- W4313531110 abstract "In this research, annealing treatment was performed on the Cu/Al corrugated clad sheets fabricated by the corrugated cold roll bonding (CCRB) process. Interface microstructure evolution, interface phase development, intermetallic compound (IMC) growth kinetics, interface bonding strength, and electrical resistivity at various positions of the Cu/Al corrugated clad sheet were investigated under different annealing conditions. The IMC layers (CuAl2, Cu9Al4 and CuAl) with uneven thickness were formed at the Cu/Al corrugated interface during the annealing process. Interface defects caused by shear deformation can effectively reduce the growth activation energies of IMC sub-layer at positions I (back waist), III (front waist), and IV (trough). On the contrary, the interface brittle layers and overlayer can slightly increase the activation energy at position II (peak). The sequence of growth activation energies for IMC sub-layer was QCuAl<QCu9Al4<QCuAl2. When Cu/Al corrugated clad sheet was annealed at 350 °C for 30 min, the recrystallization degree of Al plate at position III (front waist) was higher than the position II (peak), which was mainly due to the severe plastic deformation at the front waist position. Meanwhile, the transformation from low angle grain boundaries (LAGBs) to high angle grain boundaries (HAGBs) of the Al plate was more likely to occur at position III (front waist). Interface shear strength presented wavy distribution along the interface when the Cu/Al corrugated clad sheet was annealed at 350 °C for different times. With the increase of annealing time, the average shear strength first increased and then decreased rapidly. When the annealing time was 60 min, the average shear strength reached the maximum value of 45.61 MPa, and the average electrical resistivity reduced to the minimum value of 11.56 × 10−8 Ω m. Considering the double influence of annealing process on bonding strength and electrical resistivity, it was recommended that the Cu/Al corrugated clad sheet be annealed at 350 °C for 60 min." @default.
- W4313531110 created "2023-01-06" @default.
- W4313531110 creator A5000399610 @default.
- W4313531110 creator A5017111117 @default.
- W4313531110 creator A5052925180 @default.
- W4313531110 creator A5058017611 @default.
- W4313531110 creator A5068105992 @default.
- W4313531110 creator A5080657334 @default.
- W4313531110 date "2023-03-01" @default.
- W4313531110 modified "2023-09-28" @default.
- W4313531110 title "Effect of annealing process on interface microstructure and mechanical property of the Cu/Al corrugated clad sheet" @default.
- W4313531110 cites W1968464185 @default.
- W4313531110 cites W1993260870 @default.
- W4313531110 cites W1995862496 @default.
- W4313531110 cites W1997875013 @default.
- W4313531110 cites W2000637463 @default.
- W4313531110 cites W2005157818 @default.
- W4313531110 cites W2024207393 @default.
- W4313531110 cites W2033862491 @default.
- W4313531110 cites W2044118633 @default.
- W4313531110 cites W2045924597 @default.
- W4313531110 cites W2076018041 @default.
- W4313531110 cites W2093497848 @default.
- W4313531110 cites W2112871628 @default.
- W4313531110 cites W2522898769 @default.
- W4313531110 cites W2568221858 @default.
- W4313531110 cites W2604417214 @default.
- W4313531110 cites W2809546927 @default.
- W4313531110 cites W2896487431 @default.
- W4313531110 cites W2940864866 @default.
- W4313531110 cites W2950402495 @default.
- W4313531110 cites W2972282507 @default.
- W4313531110 cites W2975494598 @default.
- W4313531110 cites W2998754186 @default.
- W4313531110 cites W3034750202 @default.
- W4313531110 cites W3119766571 @default.
- W4313531110 cites W3135707298 @default.
- W4313531110 cites W3154859756 @default.
- W4313531110 cites W4200025339 @default.
- W4313531110 cites W4200574774 @default.
- W4313531110 cites W4281250614 @default.
- W4313531110 doi "https://doi.org/10.1016/j.jmrt.2022.12.188" @default.
- W4313531110 hasPublicationYear "2023" @default.
- W4313531110 type Work @default.
- W4313531110 citedByCount "3" @default.
- W4313531110 countsByYear W43135311102023 @default.
- W4313531110 crossrefType "journal-article" @default.
- W4313531110 hasAuthorship W4313531110A5000399610 @default.
- W4313531110 hasAuthorship W4313531110A5017111117 @default.
- W4313531110 hasAuthorship W4313531110A5052925180 @default.
- W4313531110 hasAuthorship W4313531110A5058017611 @default.
- W4313531110 hasAuthorship W4313531110A5068105992 @default.
- W4313531110 hasAuthorship W4313531110A5080657334 @default.
- W4313531110 hasBestOaLocation W43135311101 @default.
- W4313531110 hasConcept C159985019 @default.
- W4313531110 hasConcept C191897082 @default.
- W4313531110 hasConcept C192562407 @default.
- W4313531110 hasConcept C27501479 @default.
- W4313531110 hasConcept C2777777420 @default.
- W4313531110 hasConcept C2777855556 @default.
- W4313531110 hasConcept C2780026712 @default.
- W4313531110 hasConcept C47908070 @default.
- W4313531110 hasConcept C87976508 @default.
- W4313531110 hasConceptScore W4313531110C159985019 @default.
- W4313531110 hasConceptScore W4313531110C191897082 @default.
- W4313531110 hasConceptScore W4313531110C192562407 @default.
- W4313531110 hasConceptScore W4313531110C27501479 @default.
- W4313531110 hasConceptScore W4313531110C2777777420 @default.
- W4313531110 hasConceptScore W4313531110C2777855556 @default.
- W4313531110 hasConceptScore W4313531110C2780026712 @default.
- W4313531110 hasConceptScore W4313531110C47908070 @default.
- W4313531110 hasConceptScore W4313531110C87976508 @default.
- W4313531110 hasLocation W43135311101 @default.
- W4313531110 hasOpenAccess W4313531110 @default.
- W4313531110 hasPrimaryLocation W43135311101 @default.
- W4313531110 hasRelatedWork W1985813699 @default.
- W4313531110 hasRelatedWork W1999552040 @default.
- W4313531110 hasRelatedWork W2001338098 @default.
- W4313531110 hasRelatedWork W2010733322 @default.
- W4313531110 hasRelatedWork W2050291672 @default.
- W4313531110 hasRelatedWork W2058945371 @default.
- W4313531110 hasRelatedWork W2087317069 @default.
- W4313531110 hasRelatedWork W2089251307 @default.
- W4313531110 hasRelatedWork W2766515653 @default.
- W4313531110 hasRelatedWork W3133227197 @default.
- W4313531110 hasVolume "23" @default.
- W4313531110 isParatext "false" @default.
- W4313531110 isRetracted "false" @default.
- W4313531110 workType "article" @default.