- W4312056538 abstract "This paper explored the viscoelasticity-induced fracture behavior of rock-concrete interface after sustaining the creep process. Creep tests were firstly conducted on the composite rock-concrete specimens under three-point bending loading at the load levels of 50% and 75% of the maximum load. After 90-day sustained loading, composite specimens were unloaded and then reloaded under quasi-static loading conditions, and the digital image correlation technique was employed to quantify the crack profiles at the rock-concrete interface. The results indicate that the pre-set crack at the rock-concrete interface would not initiate further during the creep tests if the sustained load was below the initial cracking load. After sustaining a creep process, the initial cracking load increased obviously but the elastic strain energy near the pre-crack tip remained unchanged. The creep deformations during the creep tests made the characteristic lengths of the rock-concrete interfaces decreased largely, leading to the obvious enhancement of the interfacial brittleness. As a result, the interfacial nonlinear fracture behavior from the initial cracking state to the unstable fracture state would become weaker. In addition, the fully formed fracture process zone length and the corresponding crack length increased with the increase of the sustained load level, indicating that the boundary effect of the rock-concrete interface would decreased." @default.
- W4312056538 created "2023-01-04" @default.
- W4312056538 creator A5037698367 @default.
- W4312056538 creator A5060716417 @default.
- W4312056538 creator A5088915847 @default.
- W4312056538 creator A5089806196 @default.
- W4312056538 date "2023-02-01" @default.
- W4312056538 modified "2023-10-14" @default.
- W4312056538 title "Viscoelasticity-induced fracture behavior of rock-concrete interface after sustaining creep process" @default.
- W4312056538 cites W1970187130 @default.
- W4312056538 cites W1976786172 @default.
- W4312056538 cites W1997595029 @default.
- W4312056538 cites W2011816761 @default.
- W4312056538 cites W2016089316 @default.
- W4312056538 cites W2048397841 @default.
- W4312056538 cites W2068031085 @default.
- W4312056538 cites W2082508622 @default.
- W4312056538 cites W2086006797 @default.
- W4312056538 cites W2086036723 @default.
- W4312056538 cites W2089336375 @default.
- W4312056538 cites W2140191633 @default.
- W4312056538 cites W2149805791 @default.
- W4312056538 cites W2172256091 @default.
- W4312056538 cites W233922479 @default.
- W4312056538 cites W2551474405 @default.
- W4312056538 cites W2561877798 @default.
- W4312056538 cites W2576590490 @default.
- W4312056538 cites W2779193047 @default.
- W4312056538 cites W2883607782 @default.
- W4312056538 cites W2888685709 @default.
- W4312056538 cites W2974320428 @default.
- W4312056538 cites W307718881 @default.
- W4312056538 cites W3214647710 @default.
- W4312056538 cites W4242722365 @default.
- W4312056538 doi "https://doi.org/10.1016/j.cemconcomp.2022.104901" @default.
- W4312056538 hasPublicationYear "2023" @default.
- W4312056538 type Work @default.
- W4312056538 citedByCount "2" @default.
- W4312056538 countsByYear W43120565382023 @default.
- W4312056538 crossrefType "journal-article" @default.
- W4312056538 hasAuthorship W4312056538A5037698367 @default.
- W4312056538 hasAuthorship W4312056538A5060716417 @default.
- W4312056538 hasAuthorship W4312056538A5088915847 @default.
- W4312056538 hasAuthorship W4312056538A5089806196 @default.
- W4312056538 hasConcept C127313418 @default.
- W4312056538 hasConcept C127413603 @default.
- W4312056538 hasConcept C136478896 @default.
- W4312056538 hasConcept C149912024 @default.
- W4312056538 hasConcept C159985019 @default.
- W4312056538 hasConcept C186541917 @default.
- W4312056538 hasConcept C187320778 @default.
- W4312056538 hasConcept C192562407 @default.
- W4312056538 hasConcept C43369102 @default.
- W4312056538 hasConcept C58396970 @default.
- W4312056538 hasConcept C59085676 @default.
- W4312056538 hasConcept C66938386 @default.
- W4312056538 hasConceptScore W4312056538C127313418 @default.
- W4312056538 hasConceptScore W4312056538C127413603 @default.
- W4312056538 hasConceptScore W4312056538C136478896 @default.
- W4312056538 hasConceptScore W4312056538C149912024 @default.
- W4312056538 hasConceptScore W4312056538C159985019 @default.
- W4312056538 hasConceptScore W4312056538C186541917 @default.
- W4312056538 hasConceptScore W4312056538C187320778 @default.
- W4312056538 hasConceptScore W4312056538C192562407 @default.
- W4312056538 hasConceptScore W4312056538C43369102 @default.
- W4312056538 hasConceptScore W4312056538C58396970 @default.
- W4312056538 hasConceptScore W4312056538C59085676 @default.
- W4312056538 hasConceptScore W4312056538C66938386 @default.
- W4312056538 hasFunder F4320321001 @default.
- W4312056538 hasFunder F4320329223 @default.
- W4312056538 hasLocation W43120565381 @default.
- W4312056538 hasOpenAccess W4312056538 @default.
- W4312056538 hasPrimaryLocation W43120565381 @default.
- W4312056538 hasRelatedWork W1512319868 @default.
- W4312056538 hasRelatedWork W2006221599 @default.
- W4312056538 hasRelatedWork W2031660127 @default.
- W4312056538 hasRelatedWork W2048829577 @default.
- W4312056538 hasRelatedWork W2362004075 @default.
- W4312056538 hasRelatedWork W2382873751 @default.
- W4312056538 hasRelatedWork W2390990842 @default.
- W4312056538 hasRelatedWork W2778304221 @default.
- W4312056538 hasRelatedWork W2991685631 @default.
- W4312056538 hasRelatedWork W620426518 @default.
- W4312056538 hasVolume "136" @default.
- W4312056538 isParatext "false" @default.
- W4312056538 isRetracted "false" @default.
- W4312056538 workType "article" @default.