- W4377092014 abstract "In this study, the fatigue performance of magnetic pulse welding (MPW) joints of AA5052 aluminum alloy and T300 carbon fiber reinforced polymer (CFRP) with sandwich structure was systematically investigated. Mechanical property tests and microscopic observations were used to evaluate joint performance and damage to the CFRP. The results showed that satisfactory tensile strength (up to 92.24% of the tensile strength of the base material) was obtained by optimization of discharge energy. However, the samples in the fatigue test exhibited more sensitive properties to the fatigue environment. The higher fatigue cycle life was demonstrated only when the stress amplitude Sa ≤ 20.41 MPa. The fatigue test data were analyzed by Weibull distribution to fit the S-N curves under different reliability levels, which can be used for reliability assessment and life prediction in practical applications. The CFRP surfaces in different states were studied by scanning electron microscope (SEM). It was found that MPW would not damage the surfaces, while delamination and cracking would gradually occur during the fatigue process." @default.
- W4377092014 created "2023-05-20" @default.
- W4377092014 creator A5006000280 @default.
- W4377092014 creator A5013878126 @default.
- W4377092014 creator A5029561912 @default.
- W4377092014 creator A5047128725 @default.
- W4377092014 creator A5048012404 @default.
- W4377092014 creator A5066034271 @default.
- W4377092014 creator A5076575975 @default.
- W4377092014 date "2023-09-01" @default.
- W4377092014 modified "2023-09-23" @default.
- W4377092014 title "Fatigue behavior of Al-CFRP spot-welded joints prepared by electromagnetic pulse welding" @default.
- W4377092014 cites W1847702517 @default.
- W4377092014 cites W1966061852 @default.
- W4377092014 cites W1990816070 @default.
- W4377092014 cites W2017713335 @default.
- W4377092014 cites W2085814912 @default.
- W4377092014 cites W2088329697 @default.
- W4377092014 cites W2291506009 @default.
- W4377092014 cites W2751129494 @default.
- W4377092014 cites W2801890278 @default.
- W4377092014 cites W2809649914 @default.
- W4377092014 cites W2892098259 @default.
- W4377092014 cites W2921835375 @default.
- W4377092014 cites W2967764451 @default.
- W4377092014 cites W2975410777 @default.
- W4377092014 cites W3021837200 @default.
- W4377092014 cites W3117917733 @default.
- W4377092014 cites W3132663578 @default.
- W4377092014 cites W3152738772 @default.
- W4377092014 cites W3161570955 @default.
- W4377092014 cites W3216978970 @default.
- W4377092014 cites W4200224648 @default.
- W4377092014 cites W4200397326 @default.
- W4377092014 cites W4205552059 @default.
- W4377092014 cites W4205600163 @default.
- W4377092014 cites W4214588591 @default.
- W4377092014 cites W4221100089 @default.
- W4377092014 cites W4224884878 @default.
- W4377092014 cites W4281617348 @default.
- W4377092014 cites W4295881968 @default.
- W4377092014 cites W4307812067 @default.
- W4377092014 cites W4311968534 @default.
- W4377092014 cites W4320882450 @default.
- W4377092014 cites W606235060 @default.
- W4377092014 doi "https://doi.org/10.1016/j.ijfatigue.2023.107715" @default.
- W4377092014 hasPublicationYear "2023" @default.
- W4377092014 type Work @default.
- W4377092014 citedByCount "0" @default.
- W4377092014 crossrefType "journal-article" @default.
- W4377092014 hasAuthorship W4377092014A5006000280 @default.
- W4377092014 hasAuthorship W4377092014A5013878126 @default.
- W4377092014 hasAuthorship W4377092014A5029561912 @default.
- W4377092014 hasAuthorship W4377092014A5047128725 @default.
- W4377092014 hasAuthorship W4377092014A5048012404 @default.
- W4377092014 hasAuthorship W4377092014A5066034271 @default.
- W4377092014 hasAuthorship W4377092014A5076575975 @default.
- W4377092014 hasConcept C104779481 @default.
- W4377092014 hasConcept C105795698 @default.
- W4377092014 hasConcept C112950240 @default.
- W4377092014 hasConcept C127413603 @default.
- W4377092014 hasConcept C131850400 @default.
- W4377092014 hasConcept C151730666 @default.
- W4377092014 hasConcept C159985019 @default.
- W4377092014 hasConcept C173291955 @default.
- W4377092014 hasConcept C18555067 @default.
- W4377092014 hasConcept C192562407 @default.
- W4377092014 hasConcept C19474535 @default.
- W4377092014 hasConcept C26771246 @default.
- W4377092014 hasConcept C2777178879 @default.
- W4377092014 hasConcept C30239060 @default.
- W4377092014 hasConcept C33923547 @default.
- W4377092014 hasConcept C58097730 @default.
- W4377092014 hasConcept C58396970 @default.
- W4377092014 hasConcept C66938386 @default.
- W4377092014 hasConcept C77928131 @default.
- W4377092014 hasConcept C86803240 @default.
- W4377092014 hasConceptScore W4377092014C104779481 @default.
- W4377092014 hasConceptScore W4377092014C105795698 @default.
- W4377092014 hasConceptScore W4377092014C112950240 @default.
- W4377092014 hasConceptScore W4377092014C127413603 @default.
- W4377092014 hasConceptScore W4377092014C131850400 @default.
- W4377092014 hasConceptScore W4377092014C151730666 @default.
- W4377092014 hasConceptScore W4377092014C159985019 @default.
- W4377092014 hasConceptScore W4377092014C173291955 @default.
- W4377092014 hasConceptScore W4377092014C18555067 @default.
- W4377092014 hasConceptScore W4377092014C192562407 @default.
- W4377092014 hasConceptScore W4377092014C19474535 @default.
- W4377092014 hasConceptScore W4377092014C26771246 @default.
- W4377092014 hasConceptScore W4377092014C2777178879 @default.
- W4377092014 hasConceptScore W4377092014C30239060 @default.
- W4377092014 hasConceptScore W4377092014C33923547 @default.
- W4377092014 hasConceptScore W4377092014C58097730 @default.
- W4377092014 hasConceptScore W4377092014C58396970 @default.
- W4377092014 hasConceptScore W4377092014C66938386 @default.
- W4377092014 hasConceptScore W4377092014C77928131 @default.
- W4377092014 hasConceptScore W4377092014C86803240 @default.
- W4377092014 hasLocation W43770920141 @default.