- W4324332285 abstract "Delamination of veneering ceramic is one of the most common challenges relating to veneered zirconia restorations. Additive manufacturing (AM) is a fast-expanding technology that has gained widespread acceptance in dentistry and is increasingly being used to produce dental restorations. However, information about bonding of porcelain to AM zirconia is lacking.The purpose of this in vitro study was to investigate the shear bond strength (SBS) of porcelain to milled and additively manufactured zirconia, and the effect of surface treatment on bond strength.A Ø12×5-mm disk was designed virtually to fabricate all specimens, which were divided into 2 groups according to the manufacturing technique: additively manufactured or milled zirconia. The effect of airborne-particle abrasion and a zirconia liner before porcelain application was investigated in both groups. Veneering porcelain was fired into an alumina ring mold on the zirconia surface. SBS was measured by using a universal testing machine at a crosshead speed of 1 mm/min before and after aging (n=10). SBS data were analyzed with 3-way ANOVA (α=.05) RESULTS: A significant difference was found between milled and AM zirconia. The SBS of porcelain to milled zirconia was significantly higher (1.38 MPa) than to AM zirconia (0.68 MPa) (P<.001). The surface treatment of zirconia had no significant effect on porcelain SBS in either group (P=.254), whereas thermocycling significantly reduced the SBS of porcelain to zirconia in both milled and AM groups (P=.001).Porcelain bonding to milled zirconia was better than to AM zirconia. Pretreating the zirconia substrate before porcelain application did not improve the porcelain bond." @default.
- W4324332285 created "2023-03-16" @default.
- W4324332285 creator A5004752016 @default.
- W4324332285 creator A5017629041 @default.
- W4324332285 creator A5038300186 @default.
- W4324332285 creator A5049818420 @default.
- W4324332285 creator A5067016305 @default.
- W4324332285 creator A5088003943 @default.
- W4324332285 date "2023-03-01" @default.
- W4324332285 modified "2023-09-25" @default.
- W4324332285 title "Shear bond strength of porcelain to milled and stereolithography additively manufactured zirconia with and without surface treatment: An in vitro study" @default.
- W4324332285 cites W1543511139 @default.
- W4324332285 cites W1669438684 @default.
- W4324332285 cites W172778866 @default.
- W4324332285 cites W1965414927 @default.
- W4324332285 cites W1980752757 @default.
- W4324332285 cites W1989540378 @default.
- W4324332285 cites W1996656097 @default.
- W4324332285 cites W1999075271 @default.
- W4324332285 cites W2000651124 @default.
- W4324332285 cites W2028272252 @default.
- W4324332285 cites W2028418957 @default.
- W4324332285 cites W2032498850 @default.
- W4324332285 cites W2041150584 @default.
- W4324332285 cites W2060312936 @default.
- W4324332285 cites W2095909815 @default.
- W4324332285 cites W2111016317 @default.
- W4324332285 cites W2115131472 @default.
- W4324332285 cites W2128210354 @default.
- W4324332285 cites W2130230700 @default.
- W4324332285 cites W2145515057 @default.
- W4324332285 cites W2148590240 @default.
- W4324332285 cites W2170180763 @default.
- W4324332285 cites W2572344192 @default.
- W4324332285 cites W2586853297 @default.
- W4324332285 cites W2597065619 @default.
- W4324332285 cites W2604537564 @default.
- W4324332285 cites W2737701148 @default.
- W4324332285 cites W2748704323 @default.
- W4324332285 cites W2750873995 @default.
- W4324332285 cites W2752455108 @default.
- W4324332285 cites W2755616348 @default.
- W4324332285 cites W2766099330 @default.
- W4324332285 cites W2781732895 @default.
- W4324332285 cites W2789356420 @default.
- W4324332285 cites W2789487015 @default.
- W4324332285 cites W2808417238 @default.
- W4324332285 cites W2883951628 @default.
- W4324332285 cites W2924482863 @default.
- W4324332285 cites W2934039943 @default.
- W4324332285 cites W2969775831 @default.
- W4324332285 cites W2983037257 @default.
- W4324332285 cites W3002567001 @default.
- W4324332285 cites W3013850958 @default.
- W4324332285 cites W3020131965 @default.
- W4324332285 cites W3045210132 @default.
- W4324332285 cites W3087637670 @default.
- W4324332285 cites W3114983254 @default.
- W4324332285 cites W3133495616 @default.
- W4324332285 cites W3174916330 @default.
- W4324332285 cites W4220928639 @default.
- W4324332285 cites W4295549417 @default.
- W4324332285 doi "https://doi.org/10.1016/j.prosdent.2023.02.007" @default.
- W4324332285 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/36932021" @default.
- W4324332285 hasPublicationYear "2023" @default.
- W4324332285 type Work @default.
- W4324332285 citedByCount "0" @default.
- W4324332285 crossrefType "journal-article" @default.
- W4324332285 hasAuthorship W4324332285A5004752016 @default.
- W4324332285 hasAuthorship W4324332285A5017629041 @default.
- W4324332285 hasAuthorship W4324332285A5038300186 @default.
- W4324332285 hasAuthorship W4324332285A5049818420 @default.
- W4324332285 hasAuthorship W4324332285A5067016305 @default.
- W4324332285 hasAuthorship W4324332285A5088003943 @default.
- W4324332285 hasConcept C112950240 @default.
- W4324332285 hasConcept C118231568 @default.
- W4324332285 hasConcept C123609680 @default.
- W4324332285 hasConcept C134132462 @default.
- W4324332285 hasConcept C159096172 @default.
- W4324332285 hasConcept C159985019 @default.
- W4324332285 hasConcept C180478085 @default.
- W4324332285 hasConcept C192562407 @default.
- W4324332285 hasConcept C2779227376 @default.
- W4324332285 hasConcept C2779989610 @default.
- W4324332285 hasConcept C68928338 @default.
- W4324332285 hasConceptScore W4324332285C112950240 @default.
- W4324332285 hasConceptScore W4324332285C118231568 @default.
- W4324332285 hasConceptScore W4324332285C123609680 @default.
- W4324332285 hasConceptScore W4324332285C134132462 @default.
- W4324332285 hasConceptScore W4324332285C159096172 @default.
- W4324332285 hasConceptScore W4324332285C159985019 @default.
- W4324332285 hasConceptScore W4324332285C180478085 @default.
- W4324332285 hasConceptScore W4324332285C192562407 @default.
- W4324332285 hasConceptScore W4324332285C2779227376 @default.
- W4324332285 hasConceptScore W4324332285C2779989610 @default.
- W4324332285 hasConceptScore W4324332285C68928338 @default.
- W4324332285 hasLocation W43243322851 @default.
- W4324332285 hasLocation W43243322852 @default.
- W4324332285 hasOpenAccess W4324332285 @default.
- W4324332285 hasPrimaryLocation W43243322851 @default.