• W4376602022 abstract "One of the objectives for the development of high-strength dual-phase (DP) steel is improving the stretch-flangeability. Large-strained sheared edges are deformed and frequently cracked during stretch-flange formation. Considering shearing as the first deformation, the stretch-flange deformation may be regarded as a secondary deformation. To improve the stretch-flangeability of the DP steels, many researchers have analyzed the microvoid formation. However, in these analyses, the shearing process was not considered. With this background, ex-situ mini-bending tests combined with scanning electron microscopy (SEM) monitoring of microvoid formation were conducted during the secondary deformation. Prior to the secondary deformation, several microvoids were observed on the sheared surface and fine subgrains formed in the ferrite. During secondary deformation, the preliminary microvoids present at the ferrite-martensite interface propagated into the ferrite phase. In contrast, this behavior was not observed for the reamed surface deformation, which was formed without preliminary deformation. Furthermore, microvoids were initiated on ferrite grains that were not present at the ferrite-martensite interface, and martensite islands were not cracked during secondary deformation. This result is noteworthy because martensite cracking was the main factor involved in microvoid initiation, in the absence of shearing. Electron backscattering diffraction analysis revealed that the work hardening of ferrite, prior to the secondary deformation, caused a deviation in the strain concentration sites from those found in the reamed surface deformation. Therefore, this study elucidated microvoid formation on preliminary deformed surfaces via shearing and provided insights for material development considering deformations on the sheared surfaces of materials." @default.
• W4376602022 created "2023-05-17" @default.
• W4376602022 creator A5001486781 @default.
• W4376602022 creator A5004087361 @default.
• W4376602022 creator A5043188680 @default.
• W4376602022 creator A5065731416 @default.
• W4376602022 creator A5082308726 @default.
• W4376602022 date "2023-05-15" @default.
• W4376602022 modified "2023-10-16" @default.
• W4376602022 title "Microvoid Formation of Ferrite-martensite Dual-phase Steel via Tensile Deformation after Severe Plastic Shear-deformation" @default.
• W4376602022 cites W1583576192 @default.
• W4376602022 cites W1971476145 @default.
• W4376602022 cites W1986205235 @default.
• W4376602022 cites W1986835940 @default.
• W4376602022 cites W1987877134 @default.
• W4376602022 cites W2022130505 @default.
• W4376602022 cites W2052737295 @default.
• W4376602022 cites W2065076763 @default.
• W4376602022 cites W2084665837 @default.
• W4376602022 cites W217526684 @default.
• W4376602022 cites W2178104010 @default.
• W4376602022 cites W2211858207 @default.
• W4376602022 cites W2328239959 @default.
• W4376602022 cites W2464148939 @default.
• W4376602022 cites W2737111412 @default.
• W4376602022 cites W2913046707 @default.
• W4376602022 cites W2924009470 @default.
• W4376602022 cites W2971866289 @default.
• W4376602022 cites W3022693958 @default.
• W4376602022 cites W3118321107 @default.
• W4376602022 cites W3136591907 @default.
• W4376602022 cites W3171574631 @default.
• W4376602022 cites W3181120807 @default.
• W4376602022 cites W3209059023 @default.
• W4376602022 cites W4225113842 @default.
• W4376602022 cites W4225257330 @default.
• W4376602022 doi "https://doi.org/10.2355/isijinternational.isijint-2023-012" @default.
• W4376602022 hasPublicationYear "2023" @default.
• W4376602022 type Work @default.
• W4376602022 citedByCount "1" @default.
• W4376602022 crossrefType "journal-article" @default.
• W4376602022 hasAuthorship W4376602022A5001486781 @default.
• W4376602022 hasAuthorship W4376602022A5004087361 @default.
• W4376602022 hasAuthorship W4376602022A5043188680 @default.
• W4376602022 hasAuthorship W4376602022A5065731416 @default.
• W4376602022 hasAuthorship W4376602022A5082308726 @default.
• W4376602022 hasBestOaLocation W43766020221 @default.
• W4376602022 hasConcept C112950240 @default.
• W4376602022 hasConcept C152279782 @default.
• W4376602022 hasConcept C159985019 @default.
• W4376602022 hasConcept C18747287 @default.
• W4376602022 hasConcept C191897082 @default.
• W4376602022 hasConcept C192562407 @default.
• W4376602022 hasConcept C204366326 @default.
• W4376602022 hasConcept C2779344738 @default.
• W4376602022 hasConcept C27805521 @default.
• W4376602022 hasConcept C37210646 @default.
• W4376602022 hasConcept C87976508 @default.
• W4376602022 hasConceptScore W4376602022C112950240 @default.
• W4376602022 hasConceptScore W4376602022C152279782 @default.
• W4376602022 hasConceptScore W4376602022C159985019 @default.
• W4376602022 hasConceptScore W4376602022C18747287 @default.
• W4376602022 hasConceptScore W4376602022C191897082 @default.
• W4376602022 hasConceptScore W4376602022C192562407 @default.
• W4376602022 hasConceptScore W4376602022C204366326 @default.
• W4376602022 hasConceptScore W4376602022C2779344738 @default.
• W4376602022 hasConceptScore W4376602022C27805521 @default.
• W4376602022 hasConceptScore W4376602022C37210646 @default.
• W4376602022 hasConceptScore W4376602022C87976508 @default.
• W4376602022 hasIssue "5" @default.
• W4376602022 hasLocation W43766020221 @default.
• W4376602022 hasOpenAccess W4376602022 @default.
• W4376602022 hasPrimaryLocation W43766020221 @default.
• W4376602022 hasRelatedWork W1967149195 @default.
• W4376602022 hasRelatedWork W1968928483 @default.
• W4376602022 hasRelatedWork W1969718662 @default.
• W4376602022 hasRelatedWork W2090870198 @default.
• W4376602022 hasRelatedWork W2321792740 @default.
• W4376602022 hasRelatedWork W2791714653 @default.
• W4376602022 hasRelatedWork W2841756278 @default.
• W4376602022 hasRelatedWork W2999739669 @default.
• W4376602022 hasRelatedWork W3134325640 @default.
• W4376602022 hasRelatedWork W2184123119 @default.
• W4376602022 hasVolume "63" @default.
• W4376602022 isParatext "false" @default.
• W4376602022 isRetracted "false" @default.
• W4376602022 workType "article" @default.