- W4353079156 abstract "The possibility of effective solidification of spent sorbents containing radioactive cesium by spark plasma sintering (SPS) technology for their safe and long-term disposal was studied. The kinetics of consolidation spent sorbent based on magnetic zeolite after adsorption saturation with cesium (∼23 wt %) under SPS conditions in the range of 700–950 °C was carried out. The structural, elemental and phase composition changes during high-rate (minutes) heating of zeolite powder saturated with Cs+ ions was studied by SEM, EDX and XRD methods. As a result, ceramic samples with mineral-like structure of Fe-substituted pollucite CsFeSi2O6 were successfully obtained. It was determined that the optimal temperature of SPS consolidation was 900 °C, at which the formation of CsFeSi2O6 ceramics with a relative density of 91.2%, compressive strength of 497.6 MPa, Vickers microhardness of 1019 HV, rate of cesium leaching of 2.33 × 10−8 g/cm2 × day was reached. It was found that the mechanism of cesium diffusion from the volume of ceramics corresponded to flushing from the available surface of the sample, the lowest diffusion coefficient was 2.71 × 10−16 cm2/s, as well as the lowest penetration depth of the solution into the volume of ceramics was 1.04 × 10−5 cm. The adsorbents prepared by SPS up to 900 °C retained the magnetization, and at higher temperature the magnetization decreased, which was caused by phase and structural changes of ceramics. The characteristics of ceramic obtained from spent adsorbent complied with the requirements of GOST R 50926–96 and ISO 6961:1982 for solidified Cs-containing radioactive waste." @default.
- W4353079156 created "2023-03-23" @default.
- W4353079156 creator A5004866049 @default.
- W4353079156 creator A5008254814 @default.
- W4353079156 creator A5014572533 @default.
- W4353079156 creator A5017205756 @default.
- W4353079156 creator A5020152160 @default.
- W4353079156 creator A5027438393 @default.
- W4353079156 creator A5031046680 @default.
- W4353079156 creator A5032185491 @default.
- W4353079156 creator A5032464259 @default.
- W4353079156 creator A5038863090 @default.
- W4353079156 creator A5040459502 @default.
- W4353079156 creator A5064588828 @default.
- W4353079156 creator A5065942633 @default.
- W4353079156 creator A5066251781 @default.
- W4353079156 creator A5069506489 @default.
- W4353079156 creator A5072939652 @default.
- W4353079156 creator A5074439240 @default.
- W4353079156 creator A5078205872 @default.
- W4353079156 creator A5080602068 @default.
- W4353079156 creator A5083573697 @default.
- W4353079156 date "2023-07-01" @default.
- W4353079156 modified "2023-10-17" @default.
- W4353079156 title "Solidification of cesium containing magnetic zeolite sorbent by spark plasma sintering" @default.
- W4353079156 cites W1566227934 @default.
- W4353079156 cites W1967660997 @default.
- W4353079156 cites W1985319014 @default.
- W4353079156 cites W2000955104 @default.
- W4353079156 cites W2007749905 @default.
- W4353079156 cites W2011995074 @default.
- W4353079156 cites W2013854565 @default.
- W4353079156 cites W2016069589 @default.
- W4353079156 cites W2032469202 @default.
- W4353079156 cites W2034338250 @default.
- W4353079156 cites W2057910524 @default.
- W4353079156 cites W2080552766 @default.
- W4353079156 cites W2083765412 @default.
- W4353079156 cites W2102408407 @default.
- W4353079156 cites W2115130426 @default.
- W4353079156 cites W2201715015 @default.
- W4353079156 cites W2306180089 @default.
- W4353079156 cites W2736205261 @default.
- W4353079156 cites W2762547033 @default.
- W4353079156 cites W2767092611 @default.
- W4353079156 cites W2769866564 @default.
- W4353079156 cites W2906569030 @default.
- W4353079156 cites W2911636757 @default.
- W4353079156 cites W2940516214 @default.
- W4353079156 cites W2970817932 @default.
- W4353079156 cites W3005495058 @default.
- W4353079156 cites W3012560938 @default.
- W4353079156 cites W3013714460 @default.
- W4353079156 cites W3024689966 @default.
- W4353079156 cites W3045324174 @default.
- W4353079156 cites W3092224185 @default.
- W4353079156 cites W3094137450 @default.
- W4353079156 cites W3097853285 @default.
- W4353079156 cites W3106736439 @default.
- W4353079156 cites W3163500786 @default.
- W4353079156 cites W3165825286 @default.
- W4353079156 cites W3181616111 @default.
- W4353079156 cites W3199509027 @default.
- W4353079156 cites W3211479012 @default.
- W4353079156 cites W3213528907 @default.
- W4353079156 cites W4200601757 @default.
- W4353079156 cites W4210303428 @default.
- W4353079156 cites W4211094103 @default.
- W4353079156 cites W4220920311 @default.
- W4353079156 cites W4224903229 @default.
- W4353079156 cites W4292323213 @default.
- W4353079156 cites W4293659991 @default.
- W4353079156 cites W4303859384 @default.
- W4353079156 cites W4305056990 @default.
- W4353079156 cites W4306840209 @default.
- W4353079156 cites W629162897 @default.
- W4353079156 doi "https://doi.org/10.1016/j.matchemphys.2023.127648" @default.
- W4353079156 hasPublicationYear "2023" @default.
- W4353079156 type Work @default.
- W4353079156 citedByCount "1" @default.
- W4353079156 countsByYear W43530791562023 @default.
- W4353079156 crossrefType "journal-article" @default.
- W4353079156 hasAuthorship W4353079156A5004866049 @default.
- W4353079156 hasAuthorship W4353079156A5008254814 @default.
- W4353079156 hasAuthorship W4353079156A5014572533 @default.
- W4353079156 hasAuthorship W4353079156A5017205756 @default.
- W4353079156 hasAuthorship W4353079156A5020152160 @default.
- W4353079156 hasAuthorship W4353079156A5027438393 @default.
- W4353079156 hasAuthorship W4353079156A5031046680 @default.
- W4353079156 hasAuthorship W4353079156A5032185491 @default.
- W4353079156 hasAuthorship W4353079156A5032464259 @default.
- W4353079156 hasAuthorship W4353079156A5038863090 @default.
- W4353079156 hasAuthorship W4353079156A5040459502 @default.
- W4353079156 hasAuthorship W4353079156A5064588828 @default.
- W4353079156 hasAuthorship W4353079156A5065942633 @default.
- W4353079156 hasAuthorship W4353079156A5066251781 @default.
- W4353079156 hasAuthorship W4353079156A5069506489 @default.
- W4353079156 hasAuthorship W4353079156A5072939652 @default.