- W4308156336 abstract "The decomposition of (α2/γ) lamellae during service is an important microstructure degradation phenomenon that is worth studying. In this study, the decomposition mechanism of (α2/γ) lamellae was systematically investigated by transmission electron microscopy (TEM) and high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) techniques. The results showed facilitated α2 →βo phase transformation by [112¯0]α2/[01¯1]γ semi-coherent α2 /γ interface due to its larger misfit than that of [112¯0]α2/[1¯10]γ interface. Ellipsoidal ωo particles were formed at βo /α2 interface and nucleated at the interface dislocations. The energy-dispersive X-ray spectroscopy (EDS) results demonstrated feasible depletion of Mo and enrichment of Ti at α2 /βo interface to form ωo phase. In addition, lath-shaped ωo precipitates were observed between two precipitated large βo grains formed by direct α2 →ωo phase transformation. The formation mechanism of the lath ωo phase was attributed to both element segregation and strain accommodation caused by βo precipitate in α2 lamellae. The α2 /βo interface served as preferential nucleation sites for ωo phase due to the atomic structure of the interface, which crystallographically was closely associated with the structure of ωo phase. Moreover, βo precipitates at low stress introduced stacking faults in α2 lamellae, while delaying the parallel decomposition of α2 lamellae at high stress. In sum, these findings provided profound insights into the decomposition mechanism of (α2/γ) lamellae, relevant as theoretical basis for controlling the microstructures and improving the performance of β-solidified γ-TiAl alloys." @default.
- W4308156336 created "2022-11-08" @default.
- W4308156336 creator A5007276499 @default.
- W4308156336 creator A5021293751 @default.
- W4308156336 creator A5042133763 @default.
- W4308156336 creator A5048542101 @default.
- W4308156336 creator A5056036725 @default.
- W4308156336 creator A5056729360 @default.
- W4308156336 creator A5073896066 @default.
- W4308156336 creator A5084845056 @default.
- W4308156336 date "2023-01-01" @default.
- W4308156336 modified "2023-10-01" @default.
- W4308156336 title "Decomposition and phase transformation mechanisms of α2 lamellae in β-solidified γ-TiAl alloys" @default.
- W4308156336 cites W1967579098 @default.
- W4308156336 cites W1991730739 @default.
- W4308156336 cites W1998722335 @default.
- W4308156336 cites W2020236182 @default.
- W4308156336 cites W2032512432 @default.
- W4308156336 cites W2032671944 @default.
- W4308156336 cites W2045682389 @default.
- W4308156336 cites W2057328404 @default.
- W4308156336 cites W2062642795 @default.
- W4308156336 cites W2063290422 @default.
- W4308156336 cites W2064345286 @default.
- W4308156336 cites W2068941294 @default.
- W4308156336 cites W2069392472 @default.
- W4308156336 cites W2082680265 @default.
- W4308156336 cites W2089541837 @default.
- W4308156336 cites W2234198714 @default.
- W4308156336 cites W2252192838 @default.
- W4308156336 cites W2304689579 @default.
- W4308156336 cites W2531186432 @default.
- W4308156336 cites W2586506934 @default.
- W4308156336 cites W2591232449 @default.
- W4308156336 cites W2771019358 @default.
- W4308156336 cites W2775107482 @default.
- W4308156336 cites W2804562139 @default.
- W4308156336 cites W2938349276 @default.
- W4308156336 cites W2947201343 @default.
- W4308156336 cites W2990898648 @default.
- W4308156336 cites W3000171219 @default.
- W4308156336 cites W3032684587 @default.
- W4308156336 cites W3039477433 @default.
- W4308156336 cites W3044585145 @default.
- W4308156336 cites W3160010659 @default.
- W4308156336 cites W3200871815 @default.
- W4308156336 cites W346522623 @default.
- W4308156336 cites W4220865051 @default.
- W4308156336 cites W4221107659 @default.
- W4308156336 doi "https://doi.org/10.1016/j.actamat.2022.118492" @default.
- W4308156336 hasPublicationYear "2023" @default.
- W4308156336 type Work @default.
- W4308156336 citedByCount "6" @default.
- W4308156336 countsByYear W43081563362023 @default.
- W4308156336 crossrefType "journal-article" @default.
- W4308156336 hasAuthorship W4308156336A5007276499 @default.
- W4308156336 hasAuthorship W4308156336A5021293751 @default.
- W4308156336 hasAuthorship W4308156336A5042133763 @default.
- W4308156336 hasAuthorship W4308156336A5048542101 @default.
- W4308156336 hasAuthorship W4308156336A5056036725 @default.
- W4308156336 hasAuthorship W4308156336A5056729360 @default.
- W4308156336 hasAuthorship W4308156336A5073896066 @default.
- W4308156336 hasAuthorship W4308156336A5084845056 @default.
- W4308156336 hasConcept C121332964 @default.
- W4308156336 hasConcept C124681953 @default.
- W4308156336 hasConcept C146088050 @default.
- W4308156336 hasConcept C159985019 @default.
- W4308156336 hasConcept C171250308 @default.
- W4308156336 hasConcept C178790620 @default.
- W4308156336 hasConcept C185592680 @default.
- W4308156336 hasConcept C18747287 @default.
- W4308156336 hasConcept C192562407 @default.
- W4308156336 hasConcept C193016168 @default.
- W4308156336 hasConcept C2780430920 @default.
- W4308156336 hasConcept C33347731 @default.
- W4308156336 hasConcept C44280652 @default.
- W4308156336 hasConcept C46141821 @default.
- W4308156336 hasConcept C61048295 @default.
- W4308156336 hasConcept C8010536 @default.
- W4308156336 hasConcept C87976508 @default.
- W4308156336 hasConcept C97355855 @default.
- W4308156336 hasConceptScore W4308156336C121332964 @default.
- W4308156336 hasConceptScore W4308156336C124681953 @default.
- W4308156336 hasConceptScore W4308156336C146088050 @default.
- W4308156336 hasConceptScore W4308156336C159985019 @default.
- W4308156336 hasConceptScore W4308156336C171250308 @default.
- W4308156336 hasConceptScore W4308156336C178790620 @default.
- W4308156336 hasConceptScore W4308156336C185592680 @default.
- W4308156336 hasConceptScore W4308156336C18747287 @default.
- W4308156336 hasConceptScore W4308156336C192562407 @default.
- W4308156336 hasConceptScore W4308156336C193016168 @default.
- W4308156336 hasConceptScore W4308156336C2780430920 @default.
- W4308156336 hasConceptScore W4308156336C33347731 @default.
- W4308156336 hasConceptScore W4308156336C44280652 @default.
- W4308156336 hasConceptScore W4308156336C46141821 @default.
- W4308156336 hasConceptScore W4308156336C61048295 @default.
- W4308156336 hasConceptScore W4308156336C8010536 @default.
- W4308156336 hasConceptScore W4308156336C87976508 @default.