- W4313574140 abstract "The microstructural characteristics and mechanical properties of friction stir lap welding (FSLW) of thin Al-clad Al (1.5 mm) and ultra-thin Al-clad mild steel (0.7 mm) sheets are experimentally investigated. Optical microscopic observation confirms that the FSLW joints are successfully fabricated without noticeable joining defects, such as cracks and hooks. The material flow is correlated with the silicon (Si) element distribution in the stir zone (SZ). The distribution of Si indicates that material flow is asymmetrical between the advancing side (AS) and the retreating side (RS) of the SZ. The tensile test result shows that all the FSLW joints fracture from the Al-clad Al side of the joints. During the fatigue tests, two different crack propagation modes (vertical crack in the Al-clad Al loading side; horizontal crack in the Al-clad mild steel loading side) are observed simultaneously due to the combined effect of the asymmetric geometry of the FSLW joint and the different loading configurations. The results of fatigue tests suggest that the asymmetric microstructure of the joint retards the propagation of a vertical crack in the Al-clad Al loading side for the RS-loaded FSLW joint. As a result, the fatigue life of the RS-loaded FSLW joint becomes clearly higher than that of the AS-loaded FSLW joint." @default.
- W4313574140 created "2023-01-06" @default.
- W4313574140 creator A5007748197 @default.
- W4313574140 creator A5023883586 @default.
- W4313574140 creator A5053683357 @default.
- W4313574140 creator A5068328902 @default.
- W4313574140 creator A5070268195 @default.
- W4313574140 creator A5073496992 @default.
- W4313574140 date "2023-01-01" @default.
- W4313574140 modified "2023-10-16" @default.
- W4313574140 title "Effects of the microstructure on the fatigue fracture of friction stir lap welded Al-clad Al and Al-clad steel sheets" @default.
- W4313574140 cites W1971214524 @default.
- W4313574140 cites W1974172839 @default.
- W4313574140 cites W1983964721 @default.
- W4313574140 cites W1987142894 @default.
- W4313574140 cites W1989754081 @default.
- W4313574140 cites W2009005097 @default.
- W4313574140 cites W2041132840 @default.
- W4313574140 cites W2041278275 @default.
- W4313574140 cites W2060268334 @default.
- W4313574140 cites W2065963174 @default.
- W4313574140 cites W2068922450 @default.
- W4313574140 cites W2071544158 @default.
- W4313574140 cites W2072825430 @default.
- W4313574140 cites W2103431346 @default.
- W4313574140 cites W2202044525 @default.
- W4313574140 cites W2318505539 @default.
- W4313574140 cites W2739955896 @default.
- W4313574140 cites W2766591618 @default.
- W4313574140 cites W2769421075 @default.
- W4313574140 cites W2794399742 @default.
- W4313574140 cites W2808194302 @default.
- W4313574140 cites W2948742003 @default.
- W4313574140 cites W2966825548 @default.
- W4313574140 cites W2995853241 @default.
- W4313574140 cites W3005413504 @default.
- W4313574140 cites W3081237731 @default.
- W4313574140 cites W3184316977 @default.
- W4313574140 cites W3190675770 @default.
- W4313574140 cites W3192895813 @default.
- W4313574140 cites W4200574774 @default.
- W4313574140 cites W4214667114 @default.
- W4313574140 cites W4285025086 @default.
- W4313574140 doi "https://doi.org/10.1016/j.jmrt.2022.12.103" @default.
- W4313574140 hasPublicationYear "2023" @default.
- W4313574140 type Work @default.
- W4313574140 citedByCount "5" @default.
- W4313574140 countsByYear W43135741402023 @default.
- W4313574140 crossrefType "journal-article" @default.
- W4313574140 hasAuthorship W4313574140A5007748197 @default.
- W4313574140 hasAuthorship W4313574140A5023883586 @default.
- W4313574140 hasAuthorship W4313574140A5053683357 @default.
- W4313574140 hasAuthorship W4313574140A5068328902 @default.
- W4313574140 hasAuthorship W4313574140A5070268195 @default.
- W4313574140 hasAuthorship W4313574140A5073496992 @default.
- W4313574140 hasBestOaLocation W43135741401 @default.
- W4313574140 hasConcept C112950240 @default.
- W4313574140 hasConcept C127413603 @default.
- W4313574140 hasConcept C159985019 @default.
- W4313574140 hasConcept C185324459 @default.
- W4313574140 hasConcept C18555067 @default.
- W4313574140 hasConcept C192562407 @default.
- W4313574140 hasConcept C19474535 @default.
- W4313574140 hasConcept C40367268 @default.
- W4313574140 hasConcept C43369102 @default.
- W4313574140 hasConcept C59085676 @default.
- W4313574140 hasConcept C66938386 @default.
- W4313574140 hasConcept C87976508 @default.
- W4313574140 hasConceptScore W4313574140C112950240 @default.
- W4313574140 hasConceptScore W4313574140C127413603 @default.
- W4313574140 hasConceptScore W4313574140C159985019 @default.
- W4313574140 hasConceptScore W4313574140C185324459 @default.
- W4313574140 hasConceptScore W4313574140C18555067 @default.
- W4313574140 hasConceptScore W4313574140C192562407 @default.
- W4313574140 hasConceptScore W4313574140C19474535 @default.
- W4313574140 hasConceptScore W4313574140C40367268 @default.
- W4313574140 hasConceptScore W4313574140C43369102 @default.
- W4313574140 hasConceptScore W4313574140C59085676 @default.
- W4313574140 hasConceptScore W4313574140C66938386 @default.
- W4313574140 hasConceptScore W4313574140C87976508 @default.
- W4313574140 hasFunder F4320321408 @default.
- W4313574140 hasFunder F4320321681 @default.
- W4313574140 hasFunder F4320322030 @default.
- W4313574140 hasFunder F4320322120 @default.
- W4313574140 hasFunder F4320328359 @default.
- W4313574140 hasLocation W43135741401 @default.
- W4313574140 hasOpenAccess W4313574140 @default.
- W4313574140 hasPrimaryLocation W43135741401 @default.
- W4313574140 hasRelatedWork W1991246690 @default.
- W4313574140 hasRelatedWork W2018203961 @default.
- W4313574140 hasRelatedWork W2364643376 @default.
- W4313574140 hasRelatedWork W2378652548 @default.
- W4313574140 hasRelatedWork W2385153745 @default.
- W4313574140 hasRelatedWork W2390961626 @default.
- W4313574140 hasRelatedWork W3038595124 @default.
- W4313574140 hasRelatedWork W3045391421 @default.
- W4313574140 hasRelatedWork W3135949456 @default.
- W4313574140 hasRelatedWork W4382357740 @default.