- W4311532912 abstract "In this experiment, an annealing treatment was carried out for a rolled Zr–Ti–8V alloy, and the toughening mechanism of the material was thoroughly analyzed by combining advanced material characterization and other testing methods. The phase composition of the Zr–Ti–8V alloy was sensitive to the applied annealing temperature, while a series of changes in the phase composition of the alloy were induced by enforcing bigger thermal budgets. Implementing a temperature value of 450 °C led to a higher α-phase content, in striking contrast with the case where a lower annealing temperature of 400 °C was applied. The β grains that were stretched in the alloy’s rolling direction and annealed at 600 °C to 800 °C were recrystallized. As a result, the acquired configuration was equiaxed with β grains. The extracted results revealed that the alloy annealed at 450 °C showed a good strong–plastic ratio, with tensile strength and elongation of 1040 MPa and 8.2%, respectively. In addition, the alloy annealed at 700–800 °C showed good plasticity properties. From the hardness tests and friction wear experiments on all the experimental alloys, it was demonstrated that the dual-phase alloy with α + β had higher hardness and wear resistance, whereas the opposite trend was observed for the single β-phase alloy." @default.
- W4311532912 created "2022-12-26" @default.
- W4311532912 creator A5014937642 @default.
- W4311532912 creator A5019264377 @default.
- W4311532912 creator A5064461643 @default.
- W4311532912 creator A5069771802 @default.
- W4311532912 creator A5074339191 @default.
- W4311532912 creator A5085728336 @default.
- W4311532912 date "2022-12-05" @default.
- W4311532912 modified "2023-10-16" @default.
- W4311532912 title "Improvement of Mechanical Properties for a Novel Zr–Ti–V Alloy via Hot-Rolling and Annealing Treatment" @default.
- W4311532912 cites W1858812623 @default.
- W4311532912 cites W2005970984 @default.
- W4311532912 cites W2027148092 @default.
- W4311532912 cites W2058998925 @default.
- W4311532912 cites W2064017067 @default.
- W4311532912 cites W2100702168 @default.
- W4311532912 cites W2123895109 @default.
- W4311532912 cites W2521251686 @default.
- W4311532912 cites W2765304213 @default.
- W4311532912 cites W2771317126 @default.
- W4311532912 cites W2789152306 @default.
- W4311532912 cites W2789403617 @default.
- W4311532912 cites W2789884040 @default.
- W4311532912 cites W2893943115 @default.
- W4311532912 cites W2898342421 @default.
- W4311532912 cites W2926118945 @default.
- W4311532912 cites W2946298278 @default.
- W4311532912 cites W2947292937 @default.
- W4311532912 cites W2952498062 @default.
- W4311532912 cites W2953608741 @default.
- W4311532912 cites W2965169013 @default.
- W4311532912 cites W2970077167 @default.
- W4311532912 cites W2982330283 @default.
- W4311532912 cites W2982525310 @default.
- W4311532912 cites W3018940547 @default.
- W4311532912 cites W3118981625 @default.
- W4311532912 cites W3123501075 @default.
- W4311532912 cites W3159920441 @default.
- W4311532912 cites W3175624578 @default.
- W4311532912 cites W3179132954 @default.
- W4311532912 cites W3192421210 @default.
- W4311532912 cites W3193430363 @default.
- W4311532912 cites W3198421221 @default.
- W4311532912 cites W3203719115 @default.
- W4311532912 cites W3214659381 @default.
- W4311532912 cites W3214773950 @default.
- W4311532912 cites W4200529164 @default.
- W4311532912 cites W4210432788 @default.
- W4311532912 cites W4210618576 @default.
- W4311532912 cites W4213372233 @default.
- W4311532912 cites W4214841592 @default.
- W4311532912 doi "https://doi.org/10.3390/cryst12121765" @default.
- W4311532912 hasPublicationYear "2022" @default.
- W4311532912 type Work @default.
- W4311532912 citedByCount "0" @default.
- W4311532912 crossrefType "journal-article" @default.
- W4311532912 hasAuthorship W4311532912A5014937642 @default.
- W4311532912 hasAuthorship W4311532912A5019264377 @default.
- W4311532912 hasAuthorship W4311532912A5064461643 @default.
- W4311532912 hasAuthorship W4311532912A5069771802 @default.
- W4311532912 hasAuthorship W4311532912A5074339191 @default.
- W4311532912 hasAuthorship W4311532912A5085728336 @default.
- W4311532912 hasBestOaLocation W43115329121 @default.
- W4311532912 hasConcept C112950240 @default.
- W4311532912 hasConcept C159985019 @default.
- W4311532912 hasConcept C191897082 @default.
- W4311532912 hasConcept C192562407 @default.
- W4311532912 hasConcept C2777855556 @default.
- W4311532912 hasConcept C2780026712 @default.
- W4311532912 hasConcept C33947775 @default.
- W4311532912 hasConcept C79186407 @default.
- W4311532912 hasConcept C81710450 @default.
- W4311532912 hasConcept C87976508 @default.
- W4311532912 hasConceptScore W4311532912C112950240 @default.
- W4311532912 hasConceptScore W4311532912C159985019 @default.
- W4311532912 hasConceptScore W4311532912C191897082 @default.
- W4311532912 hasConceptScore W4311532912C192562407 @default.
- W4311532912 hasConceptScore W4311532912C2777855556 @default.
- W4311532912 hasConceptScore W4311532912C2780026712 @default.
- W4311532912 hasConceptScore W4311532912C33947775 @default.
- W4311532912 hasConceptScore W4311532912C79186407 @default.
- W4311532912 hasConceptScore W4311532912C81710450 @default.
- W4311532912 hasConceptScore W4311532912C87976508 @default.
- W4311532912 hasFunder F4320321001 @default.
- W4311532912 hasIssue "12" @default.
- W4311532912 hasLocation W43115329121 @default.
- W4311532912 hasLocation W43115329122 @default.
- W4311532912 hasOpenAccess W4311532912 @default.
- W4311532912 hasPrimaryLocation W43115329121 @default.
- W4311532912 hasRelatedWork W1979107336 @default.
- W4311532912 hasRelatedWork W2043583991 @default.
- W4311532912 hasRelatedWork W2348697288 @default.
- W4311532912 hasRelatedWork W2357499900 @default.
- W4311532912 hasRelatedWork W2369154548 @default.
- W4311532912 hasRelatedWork W2371235204 @default.
- W4311532912 hasRelatedWork W2377322010 @default.
- W4311532912 hasRelatedWork W2379439189 @default.