- W4321116768 abstract "Neutron irradiation-induced microstructural changes in variants of austenitic stainless steels were characterized using the Angle Dispersive X-Ray Diffraction (ADXRD) technique with a synchrotron X-ray source of energy 14.968 keV (wavelength ∼0.82833 Å). SS 304 L(N), SS 316 L(N), and SS 316 materials were neutron-irradiated to low displacement damage levels (1–6.75 dpa) in the Fast Breeder Test Reactor at Kalpakkam at temperatures in the range ∼380 °C-400 °C. The effect of the irradiation-induced defects on X-ray diffraction peak profile parameters such as peak broadening, peak shift, and asymmetry were quantified and related to dislocation density. Peak broadening is found to increase as a function of dpa in most of the cases. Considering the highest dpa sample, lattice contraction has been shown by SS 304 L(N) and SS 316 whereas lattice expansion is exhibited by SS 316 L(N). Asymmetry in peak broadening is found to decrease in case of the highest dpa sample. Ferrite volume percent is seen to have increased as a function of dpa in SS 304 L(N) and SS 316 L(N) but not observed in SS 316. SS 304 L(N) has shown a greater propensity towards the austenite to ferrite transformation and 5 dpa sample has about 18 vol% of α-ferrite. However, in case of 5 dpa SS 316 L(N), ferrite content has increased to ∼4 vol% . The increase in yield strength was also related to the dislocation density amongst all three grades of stainless steel. SS 304 L(N) showed saturation in dislocation density and yield strength around 2 dpa whereas SS 316 L(N) showed linear behaviour up to the highest dpa." @default.
- W4321116768 created "2023-02-18" @default.
- W4321116768 creator A5022432210 @default.
- W4321116768 creator A5032303111 @default.
- W4321116768 creator A5057005091 @default.
- W4321116768 creator A5057931714 @default.
- W4321116768 creator A5071468737 @default.
- W4321116768 creator A5073155886 @default.
- W4321116768 date "2023-04-01" @default.
- W4321116768 modified "2023-09-27" @default.
- W4321116768 title "X-ray diffraction line profile analysis of defects in neutron-irradiated austenitic stainless steels at low displacement damage levels" @default.
- W4321116768 cites W114261502 @default.
- W4321116768 cites W1246012747 @default.
- W4321116768 cites W1969987170 @default.
- W4321116768 cites W1970536218 @default.
- W4321116768 cites W1970826471 @default.
- W4321116768 cites W1974641283 @default.
- W4321116768 cites W1985303445 @default.
- W4321116768 cites W1988061088 @default.
- W4321116768 cites W1993506931 @default.
- W4321116768 cites W1997405782 @default.
- W4321116768 cites W2001275151 @default.
- W4321116768 cites W2003504582 @default.
- W4321116768 cites W2015843302 @default.
- W4321116768 cites W2016017387 @default.
- W4321116768 cites W2019286457 @default.
- W4321116768 cites W2027111900 @default.
- W4321116768 cites W2027496031 @default.
- W4321116768 cites W2031026435 @default.
- W4321116768 cites W2040432202 @default.
- W4321116768 cites W2054293435 @default.
- W4321116768 cites W2056228148 @default.
- W4321116768 cites W2071407167 @default.
- W4321116768 cites W2078320474 @default.
- W4321116768 cites W2081550164 @default.
- W4321116768 cites W2083672906 @default.
- W4321116768 cites W2088732846 @default.
- W4321116768 cites W2089031539 @default.
- W4321116768 cites W2090336384 @default.
- W4321116768 cites W2090900346 @default.
- W4321116768 cites W2093526031 @default.
- W4321116768 cites W2130315953 @default.
- W4321116768 cites W2147133561 @default.
- W4321116768 cites W2150112771 @default.
- W4321116768 cites W2250292391 @default.
- W4321116768 cites W2295466063 @default.
- W4321116768 cites W2559060834 @default.
- W4321116768 cites W2562182823 @default.
- W4321116768 cites W2800076016 @default.
- W4321116768 cites W2901833182 @default.
- W4321116768 cites W29733610 @default.
- W4321116768 cites W3036707848 @default.
- W4321116768 cites W3081836197 @default.
- W4321116768 cites W3103623891 @default.
- W4321116768 cites W3139047277 @default.
- W4321116768 cites W3160163090 @default.
- W4321116768 cites W3165408188 @default.
- W4321116768 cites W4223538598 @default.
- W4321116768 cites W2106495589 @default.
- W4321116768 doi "https://doi.org/10.1016/j.jnucmat.2023.154338" @default.
- W4321116768 hasPublicationYear "2023" @default.
- W4321116768 type Work @default.
- W4321116768 citedByCount "0" @default.
- W4321116768 crossrefType "journal-article" @default.
- W4321116768 hasAuthorship W4321116768A5022432210 @default.
- W4321116768 hasAuthorship W4321116768A5032303111 @default.
- W4321116768 hasAuthorship W4321116768A5057005091 @default.
- W4321116768 hasAuthorship W4321116768A5057931714 @default.
- W4321116768 hasAuthorship W4321116768A5071468737 @default.
- W4321116768 hasAuthorship W4321116768A5073155886 @default.
- W4321116768 hasConcept C111337013 @default.
- W4321116768 hasConcept C113196181 @default.
- W4321116768 hasConcept C120665830 @default.
- W4321116768 hasConcept C121332964 @default.
- W4321116768 hasConcept C132612359 @default.
- W4321116768 hasConcept C152568617 @default.
- W4321116768 hasConcept C159122135 @default.
- W4321116768 hasConcept C159985019 @default.
- W4321116768 hasConcept C185544564 @default.
- W4321116768 hasConcept C185592680 @default.
- W4321116768 hasConcept C191897082 @default.
- W4321116768 hasConcept C192562407 @default.
- W4321116768 hasConcept C20625102 @default.
- W4321116768 hasConcept C207114421 @default.
- W4321116768 hasConcept C2779229422 @default.
- W4321116768 hasConcept C37210646 @default.
- W4321116768 hasConcept C43617362 @default.
- W4321116768 hasConcept C73585123 @default.
- W4321116768 hasConcept C87976508 @default.
- W4321116768 hasConcept C96288455 @default.
- W4321116768 hasConceptScore W4321116768C111337013 @default.
- W4321116768 hasConceptScore W4321116768C113196181 @default.
- W4321116768 hasConceptScore W4321116768C120665830 @default.
- W4321116768 hasConceptScore W4321116768C121332964 @default.
- W4321116768 hasConceptScore W4321116768C132612359 @default.
- W4321116768 hasConceptScore W4321116768C152568617 @default.
- W4321116768 hasConceptScore W4321116768C159122135 @default.
- W4321116768 hasConceptScore W4321116768C159985019 @default.