• W4313361146 abstract "The authors developed a nanocomposite using polypropylene (PP) and graphene nanoplatelets (GNPs) with a melt mixing method. Virgin PP was filled with three sets of GNPs with a fixed thickness (15 nm) and surface area (50–80 m2/g). The selected H-type GNPs had three different sizes of 5, 15 and 25 µm. The nanocomposites were made by loading GNPs at 1, 2 and 3 wt.%. Mechanical analysis was carried out by performing tensile, flexural and impact strength tests. The crystalline, micro-structural, thermal and dynamic mechanical properties were assessed through XRD, FESEM, PLM, DSC, TGA and DMA tests. It was observed that all three types of GNPs boosted the mechanical strength of the polymer composite. Increasing the nanofiller size decreased the tensile strength and the tensile modulus, increased the flexural strength and flexural modulus, and increased the impact strength. Maximum tensile strength (≈41.18 MPa) resulted for the composite consisting 3 wt.% H5, whereas maximum flexural (≈50.931 MPa) and impact (≈42.88 J/m) strengths were observed for nanocomposite holding 3 wt.% H25. Graphene induced the PP’s crystalline phases and structure. An improvement in thermal stability was seen based on the results of onset degradation (TD) and melting (Tm) temperatures. Graphene increased the crystallization (Tc) temperatures, and acted like a nucleating agent. The experimental analysis indicated that the lateral size of graphene plays an important role for the nanocomposite’s homogeneity. It was noted that the small-sized GNPs improved dispersion and decreased agglomeration. Thus overall, small-sized GNPs are preferable, and increasing the lateral size hardly establishes feasible characteristics in the nanocomposite." @default.
• W4313361146 created "2023-01-06" @default.
• W4313361146 creator A5000311949 @default.
• W4313361146 creator A5004865369 @default.
• W4313361146 creator A5023509242 @default.
• W4313361146 creator A5032193893 @default.
• W4313361146 creator A5060467030 @default.
• W4313361146 creator A5065497279 @default.
• W4313361146 date "2022-12-29" @default.
• W4313361146 modified "2023-09-30" @default.
• W4313361146 title "Polypropylene and Graphene Nanocomposites: Effects of Selected 2D-Nanofiller’s Plate Sizes on Fundamental Physicochemical Properties" @default.
• W4313361146 cites W1605814817 @default.
• W4313361146 cites W1791645330 @default.
• W4313361146 cites W1964526609 @default.
• W4313361146 cites W1973998203 @default.
• W4313361146 cites W1975748828 @default.
• W4313361146 cites W1989668096 @default.
• W4313361146 cites W2005191545 @default.
• W4313361146 cites W2010431922 @default.
• W4313361146 cites W2011445141 @default.
• W4313361146 cites W2013060429 @default.
• W4313361146 cites W2014442686 @default.
• W4313361146 cites W2031132442 @default.
• W4313361146 cites W2032891525 @default.
• W4313361146 cites W2047316652 @default.
• W4313361146 cites W2048046484 @default.
• W4313361146 cites W2048827351 @default.
• W4313361146 cites W2050774563 @default.
• W4313361146 cites W2057611100 @default.
• W4313361146 cites W2062336986 @default.
• W4313361146 cites W2065794617 @default.
• W4313361146 cites W2067761461 @default.
• W4313361146 cites W2086458195 @default.
• W4313361146 cites W2094021556 @default.
• W4313361146 cites W2099829294 @default.
• W4313361146 cites W2102913021 @default.
• W4313361146 cites W2118609172 @default.
• W4313361146 cites W2126863855 @default.
• W4313361146 cites W2158807856 @default.
• W4313361146 cites W2164583130 @default.
• W4313361146 cites W2296441357 @default.
• W4313361146 cites W2318854899 @default.
• W4313361146 cites W2328732911 @default.
• W4313361146 cites W2330088600 @default.
• W4313361146 cites W2533105832 @default.
• W4313361146 cites W2560194733 @default.
• W4313361146 cites W2574649257 @default.
• W4313361146 cites W2605857125 @default.
• W4313361146 cites W2736441330 @default.
• W4313361146 cites W2737313588 @default.
• W4313361146 cites W2752380553 @default.
• W4313361146 cites W2755393621 @default.
• W4313361146 cites W2760485035 @default.
• W4313361146 cites W2765151262 @default.
• W4313361146 cites W2801704119 @default.
• W4313361146 cites W2887174548 @default.
• W4313361146 cites W2904642643 @default.
• W4313361146 cites W2905357128 @default.
• W4313361146 cites W2954661934 @default.
• W4313361146 cites W2963961725 @default.
• W4313361146 cites W2990431722 @default.
• W4313361146 cites W2994081623 @default.
• W4313361146 cites W3008504985 @default.
• W4313361146 cites W3037740548 @default.
• W4313361146 cites W3083973746 @default.
• W4313361146 cites W3092918154 @default.
• W4313361146 cites W3109908929 @default.
• W4313361146 cites W3118753383 @default.
• W4313361146 cites W3120493541 @default.
• W4313361146 cites W3180058769 @default.
• W4313361146 cites W4238303723 @default.
• W4313361146 doi "https://doi.org/10.3390/inventions8010008" @default.
• W4313361146 hasPublicationYear "2022" @default.
• W4313361146 type Work @default.
• W4313361146 citedByCount "2" @default.
• W4313361146 countsByYear W43133611462023 @default.
• W4313361146 crossrefType "journal-article" @default.
• W4313361146 hasAuthorship W4313361146A5000311949 @default.
• W4313361146 hasAuthorship W4313361146A5004865369 @default.
• W4313361146 hasAuthorship W4313361146A5023509242 @default.
• W4313361146 hasAuthorship W4313361146A5032193893 @default.
• W4313361146 hasAuthorship W4313361146A5060467030 @default.
• W4313361146 hasAuthorship W4313361146A5065497279 @default.
• W4313361146 hasBestOaLocation W43133611461 @default.
• W4313361146 hasConcept C102267420 @default.
• W4313361146 hasConcept C104779481 @default.
• W4313361146 hasConcept C112950240 @default.
• W4313361146 hasConcept C127413603 @default.
• W4313361146 hasConcept C159985019 @default.
• W4313361146 hasConcept C171250308 @default.
• W4313361146 hasConcept C178405089 @default.
• W4313361146 hasConcept C192562407 @default.
• W4313361146 hasConcept C196029304 @default.
• W4313361146 hasConcept C2777973245 @default.
• W4313361146 hasConcept C30080830 @default.
• W4313361146 hasConcept C42360764 @default.
• W4313361146 hasConcept C521977710 @default.
• W4313361146 hasConcept C59061564 @default.

• next