• W4377097166 abstract "The effect of various solution heat treatment temperatures (i.e., 1120, 1160, 1200 and 1240 °C) on the microstructure, grain morphology and crystallographic texture of IN939 fabricated by powder bed fusion-laser beam (PBF-LB) was investigated. Microstructural analyses showed that the high-temperature gradient and rapid solidification of the PBF-LB processing caused different resulting microstructures compared to conventionally produced counterparts. The melt pool morphologies and laser scanning paths were examined in the as-fabricated samples in the XZ- and XY-planes, respectively. After the application of solution heat treatment at 1120 °C, the as-fabricated PBF-LB initial microstructure was still apparent. For solution heat treatments of 1200 °C and above, the melt pool and scanning path morphologies disappeared and converted into a mixture of columnar grains in the XZ-plane and equiaxed grains in the XY-plane. On the other hand, large equiaxed grains were observed when the samples were solutionized at 1240 °C. Additionally, γ′ phase precipitated within the matrix after all solution heat treatment conditions, which led to increase in the microhardness values. According to electron backscatter diffraction (EBSD) analyses, both as-fabricated and solution heat-treated samples had intense texture with {001} plane normal parallel to the building direction. The first recrystallized grains began to appear when the samples were subjected to the solution heat treatment at 1160 °C and the fraction of the recrystallized grains increased with increasing temperature, as supported by kernel average misorientation (KAM) and grain spread orientation (GOS) analyses." @default.
• W4377097166 created "2023-05-20" @default.
• W4377097166 creator A5000750226 @default.
• W4377097166 creator A5006381960 @default.
• W4377097166 creator A5014912802 @default.
• W4377097166 creator A5019126862 @default.
• W4377097166 creator A5025089452 @default.
• W4377097166 creator A5027073208 @default.
• W4377097166 creator A5028009856 @default.
• W4377097166 creator A5039713662 @default.
• W4377097166 creator A5089792486 @default.
• W4377097166 date "2023-05-01" @default.
• W4377097166 modified "2023-09-27" @default.
• W4377097166 title "Effect of solution heat treatment on the microstructure and crystallographic texture of IN939 fabricated by powder bed fusion-laser beam" @default.
• W4377097166 cites W1966325830 @default.
• W4377097166 cites W2012025466 @default.
• W4377097166 cites W2041850553 @default.
• W4377097166 cites W2042927149 @default.
• W4377097166 cites W2046735213 @default.
• W4377097166 cites W2052886754 @default.
• W4377097166 cites W2607588067 @default.
• W4377097166 cites W2620464816 @default.
• W4377097166 cites W2808550274 @default.
• W4377097166 cites W2891727166 @default.
• W4377097166 cites W2912115825 @default.
• W4377097166 cites W2914658291 @default.
• W4377097166 cites W2918999636 @default.
• W4377097166 cites W3039408978 @default.
• W4377097166 cites W3043559029 @default.
• W4377097166 cites W3046205625 @default.
• W4377097166 cites W3127613765 @default.
• W4377097166 cites W3138753808 @default.
• W4377097166 cites W3174861781 @default.
• W4377097166 cites W3180147417 @default.
• W4377097166 cites W3181869550 @default.
• W4377097166 cites W4225390097 @default.
• W4377097166 cites W4283786941 @default.
• W4377097166 cites W4285033659 @default.
• W4377097166 cites W4288066809 @default.
• W4377097166 cites W4296806563 @default.
• W4377097166 cites W623231525 @default.
• W4377097166 doi "https://doi.org/10.1016/j.jmrt.2023.05.152" @default.
• W4377097166 hasPublicationYear "2023" @default.
• W4377097166 type Work @default.
• W4377097166 citedByCount "0" @default.
• W4377097166 crossrefType "journal-article" @default.
• W4377097166 hasAuthorship W4377097166A5000750226 @default.
• W4377097166 hasAuthorship W4377097166A5006381960 @default.
• W4377097166 hasAuthorship W4377097166A5014912802 @default.
• W4377097166 hasAuthorship W4377097166A5019126862 @default.
• W4377097166 hasAuthorship W4377097166A5025089452 @default.
• W4377097166 hasAuthorship W4377097166A5027073208 @default.
• W4377097166 hasAuthorship W4377097166A5028009856 @default.
• W4377097166 hasAuthorship W4377097166A5039713662 @default.
• W4377097166 hasAuthorship W4377097166A5089792486 @default.
• W4377097166 hasBestOaLocation W43770971661 @default.
• W4377097166 hasConcept C115961682 @default.
• W4377097166 hasConcept C138885662 @default.
• W4377097166 hasConcept C154945302 @default.
• W4377097166 hasConcept C158525013 @default.
• W4377097166 hasConcept C159985019 @default.
• W4377097166 hasConcept C192562407 @default.
• W4377097166 hasConcept C26771246 @default.
• W4377097166 hasConcept C2778117898 @default.
• W4377097166 hasConcept C27805521 @default.
• W4377097166 hasConcept C2781195486 @default.
• W4377097166 hasConcept C41008148 @default.
• W4377097166 hasConcept C41895202 @default.
• W4377097166 hasConcept C47908070 @default.
• W4377097166 hasConcept C81710450 @default.
• W4377097166 hasConcept C87976508 @default.
• W4377097166 hasConceptScore W4377097166C115961682 @default.
• W4377097166 hasConceptScore W4377097166C138885662 @default.
• W4377097166 hasConceptScore W4377097166C154945302 @default.
• W4377097166 hasConceptScore W4377097166C158525013 @default.
• W4377097166 hasConceptScore W4377097166C159985019 @default.
• W4377097166 hasConceptScore W4377097166C192562407 @default.
• W4377097166 hasConceptScore W4377097166C26771246 @default.
• W4377097166 hasConceptScore W4377097166C2778117898 @default.
• W4377097166 hasConceptScore W4377097166C27805521 @default.
• W4377097166 hasConceptScore W4377097166C2781195486 @default.
• W4377097166 hasConceptScore W4377097166C41008148 @default.
• W4377097166 hasConceptScore W4377097166C41895202 @default.
• W4377097166 hasConceptScore W4377097166C47908070 @default.
• W4377097166 hasConceptScore W4377097166C81710450 @default.
• W4377097166 hasConceptScore W4377097166C87976508 @default.
• W4377097166 hasFunder F4320320847 @default.
• W4377097166 hasFunder F4320335322 @default.
• W4377097166 hasLocation W43770971661 @default.
• W4377097166 hasOpenAccess W4377097166 @default.
• W4377097166 hasPrimaryLocation W43770971661 @default.
• W4377097166 hasRelatedWork W1602799148 @default.
• W4377097166 hasRelatedWork W1710701645 @default.
• W4377097166 hasRelatedWork W1975812785 @default.
• W4377097166 hasRelatedWork W1993018310 @default.
• W4377097166 hasRelatedWork W2019260000 @default.
• W4377097166 hasRelatedWork W2021889364 @default.
• W4377097166 hasRelatedWork W2046065358 @default.

• next