- W4378966345 abstract "In this study, Ti–6Al–xNb alloys with different Nb percentages (x = 3.5–21 wt%) were produced by the conventional powder metallurgy technique. After mixing and pressing the alloy powders in appropriate proportions, the green samples were sintered in a tube furnace under a vacuum atmosphere at 1200 °C for 2 h. The X-ray diffraction analysis (XRD) showed that all the alloys consist of α–Ti, TiNb (β–Ti) and AlNb2 phases. The results showed that the Ti–6Al–14Nb alloy among all alloys has the best mechanical properties, and the microhardness, tensile and flexural strength are 276.4 Vickers hardness (Hv0.2), 453 MPa and 1682 MPa, respectively. Tribological tests were carried out in both dry and wet conditions with Hanks' Balanced Salt Solution. While generally, the specific wear rates of the samples increased with Nb content up to 17.5 wt% under dry conditions, on the other hand, they increased with increasing Nb content under wet conditions. On the other hand, the specific wear rate increased with increasing the sliding distance. The best corrosion resistance alloy among all the samples was Ti–6Al–7Nb with −0.0968 V corrosion potential (Ecorr), 0.015 μA/cm2 corrosion current density (Icorr) values." @default.
- W4378966345 created "2023-06-02" @default.
- W4378966345 creator A5019568613 @default.
- W4378966345 creator A5020305028 @default.
- W4378966345 creator A5048456652 @default.
- W4378966345 creator A5092063061 @default.
- W4378966345 date "2023-08-01" @default.
- W4378966345 modified "2023-09-25" @default.
- W4378966345 title "Mechanical, wear and corrosion behavior of Ti–6Al–xNb (x = 3.5–21 wt%) alloys manufactured by powder metallurgy" @default.
- W4378966345 cites W1651243854 @default.
- W4378966345 cites W1968663624 @default.
- W4378966345 cites W1971730387 @default.
- W4378966345 cites W1973450008 @default.
- W4378966345 cites W1985577201 @default.
- W4378966345 cites W1992147020 @default.
- W4378966345 cites W2013474007 @default.
- W4378966345 cites W2014488765 @default.
- W4378966345 cites W2016558698 @default.
- W4378966345 cites W2019989023 @default.
- W4378966345 cites W2037951716 @default.
- W4378966345 cites W2066406268 @default.
- W4378966345 cites W2079954349 @default.
- W4378966345 cites W2090840767 @default.
- W4378966345 cites W2097733184 @default.
- W4378966345 cites W2128784311 @default.
- W4378966345 cites W2153577743 @default.
- W4378966345 cites W2293648577 @default.
- W4378966345 cites W2322910488 @default.
- W4378966345 cites W2528144104 @default.
- W4378966345 cites W2560643224 @default.
- W4378966345 cites W2755449836 @default.
- W4378966345 cites W2778680420 @default.
- W4378966345 cites W2792370842 @default.
- W4378966345 cites W2804899931 @default.
- W4378966345 cites W2809101453 @default.
- W4378966345 cites W2811087328 @default.
- W4378966345 cites W2890002131 @default.
- W4378966345 cites W2894035554 @default.
- W4378966345 cites W2894243922 @default.
- W4378966345 cites W2901929291 @default.
- W4378966345 cites W2936849861 @default.
- W4378966345 cites W2942008644 @default.
- W4378966345 cites W2967387545 @default.
- W4378966345 cites W2979969314 @default.
- W4378966345 cites W3018706098 @default.
- W4378966345 cites W3024142632 @default.
- W4378966345 cites W3027283677 @default.
- W4378966345 cites W3044288245 @default.
- W4378966345 cites W3092587611 @default.
- W4378966345 cites W3094932298 @default.
- W4378966345 cites W3118416626 @default.
- W4378966345 cites W3137254181 @default.
- W4378966345 cites W3137964080 @default.
- W4378966345 cites W3154594111 @default.
- W4378966345 cites W3156451894 @default.
- W4378966345 cites W3198703422 @default.
- W4378966345 cites W3216035212 @default.
- W4378966345 cites W379001449 @default.
- W4378966345 cites W4210432788 @default.
- W4378966345 cites W4220807352 @default.
- W4378966345 cites W4224012304 @default.
- W4378966345 cites W4224661796 @default.
- W4378966345 cites W4282580147 @default.
- W4378966345 cites W4286512627 @default.
- W4378966345 cites W4293394482 @default.
- W4378966345 cites W4293833210 @default.
- W4378966345 cites W4303673981 @default.
- W4378966345 cites W4307722750 @default.
- W4378966345 cites W4309433403 @default.
- W4378966345 cites W4310837402 @default.
- W4378966345 cites W4312014749 @default.
- W4378966345 cites W4317438848 @default.
- W4378966345 cites W4318426672 @default.
- W4378966345 cites W4319072764 @default.
- W4378966345 cites W4319264900 @default.
- W4378966345 cites W4361306823 @default.
- W4378966345 doi "https://doi.org/10.1016/j.powtec.2023.118696" @default.
- W4378966345 hasPublicationYear "2023" @default.
- W4378966345 type Work @default.
- W4378966345 citedByCount "0" @default.
- W4378966345 crossrefType "journal-article" @default.
- W4378966345 hasAuthorship W4378966345A5019568613 @default.
- W4378966345 hasAuthorship W4378966345A5020305028 @default.
- W4378966345 hasAuthorship W4378966345A5048456652 @default.
- W4378966345 hasAuthorship W4378966345A5092063061 @default.
- W4378966345 hasConcept C112950240 @default.
- W4378966345 hasConcept C159985019 @default.
- W4378966345 hasConcept C165720898 @default.
- W4378966345 hasConcept C167310744 @default.
- W4378966345 hasConcept C178405089 @default.
- W4378966345 hasConcept C178790620 @default.
- W4378966345 hasConcept C185592680 @default.
- W4378966345 hasConcept C191897082 @default.
- W4378966345 hasConcept C192562407 @default.
- W4378966345 hasConcept C20625102 @default.
- W4378966345 hasConcept C2780026712 @default.
- W4378966345 hasConcept C2781333061 @default.
- W4378966345 hasConcept C7794659 @default.