• W4313647519 abstract "Microstructural differences through the thickness have always been an attention focus for large-scale steel structures, since they could significantly influence fatigue crack propagation (FCP) characteristics. Here, the effects of microstructure in FCP behaviors of 42CrMo steel were analyzed with emphasis on two different tempered sorbite/bainite (TS/B) microstructures: (i) fine TS/B structures (M42); (ii) coarse TS/B structures (M52). The results show that the FCP rate is relatively slower for M52 than for M42 in the regime through the later stage of near-threshold (I-L) to the early stage of Paris-regime (Ⅱ-E) with low ΔK, but is fairly similar for the two cases in the other ΔK regimes. Under relatively low ΔK, the FCP path of M52 is more tortuous with numerous micro-cracks in B and larger-sized crack deflections at the carbides and boundaries compared to M42, especially in the I-L where fatigue micro-cracks can deflect at the single coarse carbide, thereby resulting in roughness-induced crack closure and crack retardation behavior. Theoretical analysis shows that FCP behaviors are closely related to the cyclic plastic region size (Δrp) at the crack-tip. In the early stage of near-threshold region, Δrp is restricted within a grain-size scale for both steels, thus leading to a similar FCP rate. However, from the I-L to the Ⅱ-E, coarse B/ferrite-grains in M52 are always larger than the Δrp of fatigue crack-tip, and thereby lead to numerous micro-cracks formation and crack deflections at the carbides and B boundaries, inducing crack closure. In the later stage of Paris region, B/ferrite-grains in the two cases are much smaller than Δrp, so that FCP behaviors depend on the microstructure group effects, or overall strength and fracture toughness of materials, which cause the close FCP rate." @default.
• W4313647519 created "2023-01-07" @default.
• W4313647519 creator A5019704236 @default.
• W4313647519 creator A5045710908 @default.
• W4313647519 creator A5050201432 @default.
• W4313647519 creator A5053211273 @default.
• W4313647519 creator A5082149046 @default.
• W4313647519 creator A5090431643 @default.
• W4313647519 date "2023-02-01" @default.
• W4313647519 modified "2023-10-11" @default.
• W4313647519 title "Fatigue crack growth behavior of 42CrMo high-strength steel with tempered sorbite/bainite microstructures: Roles of grain and constituent in microstructures" @default.
• W4313647519 cites W1969819694 @default.
• W4313647519 cites W1971974144 @default.
• W4313647519 cites W1973451272 @default.
• W4313647519 cites W1995819959 @default.
• W4313647519 cites W2004422948 @default.
• W4313647519 cites W2004801921 @default.
• W4313647519 cites W2008150261 @default.
• W4313647519 cites W2013856337 @default.
• W4313647519 cites W2019019629 @default.
• W4313647519 cites W2041611750 @default.
• W4313647519 cites W2041649187 @default.
• W4313647519 cites W2062190220 @default.
• W4313647519 cites W2062613656 @default.
• W4313647519 cites W2065326787 @default.
• W4313647519 cites W2081364660 @default.
• W4313647519 cites W2088250839 @default.
• W4313647519 cites W2094334248 @default.
• W4313647519 cites W2124362083 @default.
• W4313647519 cites W2124890223 @default.
• W4313647519 cites W2164309899 @default.
• W4313647519 cites W2175869387 @default.
• W4313647519 cites W2291199434 @default.
• W4313647519 cites W2348219025 @default.
• W4313647519 cites W2494740053 @default.
• W4313647519 cites W2582380507 @default.
• W4313647519 cites W2732696779 @default.
• W4313647519 cites W2791019155 @default.
• W4313647519 cites W2794215202 @default.
• W4313647519 cites W2799881376 @default.
• W4313647519 cites W2802828801 @default.
• W4313647519 cites W2887074141 @default.
• W4313647519 cites W2940214090 @default.
• W4313647519 cites W2981355582 @default.
• W4313647519 cites W3007546751 @default.
• W4313647519 cites W3010442556 @default.
• W4313647519 cites W3097250280 @default.
• W4313647519 cites W3112181328 @default.
• W4313647519 cites W3165961699 @default.
• W4313647519 cites W3188008349 @default.
• W4313647519 cites W3193791902 @default.
• W4313647519 cites W3216960352 @default.
• W4313647519 cites W4200124753 @default.
• W4313647519 cites W4206463343 @default.
• W4313647519 cites W4281784766 @default.
• W4313647519 cites W4293231317 @default.
• W4313647519 cites W431186153 @default.
• W4313647519 cites W4375834719 @default.
• W4313647519 doi "https://doi.org/10.1016/j.engfracmech.2023.109051" @default.
• W4313647519 hasPublicationYear "2023" @default.
• W4313647519 type Work @default.
• W4313647519 citedByCount "3" @default.
• W4313647519 countsByYear W43136475192023 @default.
• W4313647519 crossrefType "journal-article" @default.
• W4313647519 hasAuthorship W4313647519A5019704236 @default.
• W4313647519 hasAuthorship W4313647519A5045710908 @default.
• W4313647519 hasAuthorship W4313647519A5050201432 @default.
• W4313647519 hasAuthorship W4313647519A5053211273 @default.
• W4313647519 hasAuthorship W4313647519A5082149046 @default.
• W4313647519 hasAuthorship W4313647519A5090431643 @default.
• W4313647519 hasConcept C159985019 @default.
• W4313647519 hasConcept C18747287 @default.
• W4313647519 hasConcept C191897082 @default.
• W4313647519 hasConcept C192191005 @default.
• W4313647519 hasConcept C192562407 @default.
• W4313647519 hasConcept C37210646 @default.
• W4313647519 hasConcept C44125496 @default.
• W4313647519 hasConcept C47908070 @default.
• W4313647519 hasConcept C5335593 @default.
• W4313647519 hasConcept C59085676 @default.
• W4313647519 hasConcept C75512024 @default.
• W4313647519 hasConcept C87976508 @default.
• W4313647519 hasConceptScore W4313647519C159985019 @default.
• W4313647519 hasConceptScore W4313647519C18747287 @default.
• W4313647519 hasConceptScore W4313647519C191897082 @default.
• W4313647519 hasConceptScore W4313647519C192191005 @default.
• W4313647519 hasConceptScore W4313647519C192562407 @default.
• W4313647519 hasConceptScore W4313647519C37210646 @default.
• W4313647519 hasConceptScore W4313647519C44125496 @default.
• W4313647519 hasConceptScore W4313647519C47908070 @default.
• W4313647519 hasConceptScore W4313647519C5335593 @default.
• W4313647519 hasConceptScore W4313647519C59085676 @default.
• W4313647519 hasConceptScore W4313647519C75512024 @default.
• W4313647519 hasConceptScore W4313647519C87976508 @default.
• W4313647519 hasLocation W43136475191 @default.
• W4313647519 hasOpenAccess W4313647519 @default.
• W4313647519 hasPrimaryLocation W43136475191 @default.
• W4313647519 hasRelatedWork W1502202100 @default.

• next