- W4313303693 abstract "Application of titanium alloys is restricted due to their low hardness and poor wear resistance. Duplex surface treatment consisting of depositing of Al coating by arc ion plating (AIP) plus micro-arc oxidation (MAO) was carried out on Ti6Al4V alloy to improve its tribological performance. Ceramic coating mainly composed of α-Al2O3, γ-Al2O3 and mullite was fabricated on the aluminum-coated titanium alloy after the MAO treatment, and its thickness, compactness and hardness increased with the MAO time before the titanium alloy was oxidized. After the substrate titanium alloy was locally oxidized due to oxygen anions inward migration, a thin transition layer containing titanium oxides and aluminum titanate formed and incorporation of Ti in the alumina coating occurred. Occurrence of the strong eruptible discharges at these positions was facilitated probably due to the large difference in permittivity of the alumina and the titanium oxides, which led to the formation of penetrating cracks in the MAO coating. The hardness and compactness of the ceramic coating decreased. Tensile test results showed bonding strength of MAO ceramic coating/aluminum layer/titanium alloy substrate system was more than 40 MPa, and the maximum value could reach around 68 MPa. The bonding strength of the ceramic coating/titanium alloy substrate system decreased to around 34 MPa due to the weak bonding between the alumina ceramic coating and the titanium alloy substrate. Tribological test results show wear resistance of titanium alloy was greatly improved due to the fabrication of hard alumina ceramic coating on titanium alloy." @default.
- W4313303693 created "2023-01-06" @default.
- W4313303693 creator A5022526821 @default.
- W4313303693 creator A5028878585 @default.
- W4313303693 creator A5030081164 @default.
- W4313303693 creator A5056793018 @default.
- W4313303693 creator A5075161928 @default.
- W4313303693 creator A5076699095 @default.
- W4313303693 creator A5089632319 @default.
- W4313303693 creator A5090704187 @default.
- W4313303693 date "2022-12-19" @default.
- W4313303693 modified "2023-10-18" @default.
- W4313303693 title "Structure and mechanical properties of MAO coatings formed on aluminum-coated titanium alloy" @default.
- W4313303693 cites W1969101265 @default.
- W4313303693 cites W1971685393 @default.
- W4313303693 cites W1976710015 @default.
- W4313303693 cites W1978403491 @default.
- W4313303693 cites W1992514246 @default.
- W4313303693 cites W1997447189 @default.
- W4313303693 cites W2001137888 @default.
- W4313303693 cites W2013729050 @default.
- W4313303693 cites W2019008758 @default.
- W4313303693 cites W2025116324 @default.
- W4313303693 cites W2057902369 @default.
- W4313303693 cites W2062067261 @default.
- W4313303693 cites W2071524258 @default.
- W4313303693 cites W2076469088 @default.
- W4313303693 cites W2083513013 @default.
- W4313303693 cites W2084721001 @default.
- W4313303693 cites W2085622397 @default.
- W4313303693 cites W2087192561 @default.
- W4313303693 cites W2087904375 @default.
- W4313303693 cites W2111778586 @default.
- W4313303693 cites W2112172953 @default.
- W4313303693 cites W2126710272 @default.
- W4313303693 cites W2329771047 @default.
- W4313303693 cites W2416286460 @default.
- W4313303693 cites W2508783514 @default.
- W4313303693 cites W2604263758 @default.
- W4313303693 cites W2741898238 @default.
- W4313303693 cites W3005491093 @default.
- W4313303693 cites W3028554589 @default.
- W4313303693 cites W607747901 @default.
- W4313303693 doi "https://doi.org/10.1080/25787616.2022.2156228" @default.
- W4313303693 hasPublicationYear "2022" @default.
- W4313303693 type Work @default.
- W4313303693 citedByCount "0" @default.
- W4313303693 crossrefType "journal-article" @default.
- W4313303693 hasAuthorship W4313303693A5022526821 @default.
- W4313303693 hasAuthorship W4313303693A5028878585 @default.
- W4313303693 hasAuthorship W4313303693A5030081164 @default.
- W4313303693 hasAuthorship W4313303693A5056793018 @default.
- W4313303693 hasAuthorship W4313303693A5075161928 @default.
- W4313303693 hasAuthorship W4313303693A5076699095 @default.
- W4313303693 hasAuthorship W4313303693A5089632319 @default.
- W4313303693 hasAuthorship W4313303693A5090704187 @default.
- W4313303693 hasBestOaLocation W43133036931 @default.
- W4313303693 hasConcept C111368507 @default.
- W4313303693 hasConcept C112950240 @default.
- W4313303693 hasConcept C127313418 @default.
- W4313303693 hasConcept C134132462 @default.
- W4313303693 hasConcept C159985019 @default.
- W4313303693 hasConcept C167310744 @default.
- W4313303693 hasConcept C191897082 @default.
- W4313303693 hasConcept C192562407 @default.
- W4313303693 hasConcept C2777289219 @default.
- W4313303693 hasConcept C2779227376 @default.
- W4313303693 hasConcept C2780026712 @default.
- W4313303693 hasConcept C2781448156 @default.
- W4313303693 hasConcept C506065880 @default.
- W4313303693 hasConcept C8953137 @default.
- W4313303693 hasConceptScore W4313303693C111368507 @default.
- W4313303693 hasConceptScore W4313303693C112950240 @default.
- W4313303693 hasConceptScore W4313303693C127313418 @default.
- W4313303693 hasConceptScore W4313303693C134132462 @default.
- W4313303693 hasConceptScore W4313303693C159985019 @default.
- W4313303693 hasConceptScore W4313303693C167310744 @default.
- W4313303693 hasConceptScore W4313303693C191897082 @default.
- W4313303693 hasConceptScore W4313303693C192562407 @default.
- W4313303693 hasConceptScore W4313303693C2777289219 @default.
- W4313303693 hasConceptScore W4313303693C2779227376 @default.
- W4313303693 hasConceptScore W4313303693C2780026712 @default.
- W4313303693 hasConceptScore W4313303693C2781448156 @default.
- W4313303693 hasConceptScore W4313303693C506065880 @default.
- W4313303693 hasConceptScore W4313303693C8953137 @default.
- W4313303693 hasFunder F4320321001 @default.
- W4313303693 hasFunder F4320323190 @default.
- W4313303693 hasFunder F4320329895 @default.
- W4313303693 hasIssue "1" @default.
- W4313303693 hasLocation W43133036931 @default.
- W4313303693 hasLocation W43133036932 @default.
- W4313303693 hasOpenAccess W4313303693 @default.
- W4313303693 hasPrimaryLocation W43133036931 @default.
- W4313303693 hasRelatedWork W1969887887 @default.
- W4313303693 hasRelatedWork W2054113325 @default.
- W4313303693 hasRelatedWork W2067778584 @default.
- W4313303693 hasRelatedWork W2085703916 @default.
- W4313303693 hasRelatedWork W2089085266 @default.