- W4308195632 abstract "In this study, ultrasonic rolling (C + USRP) and plasma nitriding (C + N) is performed on the surface of M50NiL steel after carburizing， the tension-compression fatigue test of R = −1 on different samples. The results show that the maximum fatigue limit of C + N, C + USRP, and single carburizing are 770 MPa, 676 MPa, and 412 MPa, respectively. The residual stress relaxation in the fatigue process of C + N and C + USRP is tested and found that the initial residual compressive stress of C + N is lower than that of C + USRP, but its attenuation value is considerably smaller. The microscopic characterization of samples is conducted after the fatigue tests. The nanometer nitrogen compounds in the composite permeability layer showed a strong pinning effect, however, microplastic deformation limits the fatigue process. The C + N demonstrates a much lower residual compressive stress relaxation, consequently, the C + N short crack propagation effective driving force Δ K eff value decreases. As a result, due to the higher crack closure effect, the C + N fatigue limit is observed higher than the C + USRP. • The fatigue properties of carburized M50NiL steel were improved after surface ultrasonic rolling(C + USRP) and plasma nitriding(C + N), respectively • Under the action of alternating load, the residual compressive stress of C + N is more stable, which is attributed to the pinning effect of nitride on dislocation." @default.
- W4308195632 created "2022-11-09" @default.
- W4308195632 creator A5005627824 @default.
- W4308195632 creator A5006012404 @default.
- W4308195632 creator A5012230974 @default.
- W4308195632 creator A5038539867 @default.
- W4308195632 creator A5057541508 @default.
- W4308195632 creator A5091898042 @default.
- W4308195632 date "2022-12-01" @default.
- W4308195632 modified "2023-10-18" @default.
- W4308195632 title "The high-cycle fatigue behavior of carburized M50NiL steel with high-energy modification and compound infiltration: A comparative study" @default.
- W4308195632 cites W1968788953 @default.
- W4308195632 cites W1978413094 @default.
- W4308195632 cites W1982001987 @default.
- W4308195632 cites W1988145661 @default.
- W4308195632 cites W1998133001 @default.
- W4308195632 cites W2009672309 @default.
- W4308195632 cites W2012688116 @default.
- W4308195632 cites W2020791302 @default.
- W4308195632 cites W2028602369 @default.
- W4308195632 cites W2028787481 @default.
- W4308195632 cites W2039475688 @default.
- W4308195632 cites W2040791414 @default.
- W4308195632 cites W2059944146 @default.
- W4308195632 cites W2062796638 @default.
- W4308195632 cites W2075841144 @default.
- W4308195632 cites W2085537632 @default.
- W4308195632 cites W2094345055 @default.
- W4308195632 cites W2094542606 @default.
- W4308195632 cites W2139438061 @default.
- W4308195632 cites W2323199200 @default.
- W4308195632 cites W2470226803 @default.
- W4308195632 cites W2550037894 @default.
- W4308195632 cites W2799971593 @default.
- W4308195632 cites W2924491590 @default.
- W4308195632 cites W2940362916 @default.
- W4308195632 cites W2957611106 @default.
- W4308195632 cites W2981079966 @default.
- W4308195632 cites W2985214662 @default.
- W4308195632 cites W2990050338 @default.
- W4308195632 cites W2998709978 @default.
- W4308195632 cites W3015608026 @default.
- W4308195632 cites W3024720324 @default.
- W4308195632 cites W3094037697 @default.
- W4308195632 cites W3115950804 @default.
- W4308195632 cites W3179645966 @default.
- W4308195632 cites W3208113524 @default.
- W4308195632 cites W3217781190 @default.
- W4308195632 cites W4224050521 @default.
- W4308195632 cites W4225279589 @default.
- W4308195632 cites W4292869133 @default.
- W4308195632 doi "https://doi.org/10.1016/j.surfcoat.2022.129009" @default.
- W4308195632 hasPublicationYear "2022" @default.
- W4308195632 type Work @default.
- W4308195632 citedByCount "2" @default.
- W4308195632 countsByYear W43081956322023 @default.
- W4308195632 crossrefType "journal-article" @default.
- W4308195632 hasAuthorship W4308195632A5005627824 @default.
- W4308195632 hasAuthorship W4308195632A5006012404 @default.
- W4308195632 hasAuthorship W4308195632A5012230974 @default.
- W4308195632 hasAuthorship W4308195632A5038539867 @default.
- W4308195632 hasAuthorship W4308195632A5057541508 @default.
- W4308195632 hasAuthorship W4308195632A5091898042 @default.
- W4308195632 hasConcept C153400128 @default.
- W4308195632 hasConcept C159985019 @default.
- W4308195632 hasConcept C191897082 @default.
- W4308195632 hasConcept C192562407 @default.
- W4308195632 hasConcept C2779686264 @default.
- W4308195632 hasConceptScore W4308195632C153400128 @default.
- W4308195632 hasConceptScore W4308195632C159985019 @default.
- W4308195632 hasConceptScore W4308195632C191897082 @default.
- W4308195632 hasConceptScore W4308195632C192562407 @default.
- W4308195632 hasConceptScore W4308195632C2779686264 @default.
- W4308195632 hasFunder F4320322272 @default.
- W4308195632 hasFunder F4320322795 @default.
- W4308195632 hasLocation W43081956321 @default.
- W4308195632 hasOpenAccess W4308195632 @default.
- W4308195632 hasPrimaryLocation W43081956321 @default.
- W4308195632 hasRelatedWork W1994103032 @default.
- W4308195632 hasRelatedWork W2051270029 @default.
- W4308195632 hasRelatedWork W2082293200 @default.
- W4308195632 hasRelatedWork W2137307547 @default.
- W4308195632 hasRelatedWork W2351679394 @default.
- W4308195632 hasRelatedWork W2380293314 @default.
- W4308195632 hasRelatedWork W2943188944 @default.
- W4308195632 hasRelatedWork W4242480814 @default.
- W4308195632 hasRelatedWork W4285802202 @default.
- W4308195632 hasRelatedWork W4317433637 @default.
- W4308195632 hasVolume "451" @default.
- W4308195632 isParatext "false" @default.
- W4308195632 isRetracted "false" @default.
- W4308195632 workType "article" @default.