- W4307370568 abstract "The microstructure, texture, and tensile properties of hot extruded Mg-6Zn-1Y-1Ce alloy obtained at a temperature range of 300 °C to 400 °C were studied. Electron back-scatter diffraction (EBSD) results revealed that strong basal plane texture was found along extrusion direction in the sample extruded below 340 °C due to discontinuous dynamic recrystallization (DRX) mechanism. In the sample extruded at 340 °C the average value of Schmid factor (SF) of {0001}〈11-20〉 slip system was 0.09. However, the sample extruded above 370 °C had weak basal texture under the control of continuous DRX mechanism, and the SF was well-distributed with an average value of about 0.32. The strengths of as-extruded samples decreased with increase of extrusion temperatures. In addition to fine grain strengthening, texture strengthening had a significant contribution to the high strength for the sample extruded at low temperature." @default.
- W4307370568 created "2022-11-01" @default.
- W4307370568 creator A5011487190 @default.
- W4307370568 creator A5016482598 @default.
- W4307370568 creator A5016724242 @default.
- W4307370568 creator A5018863416 @default.
- W4307370568 creator A5023516382 @default.
- W4307370568 creator A5043782487 @default.
- W4307370568 date "2022-10-25" @default.
- W4307370568 modified "2023-10-16" @default.
- W4307370568 title "Effects of Texture on Tensile Properties of Hot Extruded Mg-6Zn-1Y-1Ce Alloy" @default.
- W4307370568 cites W1965327217 @default.
- W4307370568 cites W1979843502 @default.
- W4307370568 cites W1980648613 @default.
- W4307370568 cites W1984378121 @default.
- W4307370568 cites W1984747728 @default.
- W4307370568 cites W1985769224 @default.
- W4307370568 cites W1987344529 @default.
- W4307370568 cites W2000280018 @default.
- W4307370568 cites W2010887526 @default.
- W4307370568 cites W2011251579 @default.
- W4307370568 cites W2018725534 @default.
- W4307370568 cites W2020123988 @default.
- W4307370568 cites W2029481710 @default.
- W4307370568 cites W2029673354 @default.
- W4307370568 cites W2030216547 @default.
- W4307370568 cites W2033439786 @default.
- W4307370568 cites W2037146709 @default.
- W4307370568 cites W2043521263 @default.
- W4307370568 cites W2052085689 @default.
- W4307370568 cites W2066384256 @default.
- W4307370568 cites W2070052279 @default.
- W4307370568 cites W2080881309 @default.
- W4307370568 cites W2497704593 @default.
- W4307370568 cites W2517900776 @default.
- W4307370568 cites W282138798 @default.
- W4307370568 cites W2983505699 @default.
- W4307370568 cites W3141287785 @default.
- W4307370568 doi "https://doi.org/10.4028/p-hkp33v" @default.
- W4307370568 hasPublicationYear "2022" @default.
- W4307370568 type Work @default.
- W4307370568 citedByCount "0" @default.
- W4307370568 crossrefType "journal-article" @default.
- W4307370568 hasAuthorship W4307370568A5011487190 @default.
- W4307370568 hasAuthorship W4307370568A5016482598 @default.
- W4307370568 hasAuthorship W4307370568A5016724242 @default.
- W4307370568 hasAuthorship W4307370568A5018863416 @default.
- W4307370568 hasAuthorship W4307370568A5023516382 @default.
- W4307370568 hasAuthorship W4307370568A5043782487 @default.
- W4307370568 hasConcept C112950240 @default.
- W4307370568 hasConcept C115961682 @default.
- W4307370568 hasConcept C121332964 @default.
- W4307370568 hasConcept C151730666 @default.
- W4307370568 hasConcept C154945302 @default.
- W4307370568 hasConcept C159985019 @default.
- W4307370568 hasConcept C169010117 @default.
- W4307370568 hasConcept C172658604 @default.
- W4307370568 hasConcept C191897082 @default.
- W4307370568 hasConcept C192562407 @default.
- W4307370568 hasConcept C195268267 @default.
- W4307370568 hasConcept C195702682 @default.
- W4307370568 hasConcept C26771246 @default.
- W4307370568 hasConcept C2778958987 @default.
- W4307370568 hasConcept C2780026712 @default.
- W4307370568 hasConcept C27805521 @default.
- W4307370568 hasConcept C2781195486 @default.
- W4307370568 hasConcept C41008148 @default.
- W4307370568 hasConcept C86803240 @default.
- W4307370568 hasConcept C87976508 @default.
- W4307370568 hasConcept C97355855 @default.
- W4307370568 hasConceptScore W4307370568C112950240 @default.
- W4307370568 hasConceptScore W4307370568C115961682 @default.
- W4307370568 hasConceptScore W4307370568C121332964 @default.
- W4307370568 hasConceptScore W4307370568C151730666 @default.
- W4307370568 hasConceptScore W4307370568C154945302 @default.
- W4307370568 hasConceptScore W4307370568C159985019 @default.
- W4307370568 hasConceptScore W4307370568C169010117 @default.
- W4307370568 hasConceptScore W4307370568C172658604 @default.
- W4307370568 hasConceptScore W4307370568C191897082 @default.
- W4307370568 hasConceptScore W4307370568C192562407 @default.
- W4307370568 hasConceptScore W4307370568C195268267 @default.
- W4307370568 hasConceptScore W4307370568C195702682 @default.
- W4307370568 hasConceptScore W4307370568C26771246 @default.
- W4307370568 hasConceptScore W4307370568C2778958987 @default.
- W4307370568 hasConceptScore W4307370568C2780026712 @default.
- W4307370568 hasConceptScore W4307370568C27805521 @default.
- W4307370568 hasConceptScore W4307370568C2781195486 @default.
- W4307370568 hasConceptScore W4307370568C41008148 @default.
- W4307370568 hasConceptScore W4307370568C86803240 @default.
- W4307370568 hasConceptScore W4307370568C87976508 @default.
- W4307370568 hasConceptScore W4307370568C97355855 @default.
- W4307370568 hasLocation W43073705681 @default.
- W4307370568 hasOpenAccess W4307370568 @default.
- W4307370568 hasPrimaryLocation W43073705681 @default.
- W4307370568 hasRelatedWork W1982015266 @default.
- W4307370568 hasRelatedWork W1987487801 @default.
- W4307370568 hasRelatedWork W2003157036 @default.
- W4307370568 hasRelatedWork W2010291024 @default.