• W4367693325 abstract "The φ16 mm single crystal copper rod was prepared by heated-mold horizontal continuous casting, and the φ16 mm polycrystalline copper rod was prepared by up-casting technology. Both of them were drawn to φ0.2 mm, the conductivity, strength, elongation, and microstructure evolution of single-crystal copper wire and polycrystal copper wire were compared and analyzed. The results show that the plasticity of as-cast single-crystal copper rod is 13.94% higher than that of as-cast polycrystalline copper rod. When drawing to φ0.2 mm, a single crystal copper wire with high strength (506 MPa) and high conductivity (98.01% IACS). At the same deformation amount, the single crystal copper wire obviously deforms more slowly and has a higher plastic deformation capacity; the texture transformation of single crystal copper wire is from soft → hard orientation, selective orientation to discrete distribution, while the weave transformation of polycrystalline copper wire is from soft → hard orientation, then from hard → soft orientation, and finally stabilizes to selective orientation. The microstructural evolution of single-crystal copper wire and polycrystalline copper wire during continuous deformation was observed: dislocation entanglement into dislocation cells by slip → microstrip structure → lamellar organization → twinning organization, single-crystal copper wire appears twinning later, single-crystal copper deformation coordination ability is better than polycrystalline copper. It is found that the increase of dislocation density, the decrease of grain width and the increase of <111> texture are the main factors for the strength improvement of micro-nano pure copper wires." @default.
• W4367693325 created "2023-05-03" @default.
• W4367693325 creator A5001822572 @default.
• W4367693325 creator A5004934439 @default.
• W4367693325 creator A5005365468 @default.
• W4367693325 creator A5021214519 @default.
• W4367693325 creator A5022526821 @default.
• W4367693325 creator A5033561899 @default.
• W4367693325 creator A5035441361 @default.
• W4367693325 creator A5036825750 @default.
• W4367693325 creator A5065346031 @default.
• W4367693325 creator A5066863522 @default.
• W4367693325 creator A5078496288 @default.
• W4367693325 creator A5087235657 @default.
• W4367693325 date "2023-05-01" @default.
• W4367693325 modified "2023-10-18" @default.
• W4367693325 title "Texture evolution and its influence mechanism on properties of single crystal copper and polycrystalline copper during cumulative deformation" @default.
• W4367693325 cites W1750454366 @default.
• W4367693325 cites W1790858381 @default.
• W4367693325 cites W1978064892 @default.
• W4367693325 cites W1988917606 @default.
• W4367693325 cites W1991992843 @default.
• W4367693325 cites W2068248530 @default.
• W4367693325 cites W2085148203 @default.
• W4367693325 cites W2086049774 @default.
• W4367693325 cites W2089975307 @default.
• W4367693325 cites W2094951031 @default.
• W4367693325 cites W2115726702 @default.
• W4367693325 cites W2171792732 @default.
• W4367693325 cites W2295723937 @default.
• W4367693325 cites W2469890223 @default.
• W4367693325 cites W2565921259 @default.
• W4367693325 cites W2735848778 @default.
• W4367693325 cites W2769115123 @default.
• W4367693325 cites W2901430462 @default.
• W4367693325 cites W2944233160 @default.
• W4367693325 cites W3042563126 @default.
• W4367693325 cites W3081560125 @default.
• W4367693325 cites W3117593459 @default.
• W4367693325 cites W3143537928 @default.
• W4367693325 cites W3158326852 @default.
• W4367693325 cites W3163908288 @default.
• W4367693325 cites W4294958192 @default.
• W4367693325 cites W4309342212 @default.
• W4367693325 cites W595138293 @default.
• W4367693325 doi "https://doi.org/10.1016/j.jmrt.2023.04.264" @default.
• W4367693325 hasPublicationYear "2023" @default.
• W4367693325 type Work @default.
• W4367693325 citedByCount "0" @default.
• W4367693325 crossrefType "journal-article" @default.
• W4367693325 hasAuthorship W4367693325A5001822572 @default.
• W4367693325 hasAuthorship W4367693325A5004934439 @default.
• W4367693325 hasAuthorship W4367693325A5005365468 @default.
• W4367693325 hasAuthorship W4367693325A5021214519 @default.
• W4367693325 hasAuthorship W4367693325A5022526821 @default.
• W4367693325 hasAuthorship W4367693325A5033561899 @default.
• W4367693325 hasAuthorship W4367693325A5035441361 @default.
• W4367693325 hasAuthorship W4367693325A5036825750 @default.
• W4367693325 hasAuthorship W4367693325A5065346031 @default.
• W4367693325 hasAuthorship W4367693325A5066863522 @default.
• W4367693325 hasAuthorship W4367693325A5078496288 @default.
• W4367693325 hasAuthorship W4367693325A5087235657 @default.
• W4367693325 hasBestOaLocation W43676933251 @default.
• W4367693325 hasConcept C115961682 @default.
• W4367693325 hasConcept C137637335 @default.
• W4367693325 hasConcept C154945302 @default.
• W4367693325 hasConcept C159122135 @default.
• W4367693325 hasConcept C159985019 @default.
• W4367693325 hasConcept C185592680 @default.
• W4367693325 hasConcept C191897082 @default.
• W4367693325 hasConcept C192562407 @default.
• W4367693325 hasConcept C204366326 @default.
• W4367693325 hasConcept C2781195486 @default.
• W4367693325 hasConcept C41008148 @default.
• W4367693325 hasConcept C544778455 @default.
• W4367693325 hasConcept C6840138 @default.
• W4367693325 hasConcept C73922627 @default.
• W4367693325 hasConcept C8010536 @default.
• W4367693325 hasConcept C87976508 @default.
• W4367693325 hasConceptScore W4367693325C115961682 @default.
• W4367693325 hasConceptScore W4367693325C137637335 @default.
• W4367693325 hasConceptScore W4367693325C154945302 @default.
• W4367693325 hasConceptScore W4367693325C159122135 @default.
• W4367693325 hasConceptScore W4367693325C159985019 @default.
• W4367693325 hasConceptScore W4367693325C185592680 @default.
• W4367693325 hasConceptScore W4367693325C191897082 @default.
• W4367693325 hasConceptScore W4367693325C192562407 @default.
• W4367693325 hasConceptScore W4367693325C204366326 @default.
• W4367693325 hasConceptScore W4367693325C2781195486 @default.
• W4367693325 hasConceptScore W4367693325C41008148 @default.
• W4367693325 hasConceptScore W4367693325C544778455 @default.
• W4367693325 hasConceptScore W4367693325C6840138 @default.
• W4367693325 hasConceptScore W4367693325C73922627 @default.
• W4367693325 hasConceptScore W4367693325C8010536 @default.
• W4367693325 hasConceptScore W4367693325C87976508 @default.
• W4367693325 hasLocation W43676933251 @default.
• W4367693325 hasOpenAccess W4367693325 @default.
• W4367693325 hasPrimaryLocation W43676933251 @default.

• next