- W4323038401 abstract "In this study, metakaolin based geopolymer mixtures using granulated blast furnace slag and different sizes of quartz aggregate were thermally cured at 30–60–90°C for 4, 6, and 8 h. Sodium hydroxide and sodium silicate were used as alkali activators in the experiments. Early (1 d), and 28-days mechanical strengths, transport (capillarity) properties, unit weights at hardened stage, microstructural features of the mixes obtained at different curing time and curing temperature were observed. The compressive strength of the geopolymer mixtures was measured between 41.7–106.5 MPa, at early ages; and the 28 days compressive strength between 23.6–80.5 MPa. The flexural strengths varied between 7.2–22.9 MPa for 1 d. Increased the curing temperature and curing time tended to surge the mechanical properties of the mixtures while increasing aggregate size tended to decrease these properties. The unit weights of the samples at hardened stage are between 2256–2358.4 kg/m3. The capillary water absorption coefficient of the produced samples was measured as 0.015–0.059 kg/m2.min0.5. In matrix of the geopolymer mixture zeolitic phases and NASH structures were observed in XRD, SEM and FT-IR results. It was observed that quartz aggregate, blast furnace slag and metakaolin-based geopolymer with an early compressive strength of 106.28 MPa can be observed at short curing time as little as 6 h. Moreover, using experimental and theoretical approaches, photon and fast neutron radiation shielding properties of geopolymer mixtures were examined. Our results showed that the particle size reduction of Quartz aggregate improves the photon and neutron attenuation abilities of the mixture. Since the reduction in particle size enhances the radiation shielding properties as well as the mechanical strength, the produced geopolymer mixtures can be useful materials in the design of nuclear radiation facilities and spaces where advanced radiation applications are made." @default.
- W4323038401 created "2023-03-04" @default.
- W4323038401 creator A5010119885 @default.
- W4323038401 creator A5018191704 @default.
- W4323038401 creator A5026188554 @default.
- W4323038401 creator A5037416494 @default.
- W4323038401 creator A5038777802 @default.
- W4323038401 creator A5042598528 @default.
- W4323038401 creator A5088561774 @default.
- W4323038401 date "2023-03-03" @default.
- W4323038401 modified "2023-10-18" @default.
- W4323038401 title "A comprehensive characterization on geopolymer concretes with low content slag and quartz aggregates: the shielding features" @default.
- W4323038401 cites W1122819142 @default.
- W4323038401 cites W1435587914 @default.
- W4323038401 cites W1879899466 @default.
- W4323038401 cites W1921784816 @default.
- W4323038401 cites W1966946069 @default.
- W4323038401 cites W1968710188 @default.
- W4323038401 cites W1971097271 @default.
- W4323038401 cites W1974131402 @default.
- W4323038401 cites W1976526686 @default.
- W4323038401 cites W1988269990 @default.
- W4323038401 cites W1989524260 @default.
- W4323038401 cites W1991957090 @default.
- W4323038401 cites W1992183625 @default.
- W4323038401 cites W1999457110 @default.
- W4323038401 cites W2002273661 @default.
- W4323038401 cites W2010653115 @default.
- W4323038401 cites W2040812197 @default.
- W4323038401 cites W2047036241 @default.
- W4323038401 cites W2050802546 @default.
- W4323038401 cites W2054299673 @default.
- W4323038401 cites W2056371893 @default.
- W4323038401 cites W2064969593 @default.
- W4323038401 cites W2066218433 @default.
- W4323038401 cites W2070969134 @default.
- W4323038401 cites W2079408647 @default.
- W4323038401 cites W2082458175 @default.
- W4323038401 cites W2082856054 @default.
- W4323038401 cites W2087987532 @default.
- W4323038401 cites W2089136006 @default.
- W4323038401 cites W2092590736 @default.
- W4323038401 cites W2134983105 @default.
- W4323038401 cites W2182059990 @default.
- W4323038401 cites W226878523 @default.
- W4323038401 cites W2294724562 @default.
- W4323038401 cites W2419344547 @default.
- W4323038401 cites W2516429510 @default.
- W4323038401 cites W2518288186 @default.
- W4323038401 cites W2563246109 @default.
- W4323038401 cites W2602299867 @default.
- W4323038401 cites W2607436051 @default.
- W4323038401 cites W2608139855 @default.
- W4323038401 cites W2769737540 @default.
- W4323038401 cites W2769903461 @default.
- W4323038401 cites W2770300398 @default.
- W4323038401 cites W2788338336 @default.
- W4323038401 cites W2799683957 @default.
- W4323038401 cites W2802947689 @default.
- W4323038401 cites W2809588390 @default.
- W4323038401 cites W2893030228 @default.
- W4323038401 cites W2899795524 @default.
- W4323038401 cites W2903010831 @default.
- W4323038401 cites W2921602852 @default.
- W4323038401 cites W2953930841 @default.
- W4323038401 cites W2966968349 @default.
- W4323038401 cites W2980925533 @default.
- W4323038401 cites W3007139671 @default.
- W4323038401 cites W3008049559 @default.
- W4323038401 cites W3018195209 @default.
- W4323038401 cites W3126610247 @default.
- W4323038401 cites W3129051500 @default.
- W4323038401 cites W3138225051 @default.
- W4323038401 cites W3172364525 @default.
- W4323038401 cites W3180182061 @default.
- W4323038401 cites W3197570376 @default.
- W4323038401 cites W4220732691 @default.
- W4323038401 cites W4249228687 @default.
- W4323038401 cites W911610109 @default.
- W4323038401 doi "https://doi.org/10.1080/10420150.2023.2184363" @default.
- W4323038401 hasPublicationYear "2023" @default.
- W4323038401 type Work @default.
- W4323038401 citedByCount "0" @default.
- W4323038401 crossrefType "journal-article" @default.
- W4323038401 hasAuthorship W4323038401A5010119885 @default.
- W4323038401 hasAuthorship W4323038401A5018191704 @default.
- W4323038401 hasAuthorship W4323038401A5026188554 @default.
- W4323038401 hasAuthorship W4323038401A5037416494 @default.
- W4323038401 hasAuthorship W4323038401A5038777802 @default.
- W4323038401 hasAuthorship W4323038401A5042598528 @default.
- W4323038401 hasAuthorship W4323038401A5088561774 @default.
- W4323038401 hasConcept C126292034 @default.
- W4323038401 hasConcept C127413603 @default.
- W4323038401 hasConcept C132976073 @default.
- W4323038401 hasConcept C159985019 @default.
- W4323038401 hasConcept C178405089 @default.
- W4323038401 hasConcept C180145272 @default.
- W4323038401 hasConcept C192562407 @default.