- W4311762959 abstract "Based on the powder metallurgy method, FeBSiC amorphous powders were produced by a novel gas-water combined atomization process and were co-coated by five kinds of insulating agents (polyamide, aluminum dihydrogen phosphate, calcium phosphate, zinc phosphate and hydrochloric acid) and epoxy resins. The content of each insulating agents was optimized to improve the magnetic properties of the amorphous magnetic powder cores (AMPCs). The results showed that the FeBSiC powders showed extremely high saturation magnetization (171.1 emu·g–1) and low coercivity (6.11 Oe), which could provide excellent raw materials for AMPCs. Among the five insulating agents, the polyamide-coated AMPCs had the worst electrical insulating effect and magnetic properties. Although the AMPCs coated with aluminum dihydrogen, zinc phosphate, calcium phosphate and hydrochloric acid all exhibited low eddy current losses, only the AMPCs coated with calcium phosphate exhibited extremely low hysteresis losses. As the calcium phosphate content increased, the density and resistance of the AMPCs both increased and then decreased, and the core losses decreased and then increased. When the calcium phosphate content was 0.5 wt.%, the [email protected] calcium phosphate + epoxy resins core-shell structured AMPCs had high permeability of 28.1 ± 0.3, high DC bias% of 96.1 ± 0.2 at a DC magnetic field of 5671.5 A·m–1, and low core loss of 18.0 ± 0.8 kW·m–3 at 100 kHz and 0.02 T, which showed excellent magnetic properties at high frequency and confirmed to the current development trend of miniaturization, high-frequency and high-efficiency in electrical and electronic fields." @default.
- W4311762959 created "2022-12-28" @default.
- W4311762959 creator A5027114201 @default.
- W4311762959 creator A5040899817 @default.
- W4311762959 creator A5045960607 @default.
- W4311762959 creator A5060523046 @default.
- W4311762959 creator A5064169754 @default.
- W4311762959 creator A5075168365 @default.
- W4311762959 date "2023-02-01" @default.
- W4311762959 modified "2023-09-27" @default.
- W4311762959 title "Industrial-scale fabrication of amorphous magnetic powder cores with excellent high-frequency magnetic properties: Optimization for kinds and content of insulating agents" @default.
- W4311762959 cites W1982154233 @default.
- W4311762959 cites W2005520156 @default.
- W4311762959 cites W2015635724 @default.
- W4311762959 cites W2017260990 @default.
- W4311762959 cites W2020587930 @default.
- W4311762959 cites W2065010909 @default.
- W4311762959 cites W2077237812 @default.
- W4311762959 cites W2513440956 @default.
- W4311762959 cites W2538105827 @default.
- W4311762959 cites W2741356854 @default.
- W4311762959 cites W2768059692 @default.
- W4311762959 cites W2776601562 @default.
- W4311762959 cites W2783040614 @default.
- W4311762959 cites W2895008518 @default.
- W4311762959 cites W2898304272 @default.
- W4311762959 cites W2898631467 @default.
- W4311762959 cites W2899665076 @default.
- W4311762959 cites W2900259925 @default.
- W4311762959 cites W2946116575 @default.
- W4311762959 cites W2956299784 @default.
- W4311762959 cites W2961134263 @default.
- W4311762959 cites W3001439319 @default.
- W4311762959 cites W3006386008 @default.
- W4311762959 cites W3020845607 @default.
- W4311762959 cites W3082540846 @default.
- W4311762959 cites W3087495930 @default.
- W4311762959 cites W3099676037 @default.
- W4311762959 cites W3106910169 @default.
- W4311762959 cites W3126906539 @default.
- W4311762959 cites W3150319594 @default.
- W4311762959 cites W3167131209 @default.
- W4311762959 cites W3200735707 @default.
- W4311762959 cites W3208736053 @default.
- W4311762959 cites W3215091937 @default.
- W4311762959 cites W3216417649 @default.
- W4311762959 cites W4200617571 @default.
- W4311762959 cites W4210437828 @default.
- W4311762959 cites W4229366768 @default.
- W4311762959 cites W4289260035 @default.
- W4311762959 cites W4295540271 @default.
- W4311762959 doi "https://doi.org/10.1016/j.jnoncrysol.2022.122082" @default.
- W4311762959 hasPublicationYear "2023" @default.
- W4311762959 type Work @default.
- W4311762959 citedByCount "1" @default.
- W4311762959 countsByYear W43117629592023 @default.
- W4311762959 crossrefType "journal-article" @default.
- W4311762959 hasAuthorship W4311762959A5027114201 @default.
- W4311762959 hasAuthorship W4311762959A5040899817 @default.
- W4311762959 hasAuthorship W4311762959A5045960607 @default.
- W4311762959 hasAuthorship W4311762959A5060523046 @default.
- W4311762959 hasAuthorship W4311762959A5064169754 @default.
- W4311762959 hasAuthorship W4311762959A5075168365 @default.
- W4311762959 hasConcept C121332964 @default.
- W4311762959 hasConcept C126530901 @default.
- W4311762959 hasConcept C127413603 @default.
- W4311762959 hasConcept C13965031 @default.
- W4311762959 hasConcept C159985019 @default.
- W4311762959 hasConcept C178790620 @default.
- W4311762959 hasConcept C185592680 @default.
- W4311762959 hasConcept C191897082 @default.
- W4311762959 hasConcept C192562407 @default.
- W4311762959 hasConcept C26873012 @default.
- W4311762959 hasConcept C2777001299 @default.
- W4311762959 hasConcept C2777132085 @default.
- W4311762959 hasConcept C42360764 @default.
- W4311762959 hasConcept C519063684 @default.
- W4311762959 hasConcept C56052488 @default.
- W4311762959 hasConceptScore W4311762959C121332964 @default.
- W4311762959 hasConceptScore W4311762959C126530901 @default.
- W4311762959 hasConceptScore W4311762959C127413603 @default.
- W4311762959 hasConceptScore W4311762959C13965031 @default.
- W4311762959 hasConceptScore W4311762959C159985019 @default.
- W4311762959 hasConceptScore W4311762959C178790620 @default.
- W4311762959 hasConceptScore W4311762959C185592680 @default.
- W4311762959 hasConceptScore W4311762959C191897082 @default.
- W4311762959 hasConceptScore W4311762959C192562407 @default.
- W4311762959 hasConceptScore W4311762959C26873012 @default.
- W4311762959 hasConceptScore W4311762959C2777001299 @default.
- W4311762959 hasConceptScore W4311762959C2777132085 @default.
- W4311762959 hasConceptScore W4311762959C42360764 @default.
- W4311762959 hasConceptScore W4311762959C519063684 @default.
- W4311762959 hasConceptScore W4311762959C56052488 @default.
- W4311762959 hasFunder F4320325365 @default.
- W4311762959 hasFunder F4320333596 @default.
- W4311762959 hasLocation W43117629591 @default.
- W4311762959 hasOpenAccess W4311762959 @default.
- W4311762959 hasPrimaryLocation W43117629591 @default.