocation W43049433121 @default.
- W4304943312 hasRelatedWork W2051270029 @default.
- W4304943312 hasRelatedWork W2082293200 @default.
- W4304943312 hasRelatedWork W2137307547 @default.
- W4304943312 hasRelatedWork W2371413910 @default.