- W4378450574 abstract "In present study, the influence of glass wool fiber (GWF) reinforcements and the application of heat resistant paint has been studied on the performance of self-compacting mortar (SCM) at ambient condition and at elevated temperatures of 200 °C, 400 °C, 600 °C, and 800 °C. Sixteen mix designs were prepared for SCM (with 25% fly ash) using GWF reinforcement of 0%, 0.5%, 1%, 1.5%, and varying the effective water to cement (w/c) ratio as; 0.43, 0.49, 0.55, and 0.70. The intrusion of GWF resulted into decrease in slump flow and v-funnel flow speed, increase in yield stress and plastic viscosity, whereas, the influence of effective w/c ratio on rheology of fresh SCM mix was opposite to glass wool fiber (GWF). For all variation of effective w/c ratio and GWF reinforcements, the values of slump flow and v-funnel flow were within the EFNARC limits. Increasing GWF reinforcement and the effective w/c ratio, compressive strength of SCM were decreased, but GWF yielded positive impact on flexural strength. SCM with 1% GWF reinforcements showed best result at effective w/c of 0.43, imparting highest flexural strength of 8.7 MPa. The application of heat resistant coating has shown a significant protection to SCM samples up to the maximum heating temperature of 800 °C by limiting the loss of mechanical strength within small percentage, whereas, the loss of mechanical strength was severe (about 45% to 65%) for uncoated samples. Thermogravimetric (TG) analysis of SCM powder revealed the thermal stability of SCM mix up to 1000 °C and the mass loss occurred correspond to the heating at temperature of 400 °C and 800 °C was 0.3%, and 7.5%, respectively." @default.
- W4378450574 created "2023-05-27" @default.
- W4378450574 creator A5005823767 @default.
- W4378450574 creator A5058801789 @default.
- W4378450574 creator A5081743159 @default.
- W4378450574 date "2023-08-01" @default.
- W4378450574 modified "2023-10-16" @default.
- W4378450574 title "Influence of glass wool fiber reinforcement and heat resistant coating on behavior of self-compacting mortar at elevated temperatures" @default.
- W4378450574 cites W1971726089 @default.
- W4378450574 cites W1979756762 @default.
- W4378450574 cites W1983483542 @default.
- W4378450574 cites W1983905553 @default.
- W4378450574 cites W1996104466 @default.
- W4378450574 cites W2012473062 @default.
- W4378450574 cites W2015441603 @default.
- W4378450574 cites W2037434890 @default.
- W4378450574 cites W2039115883 @default.
- W4378450574 cites W2041233846 @default.
- W4378450574 cites W2046884224 @default.
- W4378450574 cites W2047601566 @default.
- W4378450574 cites W2050736700 @default.
- W4378450574 cites W2060131568 @default.
- W4378450574 cites W2072588388 @default.
- W4378450574 cites W2084088076 @default.
- W4378450574 cites W2107416083 @default.
- W4378450574 cites W2473755980 @default.
- W4378450574 cites W2604778313 @default.
- W4378450574 cites W2608212558 @default.
- W4378450574 cites W2620647314 @default.
- W4378450574 cites W2770720251 @default.
- W4378450574 cites W2888967064 @default.
- W4378450574 cites W2909925690 @default.
- W4378450574 cites W2953098929 @default.
- W4378450574 cites W2962901710 @default.
- W4378450574 cites W2998077514 @default.
- W4378450574 cites W3006941356 @default.
- W4378450574 cites W3025244164 @default.
- W4378450574 cites W3046666800 @default.
- W4378450574 cites W3127982990 @default.
- W4378450574 cites W3160166420 @default.
- W4378450574 cites W3176921192 @default.
- W4378450574 cites W3201708305 @default.
- W4378450574 doi "https://doi.org/10.1016/j.conbuildmat.2023.131876" @default.
- W4378450574 hasPublicationYear "2023" @default.
- W4378450574 type Work @default.
- W4378450574 citedByCount "0" @default.
- W4378450574 crossrefType "journal-article" @default.
- W4378450574 hasAuthorship W4378450574A5005823767 @default.
- W4378450574 hasAuthorship W4378450574A5058801789 @default.
- W4378450574 hasAuthorship W4378450574A5081743159 @default.
- W4378450574 hasConcept C159985019 @default.
- W4378450574 hasConcept C178405089 @default.
- W4378450574 hasConcept C192562407 @default.
- W4378450574 hasConcept C2779151659 @default.
- W4378450574 hasConcept C2779227376 @default.
- W4378450574 hasConcept C2781448156 @default.
- W4378450574 hasConcept C519885992 @default.
- W4378450574 hasConcept C67203356 @default.
- W4378450574 hasConceptScore W4378450574C159985019 @default.
- W4378450574 hasConceptScore W4378450574C178405089 @default.
- W4378450574 hasConceptScore W4378450574C192562407 @default.
- W4378450574 hasConceptScore W4378450574C2779151659 @default.
- W4378450574 hasConceptScore W4378450574C2779227376 @default.
- W4378450574 hasConceptScore W4378450574C2781448156 @default.
- W4378450574 hasConceptScore W4378450574C519885992 @default.
- W4378450574 hasConceptScore W4378450574C67203356 @default.
- W4378450574 hasLocation W43784505741 @default.
- W4378450574 hasOpenAccess W4378450574 @default.
- W4378450574 hasPrimaryLocation W43784505741 @default.
- W4378450574 hasRelatedWork W1975168330 @default.
- W4378450574 hasRelatedWork W2025687592 @default.
- W4378450574 hasRelatedWork W2033100407 @default.
- W4378450574 hasRelatedWork W2170527555 @default.
- W4378450574 hasRelatedWork W2376168832 @default.
- W4378450574 hasRelatedWork W2387616028 @default.
- W4378450574 hasRelatedWork W2390879093 @default.
- W4378450574 hasRelatedWork W2789571739 @default.
- W4378450574 hasRelatedWork W2944045227 @default.
- W4378450574 hasRelatedWork W3162732562 @default.
- W4378450574 hasVolume "392" @default.
- W4378450574 isParatext "false" @default.
- W4378450574 isRetracted "false" @default.
- W4378450574 workType "article" @default.