- W4323647977 abstract "Aluminum 6xxx series alloys attract attention owing to their decent strength, formability and corrosion characteristics. Mechanical properties of these alloys can be altered via precipitation hardening by applying an aging treatment known as artificial aging (AA). This investigation was focused on the behavior of mechanical properties of EN AW 6082 alloy for various aging conditions. Mechanical property response for different heat treatment procedures were analyzed together with DSC results and TEM micrographs. Solution heat treatment (SHT) temperature was found to affect the obtained yield strengths after AA considerably and higher SHT temperatures lead to higher yield strength for same artificial aging condition. It was also shown that yield strength values obtained after 480 min—180 °C artificial aging can be surpassed in shorter times at higher artificial aging temperatures. Aging times as short as 60 min may be employed using temperatures above 200 °C to obtain higher strength than 480 min—180 °C aging. Linear relationships between Vickers hardness and mechanical strengths were suggested for the complete data of the study. Negative effects of over-aging on ductility were presented and β ′′ precipitates which are responsible for hardening during aging were presented using TEM micrographs. Additionally, high cycle fatigue tests were conducted for AA procedures 480 min—180 °C and 240 min—200 °C and similar fatigue strengths were reported." @default.
- W4323647977 created "2023-03-10" @default.
- W4323647977 creator A5020237294 @default.
- W4323647977 creator A5038485115 @default.
- W4323647977 date "2023-01-01" @default.
- W4323647977 modified "2023-09-30" @default.
- W4323647977 title "Dependency of mechanical properties on artificial aging conditions for EN AW 6082 aluminum alloy" @default.
- W4323647977 cites W1194211417 @default.
- W4323647977 cites W1968641316 @default.
- W4323647977 cites W2000214820 @default.
- W4323647977 cites W2000516144 @default.
- W4323647977 cites W2020379122 @default.
- W4323647977 cites W2023271910 @default.
- W4323647977 cites W2037202771 @default.
- W4323647977 cites W2037647696 @default.
- W4323647977 cites W2040344855 @default.
- W4323647977 cites W2055955414 @default.
- W4323647977 cites W2058251987 @default.
- W4323647977 cites W2068217237 @default.
- W4323647977 cites W2072170373 @default.
- W4323647977 cites W2079988792 @default.
- W4323647977 cites W2088293111 @default.
- W4323647977 cites W2089061663 @default.
- W4323647977 cites W2102056179 @default.
- W4323647977 cites W2111006567 @default.
- W4323647977 cites W2159742573 @default.
- W4323647977 cites W2322653247 @default.
- W4323647977 cites W2512197523 @default.
- W4323647977 cites W2884536063 @default.
- W4323647977 doi "https://doi.org/10.1051/metal/2023017" @default.
- W4323647977 hasPublicationYear "2023" @default.
- W4323647977 type Work @default.
- W4323647977 citedByCount "0" @default.
- W4323647977 crossrefType "journal-article" @default.
- W4323647977 hasAuthorship W4323647977A5020237294 @default.
- W4323647977 hasAuthorship W4323647977A5038485115 @default.
- W4323647977 hasConcept C112950240 @default.
- W4323647977 hasConcept C134121241 @default.
- W4323647977 hasConcept C149912024 @default.
- W4323647977 hasConcept C154634170 @default.
- W4323647977 hasConcept C159985019 @default.
- W4323647977 hasConcept C191897082 @default.
- W4323647977 hasConcept C192562407 @default.
- W4323647977 hasConcept C2776512210 @default.
- W4323647977 hasConcept C2779227376 @default.
- W4323647977 hasConcept C2780026712 @default.
- W4323647977 hasConcept C44255700 @default.
- W4323647977 hasConcept C500499127 @default.
- W4323647977 hasConcept C54355233 @default.
- W4323647977 hasConcept C79127381 @default.
- W4323647977 hasConcept C86803240 @default.
- W4323647977 hasConceptScore W4323647977C112950240 @default.
- W4323647977 hasConceptScore W4323647977C134121241 @default.
- W4323647977 hasConceptScore W4323647977C149912024 @default.
- W4323647977 hasConceptScore W4323647977C154634170 @default.
- W4323647977 hasConceptScore W4323647977C159985019 @default.
- W4323647977 hasConceptScore W4323647977C191897082 @default.
- W4323647977 hasConceptScore W4323647977C192562407 @default.
- W4323647977 hasConceptScore W4323647977C2776512210 @default.
- W4323647977 hasConceptScore W4323647977C2779227376 @default.
- W4323647977 hasConceptScore W4323647977C2780026712 @default.
- W4323647977 hasConceptScore W4323647977C44255700 @default.
- W4323647977 hasConceptScore W4323647977C500499127 @default.
- W4323647977 hasConceptScore W4323647977C54355233 @default.
- W4323647977 hasConceptScore W4323647977C79127381 @default.
- W4323647977 hasConceptScore W4323647977C86803240 @default.
- W4323647977 hasIssue "2" @default.
- W4323647977 hasLocation W43236479771 @default.
- W4323647977 hasOpenAccess W4323647977 @default.
- W4323647977 hasPrimaryLocation W43236479771 @default.
- W4323647977 hasRelatedWork W1981588054 @default.
- W4323647977 hasRelatedWork W1982015266 @default.
- W4323647977 hasRelatedWork W1983932593 @default.
- W4323647977 hasRelatedWork W1987487801 @default.
- W4323647977 hasRelatedWork W2072649947 @default.
- W4323647977 hasRelatedWork W2805557562 @default.
- W4323647977 hasRelatedWork W4280625018 @default.
- W4323647977 hasRelatedWork W4282039964 @default.
- W4323647977 hasRelatedWork W4285097618 @default.
- W4323647977 hasRelatedWork W4306173847 @default.
- W4323647977 hasVolume "120" @default.
- W4323647977 isParatext "false" @default.
- W4323647977 isRetracted "false" @default.
- W4323647977 workType "article" @default.