- W4377141878 abstract "Warming composite resin before insertion to reduce viscosity is advocated for improving adaptation and reducing voids. This study evaluated how prewarming altered porosities, adaptation, and strength. Twenty composite restorations were placed in 2 increments in typodont teeth with a large Class II preparation. The composite was either at room temperature (control) or prewarmed to 68 °C (n = 10/group). Each increment was light-cured for 20s. After 24h, the restored teeth were sectioned and imaged under a stereomicroscope. Examiners ranked the quality of adaptation to walls and between increments, and the presence of voids on a 0-3 scale. Results were statistically analyzed using Mann-Whitney U Test. Diametral tensile strength of monolithic or incrementally-filled composite cylinders (6 mm diameter × 4 mm height; n = 10/group) made with room temperature or prewarmed composite were tested at 0.5 mm/min. Strength results were analyzed using ANOVA statistics followed by pairwise comparisons. Restorations made with prewarmed composite had significantly fewer large voids and better adaptation to cavity walls and between layers (P < 0.05). Strength of prewarmed composite was higher than room temperature composite, and was significantly higher in monolithic specimens (P < 0.05). It was concluded that prewarming conventional composite can improve its handling, making it handle more like a flowable composite without jeopardizing physical properties. The prewarmed composite was found to have better adaptation and fewer voids, and attained higher strength than composite that was not prewarmed." @default.
- W4377141878 created "2023-05-21" @default.
- W4377141878 creator A5024337839 @default.
- W4377141878 creator A5024602121 @default.
- W4377141878 creator A5060333984 @default.
- W4377141878 creator A5062962447 @default.
- W4377141878 date "2023-07-01" @default.
- W4377141878 modified "2023-09-30" @default.
- W4377141878 title "Prewarming effect on adaptation, porosities, and strength of a composite resin" @default.
- W4377141878 cites W1990262520 @default.
- W4377141878 cites W2014289309 @default.
- W4377141878 cites W2030380529 @default.
- W4377141878 cites W2040370527 @default.
- W4377141878 cites W2041121449 @default.
- W4377141878 cites W2059643718 @default.
- W4377141878 cites W2060829489 @default.
- W4377141878 cites W2064067726 @default.
- W4377141878 cites W2082849534 @default.
- W4377141878 cites W2099318589 @default.
- W4377141878 cites W2105836571 @default.
- W4377141878 cites W2109595180 @default.
- W4377141878 cites W2110683752 @default.
- W4377141878 cites W2114053828 @default.
- W4377141878 cites W2116893589 @default.
- W4377141878 cites W2122103801 @default.
- W4377141878 cites W2123082819 @default.
- W4377141878 cites W2136763833 @default.
- W4377141878 cites W2151146767 @default.
- W4377141878 cites W2793414260 @default.
- W4377141878 cites W2950803270 @default.
- W4377141878 cites W2951524617 @default.
- W4377141878 cites W2971288477 @default.
- W4377141878 cites W2993256697 @default.
- W4377141878 cites W3094397952 @default.
- W4377141878 cites W4214615958 @default.
- W4377141878 cites W4312196517 @default.
- W4377141878 doi "https://doi.org/10.1016/j.jmbbm.2023.105913" @default.
- W4377141878 hasPubMedId "https://pubmed.ncbi.nlm.nih.gov/37257311" @default.
- W4377141878 hasPublicationYear "2023" @default.
- W4377141878 type Work @default.
- W4377141878 citedByCount "0" @default.
- W4377141878 crossrefType "journal-article" @default.
- W4377141878 hasAuthorship W4377141878A5024337839 @default.
- W4377141878 hasAuthorship W4377141878A5024602121 @default.
- W4377141878 hasAuthorship W4377141878A5060333984 @default.
- W4377141878 hasAuthorship W4377141878A5062962447 @default.
- W4377141878 hasConcept C104779481 @default.
- W4377141878 hasConcept C112950240 @default.
- W4377141878 hasConcept C120665830 @default.
- W4377141878 hasConcept C121332964 @default.
- W4377141878 hasConcept C139807058 @default.
- W4377141878 hasConcept C159985019 @default.
- W4377141878 hasConcept C192562407 @default.
- W4377141878 hasConceptScore W4377141878C104779481 @default.
- W4377141878 hasConceptScore W4377141878C112950240 @default.
- W4377141878 hasConceptScore W4377141878C120665830 @default.
- W4377141878 hasConceptScore W4377141878C121332964 @default.
- W4377141878 hasConceptScore W4377141878C139807058 @default.
- W4377141878 hasConceptScore W4377141878C159985019 @default.
- W4377141878 hasConceptScore W4377141878C192562407 @default.
- W4377141878 hasLocation W43771418781 @default.
- W4377141878 hasLocation W43771418782 @default.
- W4377141878 hasOpenAccess W4377141878 @default.
- W4377141878 hasPrimaryLocation W43771418781 @default.
- W4377141878 hasRelatedWork W1975608897 @default.
- W4377141878 hasRelatedWork W2005496670 @default.
- W4377141878 hasRelatedWork W2089085266 @default.
- W4377141878 hasRelatedWork W2360132121 @default.
- W4377141878 hasRelatedWork W2729932191 @default.
- W4377141878 hasRelatedWork W2795554382 @default.
- W4377141878 hasRelatedWork W3048672776 @default.
- W4377141878 hasRelatedWork W3122552578 @default.
- W4377141878 hasRelatedWork W4281567869 @default.
- W4377141878 hasRelatedWork W4285731133 @default.
- W4377141878 hasVolume "143" @default.
- W4377141878 isParatext "false" @default.
- W4377141878 isRetracted "false" @default.
- W4377141878 workType "article" @default.