• W4313585570 abstract "A low-carbon medium manganese steel (0.12C-3.13Mn) containing Cr, Ni, Mo, V, and Cu elements was designed to replace the AISI 4330 steel applied in the oil and gas industry. The mechanical properties, microstructures, and fatigue crack growth rate were comparatively analyzed using uniaxial tension tests, microstructure characterization, and compact tension with fatigue crack growth characterization. The results showed that the ductility and -40 °C impact energy of 0.12C-3.13Mn steel were better than AISI 4330 steel (from 115 J to 179 J), while the yield strength of 957 MPa of the former was lower than the latter of 1060 MPa after being subjected to the same tempering process. The microstructure of 0.12C-3.13Mn steel was composed of a mixture of tempered martensite, reversed austenite, and nanosized precipitation particles, while the microstructure of S4330 steel contained ferrite and large-size Fe3C with lath and near-spherical morphologies. Compared to Cr-rich Fe3C, (V, Mo)C and Cu-rich particles have smaller sizes and, thus, provide more strengthening increment, leading to a higher yield ratio. The impressive fatigue-resistance property was obtained in 0.12C-3.13Mn steel because the threshold value was 5.23 MPa*m1/2 compared to the value of 4.88 MPa*m1/2 for S4330 steel. Even if the fatigue crack grew, the stress intensity factor range of 0.12C-3.13Mn steel was obviously wider than that of AISI 4330 steel due to the presence of reversed austenite and secondary cracks. Overall, the AISI 4330 steel could be replaced with the designed 0.12C-3.13Mn steel due to the similar strength and better ductility, low-temperature toughness, and fatigue-resistance property." @default.
• W4313585570 created "2023-01-06" @default.
• W4313585570 creator A5000297003 @default.
• W4313585570 creator A5055528771 @default.
• W4313585570 creator A5069936486 @default.
• W4313585570 creator A5084033431 @default.
• W4313585570 date "2023-01-04" @default.
• W4313585570 modified "2023-09-26" @default.
• W4313585570 title "Superior Comprehensive Mechanical Properties of a Low-Carbon Medium Manganese Steel for Replacing AISI 4330 Steel in the Oil and Gas Industry" @default.
• W4313585570 cites W1974641013 @default.
• W4313585570 cites W1978957662 @default.
• W4313585570 cites W2006120386 @default.
• W4313585570 cites W2009582077 @default.
• W4313585570 cites W2016304918 @default.
• W4313585570 cites W2018326592 @default.
• W4313585570 cites W2018801405 @default.
• W4313585570 cites W2019144156 @default.
• W4313585570 cites W2020792034 @default.
• W4313585570 cites W2023172348 @default.
• W4313585570 cites W2027496031 @default.
• W4313585570 cites W2046691345 @default.
• W4313585570 cites W2048791416 @default.
• W4313585570 cites W2053731163 @default.
• W4313585570 cites W2056614793 @default.
• W4313585570 cites W2093937583 @default.
• W4313585570 cites W2114835486 @default.
• W4313585570 cites W2149106585 @default.
• W4313585570 cites W2461172721 @default.
• W4313585570 cites W252253137 @default.
• W4313585570 cites W2565532520 @default.
• W4313585570 cites W2732186053 @default.
• W4313585570 cites W2771240111 @default.
• W4313585570 cites W2884561938 @default.
• W4313585570 cites W2890458854 @default.
• W4313585570 cites W2892717299 @default.
• W4313585570 cites W2942184423 @default.
• W4313585570 cites W2969278389 @default.
• W4313585570 cites W3093526915 @default.
• W4313585570 cites W3157241280 @default.
• W4313585570 cites W3188182697 @default.
• W4313585570 cites W3189660588 @default.
• W4313585570 cites W3193572038 @default.
• W4313585570 cites W3198992577 @default.
• W4313585570 cites W4200292096 @default.
• W4313585570 cites W4212957892 @default.
• W4313585570 cites W4213420936 @default.
• W4313585570 cites W4220722171 @default.
• W4313585570 cites W4221008187 @default.
• W4313585570 cites W4224029064 @default.
• W4313585570 cites W4283525899 @default.
• W4313585570 doi "https://doi.org/10.3390/ma16020490" @default.
• W4313585570 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/36676224" @default.
• W4313585570 hasPublicationYear "2023" @default.
• W4313585570 type Work @default.
• W4313585570 citedByCount "0" @default.
• W4313585570 crossrefType "journal-article" @default.
• W4313585570 hasAuthorship W4313585570A5000297003 @default.
• W4313585570 hasAuthorship W4313585570A5055528771 @default.
• W4313585570 hasAuthorship W4313585570A5069936486 @default.
• W4313585570 hasAuthorship W4313585570A5084033431 @default.
• W4313585570 hasBestOaLocation W43135855701 @default.
• W4313585570 hasConcept C159985019 @default.
• W4313585570 hasConcept C18747287 @default.
• W4313585570 hasConcept C191897082 @default.
• W4313585570 hasConcept C192562407 @default.
• W4313585570 hasConcept C20625102 @default.
• W4313585570 hasConcept C207948433 @default.
• W4313585570 hasConcept C2778560533 @default.
• W4313585570 hasConcept C2780430920 @default.
• W4313585570 hasConcept C37210646 @default.
• W4313585570 hasConcept C528890316 @default.
• W4313585570 hasConcept C87976508 @default.
• W4313585570 hasConcept C96288455 @default.
• W4313585570 hasConceptScore W4313585570C159985019 @default.
• W4313585570 hasConceptScore W4313585570C18747287 @default.
• W4313585570 hasConceptScore W4313585570C191897082 @default.
• W4313585570 hasConceptScore W4313585570C192562407 @default.
• W4313585570 hasConceptScore W4313585570C20625102 @default.
• W4313585570 hasConceptScore W4313585570C207948433 @default.
• W4313585570 hasConceptScore W4313585570C2778560533 @default.
• W4313585570 hasConceptScore W4313585570C2780430920 @default.
• W4313585570 hasConceptScore W4313585570C37210646 @default.
• W4313585570 hasConceptScore W4313585570C528890316 @default.
• W4313585570 hasConceptScore W4313585570C87976508 @default.
• W4313585570 hasConceptScore W4313585570C96288455 @default.
• W4313585570 hasIssue "2" @default.
• W4313585570 hasLocation W43135855701 @default.
• W4313585570 hasLocation W43135855702 @default.
• W4313585570 hasLocation W43135855703 @default.
• W4313585570 hasOpenAccess W4313585570 @default.
• W4313585570 hasPrimaryLocation W43135855701 @default.
• W4313585570 hasRelatedWork W1978865373 @default.
• W4313585570 hasRelatedWork W2003850019 @default.
• W4313585570 hasRelatedWork W2052632983 @default.
• W4313585570 hasRelatedWork W2357178173 @default.
• W4313585570 hasRelatedWork W2360953530 @default.
• W4313585570 hasRelatedWork W2391903753 @default.
• W4313585570 hasRelatedWork W25262218 @default.

• next