• W4315697766 abstract "A comparative study of VT-1.0 titanium boriding, carboboronizing and borosiliconizing methods was carried out in order to increase wear resistance in aggressive environments at elevated temperatures. The microstructure of diffusion coatings was investigated, their thickness and microhardness were determined. Diffusion saturation of 10×10×25 mm VT-1.0 titanium samples was carried out from saturating coatings based on boron carbide. Process temperature of 950 °C, and saturation time of 1.5 h were used as saturation conditions. At the end of high-temperature exposure, samples were removed from the furnace and cooled in air to room temperature, cleaned from saturating coatings with wooden spatulas, and boiled in the soap and soda solution for 1 h. A continuous diffusion layer 80–100 μm thick forms on the titanium surface. The borosiliconized diffusion layer obtained by titanium saturation from the mixture of 45%B 4 C–5%Na 2 B 4 O 7 –22%Si–5%NaF–3%NaCl– 20%CrB 2 has a higher microhardness: 1520 HV 0.1 versus 1280 HV 0.1 for carboboride one and 1120 HV 0.1 for boride one. In this case, boride and carboboride coatings, obtained, respectively, by saturation from 45%B 4 C–5%Na 2 B 4 O 7 –5%NaF–25%Al 2 O 3 –20%CrB 2 and 70%B 4 C– 5%Na 2 B 4 O 7 –5%NaF–20%CrB 2 coatings have a pronounced zonal structure. The upper zone of these coatings having high microhardness also features high brittleness indicators, which makes it impossible to accurately measure microhardness distribution due to chipping and cracking at microhardness measurement points. The qualitative composition of coatings on titanium was studied by X-ray diffraction using the DRON-6 X-ray diffractometer in filtered CuK α radiation (λ = 1.5418 Å) in the angle range of 2θ = 20÷80°. The diffusion coating exhibits reflections of titanium carbide, chromium and titanium borides, and a certain amount of the Cr 2 Ti intermetallic compound. Boride phases of chromium and titanium refer to high boron phases with high specific boron content: TiB, CrB, Ti 2 B 5 , Ti 3 B 4 и Cr 2 B 3 ." @default.
• W4315697766 created "2023-01-12" @default.
• W4315697766 creator A5041347384 @default.
• W4315697766 creator A5050830281 @default.
• W4315697766 creator A5066231116 @default.
• W4315697766 creator A5073315272 @default.
• W4315697766 creator A5076601284 @default.
• W4315697766 date "2022-02-19" @default.
• W4315697766 modified "2023-09-27" @default.
• W4315697766 title "Influence of the composition of a boron-containing active medium in the form of a coating on the structure and properties of a diffusion layer on titanium parts" @default.
• W4315697766 cites W1529783523 @default.
• W4315697766 cites W1972444061 @default.
• W4315697766 cites W1984330126 @default.
• W4315697766 cites W1999246039 @default.
• W4315697766 cites W2063059377 @default.
• W4315697766 cites W2090034522 @default.
• W4315697766 cites W2142054985 @default.
• W4315697766 cites W2167088850 @default.
• W4315697766 cites W2418773996 @default.
• W4315697766 cites W2516327777 @default.
• W4315697766 cites W2560098880 @default.
• W4315697766 cites W2735483343 @default.
• W4315697766 cites W2807743577 @default.
• W4315697766 cites W2908359672 @default.
• W4315697766 cites W2912629472 @default.
• W4315697766 cites W2944564888 @default.
• W4315697766 cites W2948374528 @default.
• W4315697766 cites W3007382929 @default.
• W4315697766 cites W3015051268 @default.
• W4315697766 cites W3023489673 @default.
• W4315697766 cites W3047388235 @default.
• W4315697766 cites W3081947235 @default.
• W4315697766 cites W3091842603 @default.
• W4315697766 cites W3114402112 @default.
• W4315697766 cites W3134214441 @default.
• W4315697766 cites W3156447535 @default.
• W4315697766 cites W3194835810 @default.
• W4315697766 cites W586619846 @default.
• W4315697766 doi "https://doi.org/10.17073/0021-3438-2022-1-60-66" @default.
• W4315697766 hasPublicationYear "2022" @default.
• W4315697766 type Work @default.
• W4315697766 citedByCount "0" @default.
• W4315697766 crossrefType "journal-article" @default.
• W4315697766 hasAuthorship W4315697766A5041347384 @default.
• W4315697766 hasAuthorship W4315697766A5050830281 @default.
• W4315697766 hasAuthorship W4315697766A5066231116 @default.
• W4315697766 hasAuthorship W4315697766A5073315272 @default.
• W4315697766 hasAuthorship W4315697766A5076601284 @default.
• W4315697766 hasConcept C113196181 @default.
• W4315697766 hasConcept C114614502 @default.
• W4315697766 hasConcept C121332964 @default.
• W4315697766 hasConcept C159985019 @default.
• W4315697766 hasConcept C165720898 @default.
• W4315697766 hasConcept C178790620 @default.
• W4315697766 hasConcept C185592680 @default.
• W4315697766 hasConcept C191897082 @default.
• W4315697766 hasConcept C192562407 @default.
• W4315697766 hasConcept C2776723582 @default.
• W4315697766 hasConcept C2779249216 @default.
• W4315697766 hasConcept C2781448156 @default.
• W4315697766 hasConcept C33923547 @default.
• W4315697766 hasConcept C43617362 @default.
• W4315697766 hasConcept C501308230 @default.
• W4315697766 hasConcept C504678139 @default.
• W4315697766 hasConcept C506065880 @default.
• W4315697766 hasConcept C69357855 @default.
• W4315697766 hasConcept C87976508 @default.
• W4315697766 hasConcept C97355855 @default.
• W4315697766 hasConcept C9930424 @default.
• W4315697766 hasConceptScore W4315697766C113196181 @default.
• W4315697766 hasConceptScore W4315697766C114614502 @default.
• W4315697766 hasConceptScore W4315697766C121332964 @default.
• W4315697766 hasConceptScore W4315697766C159985019 @default.
• W4315697766 hasConceptScore W4315697766C165720898 @default.
• W4315697766 hasConceptScore W4315697766C178790620 @default.
• W4315697766 hasConceptScore W4315697766C185592680 @default.
• W4315697766 hasConceptScore W4315697766C191897082 @default.
• W4315697766 hasConceptScore W4315697766C192562407 @default.
• W4315697766 hasConceptScore W4315697766C2776723582 @default.
• W4315697766 hasConceptScore W4315697766C2779249216 @default.
• W4315697766 hasConceptScore W4315697766C2781448156 @default.
• W4315697766 hasConceptScore W4315697766C33923547 @default.
• W4315697766 hasConceptScore W4315697766C43617362 @default.
• W4315697766 hasConceptScore W4315697766C501308230 @default.
• W4315697766 hasConceptScore W4315697766C504678139 @default.
• W4315697766 hasConceptScore W4315697766C506065880 @default.
• W4315697766 hasConceptScore W4315697766C69357855 @default.
• W4315697766 hasConceptScore W4315697766C87976508 @default.
• W4315697766 hasConceptScore W4315697766C97355855 @default.
• W4315697766 hasConceptScore W4315697766C9930424 @default.
• W4315697766 hasIssue "1" @default.
• W4315697766 hasLocation W43156977661 @default.
• W4315697766 hasOpenAccess W4315697766 @default.
• W4315697766 hasPrimaryLocation W43156977661 @default.
• W4315697766 hasRelatedWork W1966110301 @default.
• W4315697766 hasRelatedWork W2001108138 @default.
• W4315697766 hasRelatedWork W2009764845 @default.
• W4315697766 hasRelatedWork W2066753314 @default.

• next