- W4381682186 abstract "An experimental study was carried out on the effect of oxidation temperature and the oxide film composition on the compressibility of porous materials. samples were annealed at different temperatures; the size change in the samples after annealing was measured. The phase composition of the oxide layer was investigated. Magnetite was generated at between 350 and 450°C, and two-phase oxide was formed at 550°C, after oxidation, weight gain was determined. The presence of pore overgrowth, which reduces porosity, was confirmed by metallographic tests. The maximum porosity is found in the oxidized samples produced by pressing at room temperature. The process of high-temperature oxidation of iron powder before pressing and in the state of free filling in a fluidized bed, as well as the effect of the content of oxides on magnetic characteristics, has been studied. The impact of oxidation on the compressibility of samples of iron powder was investigated. In this study, It was observed that the range of 350-450°C, which offers the best compressibility and the necessary composition of the oxide film, is also related to the presence of magnetite in the iron oxide coating. is the ideal temperature for oxidation and repressing. the deformation of porous materials exposed to iron powder oxidation was tested." @default.
- W4381682186 created "2023-06-23" @default.
- W4381682186 creator A5025449725 @default.
- W4381682186 date "2023-06-22" @default.
- W4381682186 modified "2023-10-14" @default.
- W4381682186 title "Experimental Study on the Effect of Oxidation on the Compressibility of Iron Powder" @default.
- W4381682186 cites W2795264023 @default.
- W4381682186 cites W2804611663 @default.
- W4381682186 cites W2883821780 @default.
- W4381682186 cites W2900942907 @default.
- W4381682186 cites W2910518303 @default.
- W4381682186 cites W2937406977 @default.
- W4381682186 cites W2967577157 @default.
- W4381682186 cites W2981879967 @default.
- W4381682186 cites W2983997499 @default.
- W4381682186 cites W3016138207 @default.
- W4381682186 cites W3043358326 @default.
- W4381682186 cites W3081327505 @default.
- W4381682186 cites W3081691232 @default.
- W4381682186 cites W3088568580 @default.
- W4381682186 cites W3098649559 @default.
- W4381682186 cites W3107163732 @default.
- W4381682186 cites W3111833368 @default.
- W4381682186 cites W3162781556 @default.
- W4381682186 cites W3173527536 @default.
- W4381682186 cites W3175157447 @default.
- W4381682186 cites W3192159604 @default.
- W4381682186 cites W4200059733 @default.
- W4381682186 cites W4200409614 @default.
- W4381682186 cites W4211239371 @default.
- W4381682186 cites W4283704423 @default.
- W4381682186 cites W4289527097 @default.
- W4381682186 cites W4366817082 @default.
- W4381682186 doi "https://doi.org/10.21062/mft.2023.045" @default.
- W4381682186 hasPublicationYear "2023" @default.
- W4381682186 type Work @default.
- W4381682186 citedByCount "0" @default.
- W4381682186 crossrefType "journal-article" @default.
- W4381682186 hasAuthorship W4381682186A5025449725 @default.
- W4381682186 hasBestOaLocation W43816821861 @default.
- W4381682186 hasConcept C121332964 @default.
- W4381682186 hasConcept C127413603 @default.
- W4381682186 hasConcept C159985019 @default.
- W4381682186 hasConcept C191897082 @default.
- W4381682186 hasConcept C192562407 @default.
- W4381682186 hasConcept C2777697756 @default.
- W4381682186 hasConcept C2777781897 @default.
- W4381682186 hasConcept C2777855556 @default.
- W4381682186 hasConcept C2779851234 @default.
- W4381682186 hasConcept C42360764 @default.
- W4381682186 hasConcept C6648577 @default.
- W4381682186 hasConcept C84655787 @default.
- W4381682186 hasConcept C97355855 @default.
- W4381682186 hasConceptScore W4381682186C121332964 @default.
- W4381682186 hasConceptScore W4381682186C127413603 @default.
- W4381682186 hasConceptScore W4381682186C159985019 @default.
- W4381682186 hasConceptScore W4381682186C191897082 @default.
- W4381682186 hasConceptScore W4381682186C192562407 @default.
- W4381682186 hasConceptScore W4381682186C2777697756 @default.
- W4381682186 hasConceptScore W4381682186C2777781897 @default.
- W4381682186 hasConceptScore W4381682186C2777855556 @default.
- W4381682186 hasConceptScore W4381682186C2779851234 @default.
- W4381682186 hasConceptScore W4381682186C42360764 @default.
- W4381682186 hasConceptScore W4381682186C6648577 @default.
- W4381682186 hasConceptScore W4381682186C84655787 @default.
- W4381682186 hasConceptScore W4381682186C97355855 @default.
- W4381682186 hasLocation W43816821861 @default.
- W4381682186 hasOpenAccess W4381682186 @default.
- W4381682186 hasPrimaryLocation W43816821861 @default.
- W4381682186 hasRelatedWork W1990717809 @default.
- W4381682186 hasRelatedWork W1999457347 @default.
- W4381682186 hasRelatedWork W2087190874 @default.
- W4381682186 hasRelatedWork W2154206987 @default.
- W4381682186 hasRelatedWork W2161845819 @default.
- W4381682186 hasRelatedWork W2371791606 @default.
- W4381682186 hasRelatedWork W2926371681 @default.
- W4381682186 hasRelatedWork W297328956 @default.
- W4381682186 hasRelatedWork W4282826538 @default.
- W4381682186 hasRelatedWork W4367316069 @default.
- W4381682186 isParatext "false" @default.
- W4381682186 isRetracted "false" @default.
- W4381682186 workType "article" @default.