- W4307891391 abstract "The surface checks or internal cracks from drying could significantly affect the processing and utilization of the wood. Therefore, it is of great significance to investigate the formation mechanism of cracks and reduce its occurrence. In this work, the development of cracking was quantified and its relationship with moisture content (MC) gradient and anisotropic shrinkage was analyzed. Results showed that the slight shrinkage occurred at the MC of 40%, and the shrinkage ratio at the end of drying was about 7.38% in the tangential (T) direction and 4.35% in the radial (R) direction. The shrinkage ratio of T/R in the MC range of 30%–15% was about 1.8, which was higher than that (1.65) in the MC range of 15%–5%. Cracks initiation was observed at average MC of 45%. The area and number of cracks reached a maximum at 15% MC. During the late stage of drying, the drying stress of the surface layer was reversed from tensile to compressive, which leads to the narrowing or closure of the cracks. Moreover, the fracture morphology of wood cells was observed at the microscopic level, indicating that the failure firstly occurred in the intercellular layer between the ray tissue and the tracheid in the latewood. The ray cells presented intact, and the lamellar structure between ray tissues and between the ray cells and the tracheids were the weak points of wood during drying. The results would contribute to keeping in minimum drying defects and improving the drying quality of wood." @default.
- W4307891391 created "2022-11-06" @default.
- W4307891391 creator A5037714008 @default.
- W4307891391 creator A5047540084 @default.
- W4307891391 creator A5051749291 @default.
- W4307891391 creator A5075445845 @default.
- W4307891391 creator A5079914638 @default.
- W4307891391 creator A5086924288 @default.
- W4307891391 date "2022-10-31" @default.
- W4307891391 modified "2023-09-29" @default.
- W4307891391 title "The formation mechanism of microcracks and fracture morphology of wood during drying" @default.
- W4307891391 cites W1978172017 @default.
- W4307891391 cites W1991835144 @default.
- W4307891391 cites W2009073621 @default.
- W4307891391 cites W2021496507 @default.
- W4307891391 cites W2021587135 @default.
- W4307891391 cites W2026035746 @default.
- W4307891391 cites W2038984403 @default.
- W4307891391 cites W2048227022 @default.
- W4307891391 cites W2052871748 @default.
- W4307891391 cites W2062778807 @default.
- W4307891391 cites W2065316445 @default.
- W4307891391 cites W2068936711 @default.
- W4307891391 cites W2070635303 @default.
- W4307891391 cites W2074808372 @default.
- W4307891391 cites W2078492587 @default.
- W4307891391 cites W2082126318 @default.
- W4307891391 cites W2303480060 @default.
- W4307891391 cites W2322027275 @default.
- W4307891391 cites W2323291258 @default.
- W4307891391 cites W2328311929 @default.
- W4307891391 cites W2555996110 @default.
- W4307891391 cites W2585382465 @default.
- W4307891391 cites W2927046738 @default.
- W4307891391 cites W2949273810 @default.
- W4307891391 cites W2956398831 @default.
- W4307891391 cites W2984295143 @default.
- W4307891391 cites W3040398568 @default.
- W4307891391 cites W3083991509 @default.
- W4307891391 cites W3159628609 @default.
- W4307891391 cites W3172136015 @default.
- W4307891391 cites W3172813235 @default.
- W4307891391 cites W4200024630 @default.
- W4307891391 cites W4229489487 @default.
- W4307891391 cites W4253540857 @default.
- W4307891391 cites W4293125237 @default.
- W4307891391 cites W2032321700 @default.
- W4307891391 doi "https://doi.org/10.1080/07373937.2022.2139270" @default.
- W4307891391 hasPublicationYear "2022" @default.
- W4307891391 type Work @default.
- W4307891391 citedByCount "1" @default.
- W4307891391 countsByYear W43078913912023 @default.
- W4307891391 crossrefType "journal-article" @default.
- W4307891391 hasAuthorship W4307891391A5037714008 @default.
- W4307891391 hasAuthorship W4307891391A5047540084 @default.
- W4307891391 hasAuthorship W4307891391A5051749291 @default.
- W4307891391 hasAuthorship W4307891391A5075445845 @default.
- W4307891391 hasAuthorship W4307891391A5079914638 @default.
- W4307891391 hasAuthorship W4307891391A5086924288 @default.
- W4307891391 hasConcept C121332964 @default.
- W4307891391 hasConcept C121469830 @default.
- W4307891391 hasConcept C127413603 @default.
- W4307891391 hasConcept C159985019 @default.
- W4307891391 hasConcept C162838533 @default.
- W4307891391 hasConcept C176864760 @default.
- W4307891391 hasConcept C180145272 @default.
- W4307891391 hasConcept C187320778 @default.
- W4307891391 hasConcept C192562407 @default.
- W4307891391 hasConcept C24939127 @default.
- W4307891391 hasConcept C2779227376 @default.
- W4307891391 hasConcept C43369102 @default.
- W4307891391 hasConcept C49799701 @default.
- W4307891391 hasConcept C499950583 @default.
- W4307891391 hasConcept C54355233 @default.
- W4307891391 hasConcept C58396970 @default.
- W4307891391 hasConcept C59822182 @default.
- W4307891391 hasConcept C62520636 @default.
- W4307891391 hasConcept C77851909 @default.
- W4307891391 hasConcept C85725439 @default.
- W4307891391 hasConcept C86803240 @default.
- W4307891391 hasConceptScore W4307891391C121332964 @default.
- W4307891391 hasConceptScore W4307891391C121469830 @default.
- W4307891391 hasConceptScore W4307891391C127413603 @default.
- W4307891391 hasConceptScore W4307891391C159985019 @default.
- W4307891391 hasConceptScore W4307891391C162838533 @default.
- W4307891391 hasConceptScore W4307891391C176864760 @default.
- W4307891391 hasConceptScore W4307891391C180145272 @default.
- W4307891391 hasConceptScore W4307891391C187320778 @default.
- W4307891391 hasConceptScore W4307891391C192562407 @default.
- W4307891391 hasConceptScore W4307891391C24939127 @default.
- W4307891391 hasConceptScore W4307891391C2779227376 @default.
- W4307891391 hasConceptScore W4307891391C43369102 @default.
- W4307891391 hasConceptScore W4307891391C49799701 @default.
- W4307891391 hasConceptScore W4307891391C499950583 @default.
- W4307891391 hasConceptScore W4307891391C54355233 @default.
- W4307891391 hasConceptScore W4307891391C58396970 @default.
- W4307891391 hasConceptScore W4307891391C59822182 @default.
- W4307891391 hasConceptScore W4307891391C62520636 @default.