- W4307607310 abstract "Abstract The development of dielectric constant materials for energy storage applications is in high demand. Lead zirconate and lead zirconate titanate doping with erbium thin films and bulk -based devices with variant dielectric constant were created in this work. Pb (0.9) ) -Er 0.01 Zr (0.09 (PEZ) and Pb 0.9 -Er 0.01 -Zr 0.045 -Ti 0.045 (PEZT) thin films were produced on a glass substrate using a sol-gel doctor blade technique at low temperature. X-ray diffraction (XRD), transmission electron microscopy (TEM), and electron diffraction (ED) were used to examine the structure of the produced nanocrystals. PEZ and PEZT films had nanocrystals that were 9.5 nm and 15 nm in size, respectively, whereas PEZ and PEZT bulk nano-rods had 455 ± 5 nm in length and 45 ± 1 nm in diameter. The TEM and XRD results were found to be completely consistent in terms of particle size. Ferroelectric properties and dielectric characteristics were found to be frequency dependent. Dielectric experiments revealed that the dielectric constant was decreasing for bulk samples as compared to film samples. The residual polarization of the Er-doped PEZ and PEZT films was the highest, reaching 36.25 µC/cm 2 and 69.79 µC/cm 2 , respectively, and the coercive fields were 43kV/cm and 45.43 kV/cm, respectively. On the other hand, PEZ and PEZT bulk samples had residual polarizations of 27.15 µC/cm 2 and 37.29 µC/cm 2 , respectively, while having coercive fields of 32.3 kV/cm and 39.3 kV/cm, respectively. On the other hand, (PEZ) and (PEZT) samples may have potential use in energy storage applications." @default.
- W4307607310 created "2022-11-04" @default.
- W4307607310 creator A5002917151 @default.
- W4307607310 creator A5043799996 @default.
- W4307607310 date "2022-10-28" @default.
- W4307607310 modified "2023-10-18" @default.
- W4307607310 title "Erbium-doped (Pb 0.9 −Er 0.01 -Zr 0.09 ) and (Pb 0.9 -Er 0.01 -Zr 0.045 - Ti 0.045 ) nano-crystalline films and nano-rods ceramic synthesis by sol-gel technique for energy-storage application" @default.
- W4307607310 cites W1515732557 @default.
- W4307607310 cites W1589604442 @default.
- W4307607310 cites W1969028213 @default.
- W4307607310 cites W1972064284 @default.
- W4307607310 cites W1972391961 @default.
- W4307607310 cites W1989555430 @default.
- W4307607310 cites W2014935272 @default.
- W4307607310 cites W2024123877 @default.
- W4307607310 cites W2038883131 @default.
- W4307607310 cites W2039729629 @default.
- W4307607310 cites W2039824868 @default.
- W4307607310 cites W2049177906 @default.
- W4307607310 cites W2069289457 @default.
- W4307607310 cites W2074017169 @default.
- W4307607310 cites W2129041343 @default.
- W4307607310 cites W2144478581 @default.
- W4307607310 cites W2195947011 @default.
- W4307607310 cites W2374558944 @default.
- W4307607310 cites W2515207495 @default.
- W4307607310 cites W2520222739 @default.
- W4307607310 cites W2571546311 @default.
- W4307607310 cites W2605884719 @default.
- W4307607310 cites W2607182570 @default.
- W4307607310 cites W2611652558 @default.
- W4307607310 cites W2762544326 @default.
- W4307607310 cites W2788148843 @default.
- W4307607310 cites W2884429699 @default.
- W4307607310 cites W2922042885 @default.
- W4307607310 cites W2972369262 @default.
- W4307607310 cites W2995229126 @default.
- W4307607310 cites W3010046902 @default.
- W4307607310 cites W3012610842 @default.
- W4307607310 cites W3131638709 @default.
- W4307607310 cites W3155363588 @default.
- W4307607310 cites W40127693 @default.
- W4307607310 doi "https://doi.org/10.21203/rs.3.rs-2144949/v1" @default.
- W4307607310 hasPublicationYear "2022" @default.
- W4307607310 type Work @default.
- W4307607310 citedByCount "0" @default.
- W4307607310 crossrefType "posted-content" @default.
- W4307607310 hasAuthorship W4307607310A5002917151 @default.
- W4307607310 hasAuthorship W4307607310A5043799996 @default.
- W4307607310 hasBestOaLocation W43076073101 @default.
- W4307607310 hasConcept C113196181 @default.
- W4307607310 hasConcept C133386390 @default.
- W4307607310 hasConcept C159985019 @default.
- W4307607310 hasConcept C171250308 @default.
- W4307607310 hasConcept C185592680 @default.
- W4307607310 hasConcept C19067145 @default.
- W4307607310 hasConcept C192191005 @default.
- W4307607310 hasConcept C192562407 @default.
- W4307607310 hasConcept C199289684 @default.
- W4307607310 hasConcept C2781128178 @default.
- W4307607310 hasConcept C43617362 @default.
- W4307607310 hasConcept C49040817 @default.
- W4307607310 hasConcept C513967374 @default.
- W4307607310 hasConcept C57863236 @default.
- W4307607310 hasConcept C79090758 @default.
- W4307607310 hasConceptScore W4307607310C113196181 @default.
- W4307607310 hasConceptScore W4307607310C133386390 @default.
- W4307607310 hasConceptScore W4307607310C159985019 @default.
- W4307607310 hasConceptScore W4307607310C171250308 @default.
- W4307607310 hasConceptScore W4307607310C185592680 @default.
- W4307607310 hasConceptScore W4307607310C19067145 @default.
- W4307607310 hasConceptScore W4307607310C192191005 @default.
- W4307607310 hasConceptScore W4307607310C192562407 @default.
- W4307607310 hasConceptScore W4307607310C199289684 @default.
- W4307607310 hasConceptScore W4307607310C2781128178 @default.
- W4307607310 hasConceptScore W4307607310C43617362 @default.
- W4307607310 hasConceptScore W4307607310C49040817 @default.
- W4307607310 hasConceptScore W4307607310C513967374 @default.
- W4307607310 hasConceptScore W4307607310C57863236 @default.
- W4307607310 hasConceptScore W4307607310C79090758 @default.
- W4307607310 hasLocation W43076073101 @default.
- W4307607310 hasOpenAccess W4307607310 @default.
- W4307607310 hasPrimaryLocation W43076073101 @default.
- W4307607310 hasRelatedWork W1967406975 @default.
- W4307607310 hasRelatedWork W2040729103 @default.
- W4307607310 hasRelatedWork W2076728855 @default.
- W4307607310 hasRelatedWork W2079496011 @default.
- W4307607310 hasRelatedWork W2090723813 @default.
- W4307607310 hasRelatedWork W2248971758 @default.
- W4307607310 hasRelatedWork W4251731606 @default.
- W4307607310 hasRelatedWork W4327948915 @default.
- W4307607310 hasRelatedWork W4377695079 @default.
- W4307607310 hasRelatedWork W1672619082 @default.
- W4307607310 isParatext "false" @default.
- W4307607310 isRetracted "false" @default.
- W4307607310 workType "article" @default.