- W4380899018 abstract "Both surface nanocrystallization and high temperature favor nitrogen diffusion during plasma nitriding, but the surface nanostructure may be destroyed by high temperature to lose its diffusion-enhancing effect. In this paper, the combined effect of surface nanocrystallization by shot peening (SP) and nitriding temperature on the plasma nitriding of Ti–4Al–2V titanium alloy was studied. The results show that the interaction of nanocrystallization and temperature on plasma nitriding balanced best at 500 °C of the Ti–4Al–2V sample shot peened at both 0.2 MPa-10 min and 0.6 MPa-10 min. At this temperature, the surface nanocrystalline had maintained its thermal stability to some extent and played the greatest role in promoting nitrogen diffusion by more grain boundaries and a thickest nitrided layer was obtained on the SPed sample. The SPed sample nitrided at 500 °C exhibited better corrosion resistance and interface adhesion than the coarse-grained sample due to its denser/thicker nitrided layer and the retained gradient structure. In addition, the effect of surface roughness under different SP pressures on the corrosion resistance and adhesion of the nitrided layer was also concerned. A small surface roughness obtained under a low SP pressure was beneficial to improve the corrosion resistance and reflect the true adhesion of the nitrided layer." @default.
- W4380899018 created "2023-06-17" @default.
- W4380899018 creator A5021761853 @default.
- W4380899018 creator A5041358852 @default.
- W4380899018 creator A5082662124 @default.
- W4380899018 date "2023-09-01" @default.
- W4380899018 modified "2023-09-27" @default.
- W4380899018 title "Low-temperature plasma nitriding at 500°C on surface-nanocrystalline Ti–4Al–2V alloy" @default.
- W4380899018 cites W154904929 @default.
- W4380899018 cites W1886914095 @default.
- W4380899018 cites W1964968091 @default.
- W4380899018 cites W1965492739 @default.
- W4380899018 cites W1966406806 @default.
- W4380899018 cites W1971685393 @default.
- W4380899018 cites W1975517637 @default.
- W4380899018 cites W1996542466 @default.
- W4380899018 cites W2002288288 @default.
- W4380899018 cites W2007886232 @default.
- W4380899018 cites W2012472956 @default.
- W4380899018 cites W2019391149 @default.
- W4380899018 cites W2032709100 @default.
- W4380899018 cites W2034627905 @default.
- W4380899018 cites W2041926361 @default.
- W4380899018 cites W2050720478 @default.
- W4380899018 cites W2063401697 @default.
- W4380899018 cites W2069416742 @default.
- W4380899018 cites W2070674909 @default.
- W4380899018 cites W2078940142 @default.
- W4380899018 cites W2086917164 @default.
- W4380899018 cites W2093001977 @default.
- W4380899018 cites W2100652762 @default.
- W4380899018 cites W2119942169 @default.
- W4380899018 cites W2127210151 @default.
- W4380899018 cites W2398544446 @default.
- W4380899018 cites W2429464928 @default.
- W4380899018 cites W2555379057 @default.
- W4380899018 cites W2624682134 @default.
- W4380899018 cites W2790829659 @default.
- W4380899018 cites W2944847224 @default.
- W4380899018 cites W2946972549 @default.
- W4380899018 cites W2951840268 @default.
- W4380899018 cites W3095921726 @default.
- W4380899018 cites W3133658070 @default.
- W4380899018 cites W4220701207 @default.
- W4380899018 cites W4318567202 @default.
- W4380899018 doi "https://doi.org/10.1016/j.matchemphys.2023.128080" @default.
- W4380899018 hasPublicationYear "2023" @default.
- W4380899018 type Work @default.
- W4380899018 citedByCount "0" @default.
- W4380899018 crossrefType "journal-article" @default.
- W4380899018 hasAuthorship W4380899018A5021761853 @default.
- W4380899018 hasAuthorship W4380899018A5041358852 @default.
- W4380899018 hasAuthorship W4380899018A5082662124 @default.
- W4380899018 hasConcept C107365816 @default.
- W4380899018 hasConcept C13862629 @default.
- W4380899018 hasConcept C140676511 @default.
- W4380899018 hasConcept C159985019 @default.
- W4380899018 hasConcept C171250308 @default.
- W4380899018 hasConcept C191897082 @default.
- W4380899018 hasConcept C192562407 @default.
- W4380899018 hasConcept C194760766 @default.
- W4380899018 hasConcept C197751951 @default.
- W4380899018 hasConcept C20625102 @default.
- W4380899018 hasConcept C2779227376 @default.
- W4380899018 hasConcept C2780026712 @default.
- W4380899018 hasConceptScore W4380899018C107365816 @default.
- W4380899018 hasConceptScore W4380899018C13862629 @default.
- W4380899018 hasConceptScore W4380899018C140676511 @default.
- W4380899018 hasConceptScore W4380899018C159985019 @default.
- W4380899018 hasConceptScore W4380899018C171250308 @default.
- W4380899018 hasConceptScore W4380899018C191897082 @default.
- W4380899018 hasConceptScore W4380899018C192562407 @default.
- W4380899018 hasConceptScore W4380899018C194760766 @default.
- W4380899018 hasConceptScore W4380899018C197751951 @default.
- W4380899018 hasConceptScore W4380899018C20625102 @default.
- W4380899018 hasConceptScore W4380899018C2779227376 @default.
- W4380899018 hasConceptScore W4380899018C2780026712 @default.
- W4380899018 hasFunder F4320321001 @default.
- W4380899018 hasLocation W43808990181 @default.
- W4380899018 hasOpenAccess W4380899018 @default.
- W4380899018 hasPrimaryLocation W43808990181 @default.
- W4380899018 hasRelatedWork W1978924262 @default.
- W4380899018 hasRelatedWork W2054511049 @default.
- W4380899018 hasRelatedWork W2348019730 @default.
- W4380899018 hasRelatedWork W2353625337 @default.
- W4380899018 hasRelatedWork W2374443305 @default.
- W4380899018 hasRelatedWork W2376938014 @default.
- W4380899018 hasRelatedWork W2889384114 @default.
- W4380899018 hasRelatedWork W3097783663 @default.
- W4380899018 hasRelatedWork W4210319990 @default.
- W4380899018 hasRelatedWork W4386192417 @default.
- W4380899018 hasVolume "306" @default.
- W4380899018 isParatext "false" @default.
- W4380899018 isRetracted "false" @default.
- W4380899018 workType "article" @default.