- W4367183487 abstract "The recrystallization, texture, and mechanical properties of hot-rolled and hot-rolled + annealed Mg-10Ho (wt %) are investigated. Mg-10Ho binary alloy is first solution treated followed by multipass rolling at 420 °C for up to 50 % reduction and subsequently annealed at 400 °C for different times for up to 60 min. The microstructure of deformed and annealed samples was characterized using a field-emission secondary electron microscope (FESEM) and electron back-scattered diffraction (EBSD) and the mechanical properties were examined using hardness and tensile tests. The as-rolled microstructure contains fine dynamic recrystallized grains and different types of deformation twins. With increasing annealing time, a decrease in the hardness was observed, suggesting initiation of recovery and static recrystallization. After 10 min of annealing, an equiaxed, nearly fully recrystallized microstructure with a grain size of 14 µm and weaker basal texture was obtained. This annealed sample exhibits an ultimate tensile strength of 213 MPa, yield strength of 145 MPa, and ductility of ∼7 %. Such an optimum combination of strength and ductility is attributed to the combined effect of solid solution strengthening, grain refinement, and texture weakening. Additionally, the Johnson-Mehl-Avrami-Kolmogorov (JMAK) model was used to understand the recrystallization kinetics of Mg-10Ho and compared it with that of Mg-10Y. Results indicate that the solute drag effect plays a dominant role in the faster recrystallization kinetics of Mg-10Ho alloy. Finally, the texture variation in Mg-10Ho and Mg-10Y is also explained based on the solute drag effect." @default.
- W4367183487 created "2023-04-28" @default.
- W4367183487 creator A5002234479 @default.
- W4367183487 creator A5008707565 @default.
- W4367183487 creator A5031027555 @default.
- W4367183487 creator A5068614047 @default.
- W4367183487 date "2023-09-01" @default.
- W4367183487 modified "2023-10-14" @default.
- W4367183487 title "The recrystallization, texture and mechanical behavior of hot rolled and annealed Mg-10Ho binary alloy" @default.
- W4367183487 cites W1236690264 @default.
- W4367183487 cites W1724375762 @default.
- W4367183487 cites W1964746686 @default.
- W4367183487 cites W1972095222 @default.
- W4367183487 cites W1976446845 @default.
- W4367183487 cites W2003587592 @default.
- W4367183487 cites W2009098341 @default.
- W4367183487 cites W2009736701 @default.
- W4367183487 cites W2013428459 @default.
- W4367183487 cites W2014690755 @default.
- W4367183487 cites W2017844793 @default.
- W4367183487 cites W2027984778 @default.
- W4367183487 cites W2030216547 @default.
- W4367183487 cites W2034073956 @default.
- W4367183487 cites W2042225286 @default.
- W4367183487 cites W2045738969 @default.
- W4367183487 cites W2047003555 @default.
- W4367183487 cites W2064593063 @default.
- W4367183487 cites W2071485055 @default.
- W4367183487 cites W2076016788 @default.
- W4367183487 cites W2081344683 @default.
- W4367183487 cites W2083625555 @default.
- W4367183487 cites W2086115893 @default.
- W4367183487 cites W2089090893 @default.
- W4367183487 cites W2090732497 @default.
- W4367183487 cites W2110733247 @default.
- W4367183487 cites W2147014468 @default.
- W4367183487 cites W2238395753 @default.
- W4367183487 cites W2519585498 @default.
- W4367183487 cites W2562369915 @default.
- W4367183487 cites W2584361667 @default.
- W4367183487 cites W2617202128 @default.
- W4367183487 cites W2737630260 @default.
- W4367183487 cites W2759027428 @default.
- W4367183487 cites W2791601348 @default.
- W4367183487 cites W2806075725 @default.
- W4367183487 cites W2808101433 @default.
- W4367183487 cites W2895191087 @default.
- W4367183487 cites W2977991244 @default.
- W4367183487 cites W2996692208 @default.
- W4367183487 cites W3000443620 @default.
- W4367183487 cites W3040837509 @default.
- W4367183487 cites W3185027901 @default.
- W4367183487 cites W4200409201 @default.
- W4367183487 cites W658838585 @default.
- W4367183487 doi "https://doi.org/10.1016/j.jallcom.2023.170329" @default.
- W4367183487 hasPublicationYear "2023" @default.
- W4367183487 type Work @default.
- W4367183487 citedByCount "3" @default.
- W4367183487 countsByYear W43671834872023 @default.
- W4367183487 crossrefType "journal-article" @default.
- W4367183487 hasAuthorship W4367183487A5002234479 @default.
- W4367183487 hasAuthorship W4367183487A5008707565 @default.
- W4367183487 hasAuthorship W4367183487A5031027555 @default.
- W4367183487 hasAuthorship W4367183487A5068614047 @default.
- W4367183487 hasConcept C112950240 @default.
- W4367183487 hasConcept C12487841 @default.
- W4367183487 hasConcept C151730666 @default.
- W4367183487 hasConcept C169010117 @default.
- W4367183487 hasConcept C172658604 @default.
- W4367183487 hasConcept C191897082 @default.
- W4367183487 hasConcept C192191005 @default.
- W4367183487 hasConcept C192562407 @default.
- W4367183487 hasConcept C195702682 @default.
- W4367183487 hasConcept C2777855556 @default.
- W4367183487 hasConcept C2780026712 @default.
- W4367183487 hasConcept C27805521 @default.
- W4367183487 hasConcept C47908070 @default.
- W4367183487 hasConcept C86803240 @default.
- W4367183487 hasConcept C87976508 @default.
- W4367183487 hasConceptScore W4367183487C112950240 @default.
- W4367183487 hasConceptScore W4367183487C12487841 @default.
- W4367183487 hasConceptScore W4367183487C151730666 @default.
- W4367183487 hasConceptScore W4367183487C169010117 @default.
- W4367183487 hasConceptScore W4367183487C172658604 @default.
- W4367183487 hasConceptScore W4367183487C191897082 @default.
- W4367183487 hasConceptScore W4367183487C192191005 @default.
- W4367183487 hasConceptScore W4367183487C192562407 @default.
- W4367183487 hasConceptScore W4367183487C195702682 @default.
- W4367183487 hasConceptScore W4367183487C2777855556 @default.
- W4367183487 hasConceptScore W4367183487C2780026712 @default.
- W4367183487 hasConceptScore W4367183487C27805521 @default.
- W4367183487 hasConceptScore W4367183487C47908070 @default.
- W4367183487 hasConceptScore W4367183487C86803240 @default.
- W4367183487 hasConceptScore W4367183487C87976508 @default.
- W4367183487 hasLocation W43671834871 @default.
- W4367183487 hasOpenAccess W4367183487 @default.
- W4367183487 hasPrimaryLocation W43671834871 @default.
- W4367183487 hasRelatedWork W2033045588 @default.