- W4313367916 abstract "In this study, hydrostatic twist extrusion (HTE) has been introduced for processing relatively long ultrafine grained (UFG) bulk samples. By using high-pressure fluid surrounded the sample, surface contact between die and sample was eliminated. The high-pressure fluid causes high hydrostatic pressure, which leads to improvement of material properties and increased the aspect ratio of the sample (length/diameter). The HTE process was applied to commercial pure aluminum samples at room temperature, and then microstructure and mechanical properties were examined. The results demonstrate that after HTE process, the grain size was reduced from 54 µm to ∼800 nm, and microhardness was increased from 29.2 HV to 37.7 HV. Also, yield and ultimate strength were noticeably increased from 78 MPa and 103 MPa to 166 MPa and 175 MPa, respectively. This process seems to be very promising and interesting for the future industrial application." @default.
- W4313367916 created "2023-01-06" @default.
- W4313367916 creator A5000673974 @default.
- W4313367916 creator A5005077263 @default.
- W4313367916 creator A5023058513 @default.
- W4313367916 creator A5050377433 @default.
- W4313367916 creator A5051867217 @default.
- W4313367916 creator A5077854901 @default.
- W4313367916 date "2023-02-01" @default.
- W4313367916 modified "2023-09-27" @default.
- W4313367916 title "Hydrostatic twist extrusion (HTE) for processing relatively long ultrafine grained samples" @default.
- W4313367916 cites W1998227567 @default.
- W4313367916 cites W2019086014 @default.
- W4313367916 cites W2033281979 @default.
- W4313367916 cites W2091135947 @default.
- W4313367916 cites W2095558183 @default.
- W4313367916 cites W2123401672 @default.
- W4313367916 cites W2142434676 @default.
- W4313367916 cites W2486353571 @default.
- W4313367916 cites W2605854934 @default.
- W4313367916 cites W2793958049 @default.
- W4313367916 cites W2804981464 @default.
- W4313367916 cites W2909420304 @default.
- W4313367916 cites W3085337509 @default.
- W4313367916 cites W770834036 @default.
- W4313367916 doi "https://doi.org/10.1016/j.matlet.2022.133660" @default.
- W4313367916 hasPublicationYear "2023" @default.
- W4313367916 type Work @default.
- W4313367916 citedByCount "2" @default.
- W4313367916 countsByYear W43133679162023 @default.
- W4313367916 crossrefType "journal-article" @default.
- W4313367916 hasAuthorship W4313367916A5000673974 @default.
- W4313367916 hasAuthorship W4313367916A5005077263 @default.
- W4313367916 hasAuthorship W4313367916A5023058513 @default.
- W4313367916 hasAuthorship W4313367916A5050377433 @default.
- W4313367916 hasAuthorship W4313367916A5051867217 @default.
- W4313367916 hasAuthorship W4313367916A5077854901 @default.
- W4313367916 hasConcept C121332964 @default.
- W4313367916 hasConcept C134853933 @default.
- W4313367916 hasConcept C159985019 @default.
- W4313367916 hasConcept C165720898 @default.
- W4313367916 hasConcept C191897082 @default.
- W4313367916 hasConcept C192191005 @default.
- W4313367916 hasConcept C192562407 @default.
- W4313367916 hasConcept C2777618503 @default.
- W4313367916 hasConcept C2778958987 @default.
- W4313367916 hasConcept C2910081258 @default.
- W4313367916 hasConcept C513153333 @default.
- W4313367916 hasConcept C62520636 @default.
- W4313367916 hasConcept C87976508 @default.
- W4313367916 hasConcept C97355855 @default.
- W4313367916 hasConceptScore W4313367916C121332964 @default.
- W4313367916 hasConceptScore W4313367916C134853933 @default.
- W4313367916 hasConceptScore W4313367916C159985019 @default.
- W4313367916 hasConceptScore W4313367916C165720898 @default.
- W4313367916 hasConceptScore W4313367916C191897082 @default.
- W4313367916 hasConceptScore W4313367916C192191005 @default.
- W4313367916 hasConceptScore W4313367916C192562407 @default.
- W4313367916 hasConceptScore W4313367916C2777618503 @default.
- W4313367916 hasConceptScore W4313367916C2778958987 @default.
- W4313367916 hasConceptScore W4313367916C2910081258 @default.
- W4313367916 hasConceptScore W4313367916C513153333 @default.
- W4313367916 hasConceptScore W4313367916C62520636 @default.
- W4313367916 hasConceptScore W4313367916C87976508 @default.
- W4313367916 hasConceptScore W4313367916C97355855 @default.
- W4313367916 hasFunder F4320322243 @default.
- W4313367916 hasLocation W43133679161 @default.
- W4313367916 hasOpenAccess W4313367916 @default.
- W4313367916 hasPrimaryLocation W43133679161 @default.
- W4313367916 hasRelatedWork W1972254111 @default.
- W4313367916 hasRelatedWork W1976325869 @default.
- W4313367916 hasRelatedWork W2010582503 @default.
- W4313367916 hasRelatedWork W2063388647 @default.
- W4313367916 hasRelatedWork W2073931833 @default.
- W4313367916 hasRelatedWork W3015701583 @default.
- W4313367916 hasRelatedWork W3118359290 @default.
- W4313367916 hasRelatedWork W3119430064 @default.
- W4313367916 hasRelatedWork W3162861143 @default.
- W4313367916 hasRelatedWork W4324144252 @default.
- W4313367916 hasVolume "333" @default.
- W4313367916 isParatext "false" @default.
- W4313367916 isRetracted "false" @default.
- W4313367916 workType "article" @default.