- W4320001630 abstract "The effect of temperature on the compressive behavior and deformation mechanism of a Ni-based single crystal superalloy with low stacking fault energy was investigated in the temperature range from room temperature to 1000 °C. The results indicated that both the compressive behavior and deformation microstructure were temperature- dependent. There was a higher yield strength at room temperature and then the yield strength decreased at 600 °C. After that, the yield strength would increase continuously to the maximum at 800 °C and then decrease rapidly. Furthermore, the deformation mechanisms were revealed by transmission electron microscope observation. The dislocation tangle and dislocation pairs pile-up were the main reasons for the higher yield strength at room temperature. At 600 °C, the transition in the deformation mechanisms from anti-phase boundary shearing to stacking fault shearing accounted for the slight decrease of the yield strength. At 800 °C, the deformation mechanism was mainly controlled by stacking fault shearing and the reaction of stacking faults along different directions as well as Lomer−Cottrell locks was responsible for the maximum yield strength. Above 900 °C, the primary deformation mechanism was the by-passing of dislocations, although there were still some stacking faults. Finally, the temperature dependence of deformation mechanism and compressive behavior was discussed." @default.
- W4320001630 created "2023-02-11" @default.
- W4320001630 creator A5017932004 @default.
- W4320001630 creator A5018858170 @default.
- W4320001630 creator A5018872141 @default.
- W4320001630 creator A5032328621 @default.
- W4320001630 creator A5034917397 @default.
- W4320001630 creator A5035619653 @default.
- W4320001630 creator A5059884717 @default.
- W4320001630 creator A5071672663 @default.
- W4320001630 creator A5086335766 @default.
- W4320001630 date "2023-01-01" @default.
- W4320001630 modified "2023-10-18" @default.
- W4320001630 title "Temperature dependence of compressive behavior and deformation microstructure of a Ni-based single crystal superalloy with low stacking fault energy" @default.
- W4320001630 cites W1248417357 @default.
- W4320001630 cites W1720859809 @default.
- W4320001630 cites W1967953995 @default.
- W4320001630 cites W1974029880 @default.
- W4320001630 cites W1988141305 @default.
- W4320001630 cites W1993758565 @default.
- W4320001630 cites W2003728540 @default.
- W4320001630 cites W2009157576 @default.
- W4320001630 cites W2010788054 @default.
- W4320001630 cites W2017994586 @default.
- W4320001630 cites W2023552808 @default.
- W4320001630 cites W2030459137 @default.
- W4320001630 cites W2035933089 @default.
- W4320001630 cites W2068258375 @default.
- W4320001630 cites W2088858524 @default.
- W4320001630 cites W2089463430 @default.
- W4320001630 cites W2092992294 @default.
- W4320001630 cites W2102217281 @default.
- W4320001630 cites W2334079918 @default.
- W4320001630 cites W2478064740 @default.
- W4320001630 cites W2494523946 @default.
- W4320001630 cites W2526827254 @default.
- W4320001630 cites W2605484908 @default.
- W4320001630 cites W2612063982 @default.
- W4320001630 cites W2782076683 @default.
- W4320001630 cites W2797529373 @default.
- W4320001630 cites W2803951661 @default.
- W4320001630 cites W2897730941 @default.
- W4320001630 cites W2936267011 @default.
- W4320001630 cites W2944356753 @default.
- W4320001630 cites W2945371939 @default.
- W4320001630 cites W3046729934 @default.
- W4320001630 cites W3187859429 @default.
- W4320001630 cites W3198487503 @default.
- W4320001630 cites W3200214633 @default.
- W4320001630 doi "https://doi.org/10.1016/s1003-6326(22)66097-7" @default.
- W4320001630 hasPublicationYear "2023" @default.
- W4320001630 type Work @default.
- W4320001630 citedByCount "2" @default.
- W4320001630 countsByYear W43200016302023 @default.
- W4320001630 crossrefType "journal-article" @default.
- W4320001630 hasAuthorship W4320001630A5017932004 @default.
- W4320001630 hasAuthorship W4320001630A5018858170 @default.
- W4320001630 hasAuthorship W4320001630A5018872141 @default.
- W4320001630 hasAuthorship W4320001630A5032328621 @default.
- W4320001630 hasAuthorship W4320001630A5034917397 @default.
- W4320001630 hasAuthorship W4320001630A5035619653 @default.
- W4320001630 hasAuthorship W4320001630A5059884717 @default.
- W4320001630 hasAuthorship W4320001630A5071672663 @default.
- W4320001630 hasAuthorship W4320001630A5086335766 @default.
- W4320001630 hasBestOaLocation W43200016301 @default.
- W4320001630 hasConcept C121332964 @default.
- W4320001630 hasConcept C134121241 @default.
- W4320001630 hasConcept C152279782 @default.
- W4320001630 hasConcept C159122135 @default.
- W4320001630 hasConcept C159985019 @default.
- W4320001630 hasConcept C192562407 @default.
- W4320001630 hasConcept C204366326 @default.
- W4320001630 hasConcept C205539056 @default.
- W4320001630 hasConcept C207055975 @default.
- W4320001630 hasConcept C22372946 @default.
- W4320001630 hasConcept C2778536302 @default.
- W4320001630 hasConcept C30407753 @default.
- W4320001630 hasConcept C33347731 @default.
- W4320001630 hasConcept C39353612 @default.
- W4320001630 hasConcept C46141821 @default.
- W4320001630 hasConcept C87976508 @default.
- W4320001630 hasConcept C97355855 @default.
- W4320001630 hasConceptScore W4320001630C121332964 @default.
- W4320001630 hasConceptScore W4320001630C134121241 @default.
- W4320001630 hasConceptScore W4320001630C152279782 @default.
- W4320001630 hasConceptScore W4320001630C159122135 @default.
- W4320001630 hasConceptScore W4320001630C159985019 @default.
- W4320001630 hasConceptScore W4320001630C192562407 @default.
- W4320001630 hasConceptScore W4320001630C204366326 @default.
- W4320001630 hasConceptScore W4320001630C205539056 @default.
- W4320001630 hasConceptScore W4320001630C207055975 @default.
- W4320001630 hasConceptScore W4320001630C22372946 @default.
- W4320001630 hasConceptScore W4320001630C2778536302 @default.
- W4320001630 hasConceptScore W4320001630C30407753 @default.
- W4320001630 hasConceptScore W4320001630C33347731 @default.
- W4320001630 hasConceptScore W4320001630C39353612 @default.
- W4320001630 hasConceptScore W4320001630C46141821 @default.
- W4320001630 hasConceptScore W4320001630C87976508 @default.