- W4362511306 abstract "This study aims to develop a manufacturing route for a low-cost dense magnetocaloric Ni-Mn-Sn Heusler alloy (HA) using laser powder bed fusion (LPBF) additive manufacturing technique by in-situ alloying from its elemental constituents. LPBF enables the production of high surface-area-to-volume 3D-printed components to increase heat transfer efficiency in magnetic refrigerators. A laser parametric study was performed on blocks, lattices and microchanneled cylinders for maximum densification, the highest density was observed at the samples with laser energy density (EV) of 18.52 J/mm3, 53.33 J/mm3 and 89.89 J/mm3, where they achieved a density of 6.8 g/cm3, 8.2 g/cm3 and 8.3 g/cm3, respectively. After heat treatment, the three samples show the L21 phase with a minor 4 O orthorhombic phase and double magnetic transitions, martensitie-austenite transition (TM) and curie temperature (TCA). The maximum magnetic entropy change (ΔSmax) values of the three samples around TM are 0.53 Jkg-1 K-1 at 160 K, 0.5 Jkg-1 K-1 at 130 K, and 0.3 Jkg-1 K-1 at 170 K, respectively. And ΔSmax of almost 1.0 Jkg-1 K-1 at TCA (∼320 K) for these samples with a field change of 1 T." @default.
- W4362511306 created "2023-04-06" @default.
- W4362511306 creator A5029482890 @default.
- W4362511306 creator A5038521703 @default.
- W4362511306 creator A5062639631 @default.
- W4362511306 creator A5069184870 @default.
- W4362511306 creator A5080106254 @default.
- W4362511306 creator A5084603626 @default.
- W4362511306 date "2023-05-01" @default.
- W4362511306 modified "2023-09-25" @default.
- W4362511306 title "Laser powder bed fusion of the Ni-Mn-Sn Heusler alloy for magnetic refrigeration applications" @default.
- W4362511306 cites W1544262616 @default.
- W4362511306 cites W1964914129 @default.
- W4362511306 cites W1972988106 @default.
- W4362511306 cites W1976211035 @default.
- W4362511306 cites W1980624489 @default.
- W4362511306 cites W1994595537 @default.
- W4362511306 cites W1997073843 @default.
- W4362511306 cites W2001965131 @default.
- W4362511306 cites W2009074044 @default.
- W4362511306 cites W2014701806 @default.
- W4362511306 cites W2028528116 @default.
- W4362511306 cites W2044722549 @default.
- W4362511306 cites W2056992292 @default.
- W4362511306 cites W2058268842 @default.
- W4362511306 cites W2064438715 @default.
- W4362511306 cites W2069315691 @default.
- W4362511306 cites W2073461614 @default.
- W4362511306 cites W2078799048 @default.
- W4362511306 cites W2081382550 @default.
- W4362511306 cites W2088290941 @default.
- W4362511306 cites W2099540110 @default.
- W4362511306 cites W2105971191 @default.
- W4362511306 cites W2213843778 @default.
- W4362511306 cites W2275557589 @default.
- W4362511306 cites W2292808995 @default.
- W4362511306 cites W2411633023 @default.
- W4362511306 cites W2473544504 @default.
- W4362511306 cites W2560482577 @default.
- W4362511306 cites W2593239660 @default.
- W4362511306 cites W2593978915 @default.
- W4362511306 cites W2762367303 @default.
- W4362511306 cites W2767998993 @default.
- W4362511306 cites W2769768452 @default.
- W4362511306 cites W2807597524 @default.
- W4362511306 cites W2809085022 @default.
- W4362511306 cites W2846406822 @default.
- W4362511306 cites W2892065905 @default.
- W4362511306 cites W2892634276 @default.
- W4362511306 cites W2933807090 @default.
- W4362511306 cites W2979516976 @default.
- W4362511306 cites W3004167988 @default.
- W4362511306 cites W3004534251 @default.
- W4362511306 cites W3008582428 @default.
- W4362511306 cites W3015787210 @default.
- W4362511306 cites W3031840420 @default.
- W4362511306 cites W3034685208 @default.
- W4362511306 cites W3045687444 @default.
- W4362511306 cites W3096502201 @default.
- W4362511306 cites W3137177204 @default.
- W4362511306 cites W3138174894 @default.
- W4362511306 cites W37403586 @default.
- W4362511306 cites W4308343608 @default.
- W4362511306 cites W3025941577 @default.
- W4362511306 doi "https://doi.org/10.1016/j.addma.2023.103536" @default.
- W4362511306 hasPublicationYear "2023" @default.
- W4362511306 type Work @default.
- W4362511306 citedByCount "0" @default.
- W4362511306 crossrefType "journal-article" @default.
- W4362511306 hasAuthorship W4362511306A5029482890 @default.
- W4362511306 hasAuthorship W4362511306A5038521703 @default.
- W4362511306 hasAuthorship W4362511306A5062639631 @default.
- W4362511306 hasAuthorship W4362511306A5069184870 @default.
- W4362511306 hasAuthorship W4362511306A5080106254 @default.
- W4362511306 hasAuthorship W4362511306A5084603626 @default.
- W4362511306 hasBestOaLocation W43625113061 @default.
- W4362511306 hasConcept C113196181 @default.
- W4362511306 hasConcept C115260700 @default.
- W4362511306 hasConcept C115624301 @default.
- W4362511306 hasConcept C120665830 @default.
- W4362511306 hasConcept C121332964 @default.
- W4362511306 hasConcept C185592680 @default.
- W4362511306 hasConcept C186116631 @default.
- W4362511306 hasConcept C191897082 @default.
- W4362511306 hasConcept C192562407 @default.
- W4362511306 hasConcept C26873012 @default.
- W4362511306 hasConcept C2780026712 @default.
- W4362511306 hasConcept C32546565 @default.
- W4362511306 hasConcept C37243968 @default.
- W4362511306 hasConcept C43617362 @default.
- W4362511306 hasConcept C520434653 @default.
- W4362511306 hasConcept C62520636 @default.
- W4362511306 hasConcept C63648874 @default.
- W4362511306 hasConcept C8010536 @default.
- W4362511306 hasConcept C82217956 @default.
- W4362511306 hasConcept C87976508 @default.
- W4362511306 hasConcept C96288455 @default.
- W4362511306 hasConceptScore W4362511306C113196181 @default.