- W4376619254 abstract "A new process of “cold spraying interlayer + roll-bonding” (CSIR) was put forward for the preparation of Mg/Al clad plates. First, the micron Ni and Al powders (including some Zn particles) were cold sprayed to form an ultrathin coating on Al or Mg substrate slabs. Then roll-bonding was performed at 400 °C. The influence of cold sprayed coating on slab surfaces, interfacial microstructures, texture evolutions, mechanical properties and the related mechanism were systematically investigated. The results show that the average shear strength of the as-rolled Mg/Al clad plate assisted by cold spraying Al and Ni micron powders interlayer on the substrate slabs was nearly twice (35.58 MPa) than that of conventional rolling under the same conditions (single pass, reduction ratio was 35%). For as-rolled Mg/Al clad plates, almost no reaction diffusion layers are generated, and the mechanical interlocking between cold sprayed coatings and substrate slabs is the main mechanism for improving the shear strength. The interface between the Al coating and the Ni coating is weakest of the as-rolled Mg/Al clad plates. As the reduction rate increases from 27.5% to 47.5%, the function of the mechanical interlocking of cold sprayed coatings will first increase and then weaken. After annealing at 400 °C for 1 h, the interface between the Al coating and the Mg substrate slab will form thick mixed brittle intermetallic compounds, including Al3Mg2, Mg17Al12, MgZn2 and AlMg4Zn11, and cause local gaps, holes, and cracks around the Zn-rich Ni coating. The fracture path after annealing starts from the vicinity of the defective Ni particles, and eventually enlarges along the mixed intermetallic compounds layer between the Al coating and the Mg substrate slab. The research indicates that the CSIR process has great potential in cooperating the metallurgical bonding with the mechanical interlocking of clad plates." @default.
- W4376619254 created "2023-05-17" @default.
- W4376619254 creator A5000399610 @default.
- W4376619254 creator A5011417555 @default.
- W4376619254 creator A5043760395 @default.
- W4376619254 creator A5044488250 @default.
- W4376619254 creator A5048440534 @default.
- W4376619254 creator A5051532580 @default.
- W4376619254 creator A5053372664 @default.
- W4376619254 creator A5071458554 @default.
- W4376619254 creator A5090057180 @default.
- W4376619254 date "2023-06-01" @default.
- W4376619254 modified "2023-09-29" @default.
- W4376619254 title "Microstructural evolutions and mechanical characteristics of roll-bonding Mg/Al clad plate regulated by cold spraying micron particle interlayer" @default.
- W4376619254 cites W1965903222 @default.
- W4376619254 cites W1980865252 @default.
- W4376619254 cites W1997279922 @default.
- W4376619254 cites W2001051114 @default.
- W4376619254 cites W2004490202 @default.
- W4376619254 cites W2018224703 @default.
- W4376619254 cites W2024789382 @default.
- W4376619254 cites W2041148254 @default.
- W4376619254 cites W2044529625 @default.
- W4376619254 cites W2063952377 @default.
- W4376619254 cites W2068717209 @default.
- W4376619254 cites W2078800630 @default.
- W4376619254 cites W2086216058 @default.
- W4376619254 cites W2104024646 @default.
- W4376619254 cites W2184397554 @default.
- W4376619254 cites W2269483019 @default.
- W4376619254 cites W2745202594 @default.
- W4376619254 cites W2792374107 @default.
- W4376619254 cites W2794814081 @default.
- W4376619254 cites W2902478077 @default.
- W4376619254 cites W2919562555 @default.
- W4376619254 cites W2951194685 @default.
- W4376619254 cites W2969352827 @default.
- W4376619254 cites W3004282760 @default.
- W4376619254 cites W3005022217 @default.
- W4376619254 cites W3021031474 @default.
- W4376619254 cites W3036220264 @default.
- W4376619254 cites W3046773681 @default.
- W4376619254 cites W3092540985 @default.
- W4376619254 cites W3129457386 @default.
- W4376619254 cites W3135658063 @default.
- W4376619254 cites W3193180140 @default.
- W4376619254 cites W3199999397 @default.
- W4376619254 cites W3205236868 @default.
- W4376619254 cites W4283528503 @default.
- W4376619254 cites W4293569897 @default.
- W4376619254 doi "https://doi.org/10.1016/j.msea.2023.145153" @default.
- W4376619254 hasPublicationYear "2023" @default.
- W4376619254 type Work @default.
- W4376619254 citedByCount "1" @default.
- W4376619254 countsByYear W43766192542023 @default.
- W4376619254 crossrefType "journal-article" @default.
- W4376619254 hasAuthorship W4376619254A5000399610 @default.
- W4376619254 hasAuthorship W4376619254A5011417555 @default.
- W4376619254 hasAuthorship W4376619254A5043760395 @default.
- W4376619254 hasAuthorship W4376619254A5044488250 @default.
- W4376619254 hasAuthorship W4376619254A5048440534 @default.
- W4376619254 hasAuthorship W4376619254A5051532580 @default.
- W4376619254 hasAuthorship W4376619254A5053372664 @default.
- W4376619254 hasAuthorship W4376619254A5071458554 @default.
- W4376619254 hasAuthorship W4376619254A5090057180 @default.
- W4376619254 hasConcept C113740112 @default.
- W4376619254 hasConcept C127313418 @default.
- W4376619254 hasConcept C127413603 @default.
- W4376619254 hasConcept C136478896 @default.
- W4376619254 hasConcept C159985019 @default.
- W4376619254 hasConcept C191897082 @default.
- W4376619254 hasConcept C192562407 @default.
- W4376619254 hasConcept C202752663 @default.
- W4376619254 hasConcept C27501479 @default.
- W4376619254 hasConcept C2777855556 @default.
- W4376619254 hasConcept C2778844933 @default.
- W4376619254 hasConcept C2780026712 @default.
- W4376619254 hasConcept C2781448156 @default.
- W4376619254 hasConcept C78519656 @default.
- W4376619254 hasConcept C8058405 @default.
- W4376619254 hasConcept C87976508 @default.
- W4376619254 hasConceptScore W4376619254C113740112 @default.
- W4376619254 hasConceptScore W4376619254C127313418 @default.
- W4376619254 hasConceptScore W4376619254C127413603 @default.
- W4376619254 hasConceptScore W4376619254C136478896 @default.
- W4376619254 hasConceptScore W4376619254C159985019 @default.
- W4376619254 hasConceptScore W4376619254C191897082 @default.
- W4376619254 hasConceptScore W4376619254C192562407 @default.
- W4376619254 hasConceptScore W4376619254C202752663 @default.
- W4376619254 hasConceptScore W4376619254C27501479 @default.
- W4376619254 hasConceptScore W4376619254C2777855556 @default.
- W4376619254 hasConceptScore W4376619254C2778844933 @default.
- W4376619254 hasConceptScore W4376619254C2780026712 @default.
- W4376619254 hasConceptScore W4376619254C2781448156 @default.
- W4376619254 hasConceptScore W4376619254C78519656 @default.
- W4376619254 hasConceptScore W4376619254C8058405 @default.
- W4376619254 hasConceptScore W4376619254C87976508 @default.
- W4376619254 hasFunder F4320321001 @default.