- W4382139417 abstract "In the present study three systems of carbon steel (1008) are evaluated, which were provide of two corrosion control methods, barrier and cathodic protection (painted and galvanized respectively) commonly used in the construction industry. They were evaluated under accelerated conditions exposed in fog chamber, according to ASTM B-117, which specifies continues exposition of sodium chloride at 5% and 35 °C. The main aim of the research was to characterize the corrosion resistance and to determine the degradation mechanism under test’s conditions. The results after 1080 and 3500 hours of exposure are presented, with adhesion measure (ASTM D-3359) and scratch resistance measure (D-1654) for each exposure time, as well as the characterization of corrosion attack through the mapping analysis of Scanning Electron Microscope / Energy Dispersive X-ray. According to the results it is proposed that the corrosion of the systems under study begins at galvanized – metal base interface. Later advances due to formation of porous layer of zinc hydroxi-chloride, which it’s characteristic of environments with chloride ions, forming zinc’s corrosion products like zinc oxide and zinc hydroxide on the porous layer until iron starts to dissolve, producing iron oxide and iron oxy-hydroxide on the zinc’s corrosion products and porous layer." @default.
- W4382139417 created "2023-06-27" @default.
- W4382139417 creator A5000504721 @default.
- W4382139417 creator A5021599594 @default.
- W4382139417 creator A5041289624 @default.
- W4382139417 creator A5041418608 @default.
- W4382139417 creator A5042750808 @default.
- W4382139417 creator A5050733247 @default.
- W4382139417 creator A5056919829 @default.
- W4382139417 creator A5065559927 @default.
- W4382139417 creator A5070648104 @default.
- W4382139417 creator A5092272496 @default.
- W4382139417 date "2015-06-01" @default.
- W4382139417 modified "2023-09-26" @default.
- W4382139417 title "Characterization of Corrosion Behavior of Painted Galvanized Steel under Accelerated Conditions." @default.
- W4382139417 cites W1996391661 @default.
- W4382139417 cites W2075748535 @default.
- W4382139417 cites W4240121232 @default.
- W4382139417 doi "https://doi.org/10.1016/s1452-3981(23)06653-1" @default.
- W4382139417 hasPublicationYear "2015" @default.
- W4382139417 type Work @default.
- W4382139417 citedByCount "0" @default.
- W4382139417 crossrefType "journal-article" @default.
- W4382139417 hasAuthorship W4382139417A5000504721 @default.
- W4382139417 hasAuthorship W4382139417A5021599594 @default.
- W4382139417 hasAuthorship W4382139417A5041289624 @default.
- W4382139417 hasAuthorship W4382139417A5041418608 @default.
- W4382139417 hasAuthorship W4382139417A5042750808 @default.
- W4382139417 hasAuthorship W4382139417A5050733247 @default.
- W4382139417 hasAuthorship W4382139417A5056919829 @default.
- W4382139417 hasAuthorship W4382139417A5065559927 @default.
- W4382139417 hasAuthorship W4382139417A5070648104 @default.
- W4382139417 hasAuthorship W4382139417A5092272496 @default.
- W4382139417 hasBestOaLocation W43821394171 @default.
- W4382139417 hasConcept C147789679 @default.
- W4382139417 hasConcept C159985019 @default.
- W4382139417 hasConcept C179104552 @default.
- W4382139417 hasConcept C185592680 @default.
- W4382139417 hasConcept C191897082 @default.
- W4382139417 hasConcept C192562407 @default.
- W4382139417 hasConcept C20625102 @default.
- W4382139417 hasConcept C26771246 @default.
- W4382139417 hasConcept C2775896084 @default.
- W4382139417 hasConcept C2776066698 @default.
- W4382139417 hasConcept C2778560533 @default.
- W4382139417 hasConcept C2778562268 @default.
- W4382139417 hasConcept C2778695967 @default.
- W4382139417 hasConcept C2779227376 @default.
- W4382139417 hasConcept C2779851234 @default.
- W4382139417 hasConcept C535196362 @default.
- W4382139417 hasConcept C6648577 @default.
- W4382139417 hasConcept C8846229 @default.
- W4382139417 hasConceptScore W4382139417C147789679 @default.
- W4382139417 hasConceptScore W4382139417C159985019 @default.
- W4382139417 hasConceptScore W4382139417C179104552 @default.
- W4382139417 hasConceptScore W4382139417C185592680 @default.
- W4382139417 hasConceptScore W4382139417C191897082 @default.
- W4382139417 hasConceptScore W4382139417C192562407 @default.
- W4382139417 hasConceptScore W4382139417C20625102 @default.
- W4382139417 hasConceptScore W4382139417C26771246 @default.
- W4382139417 hasConceptScore W4382139417C2775896084 @default.
- W4382139417 hasConceptScore W4382139417C2776066698 @default.
- W4382139417 hasConceptScore W4382139417C2778560533 @default.
- W4382139417 hasConceptScore W4382139417C2778562268 @default.
- W4382139417 hasConceptScore W4382139417C2778695967 @default.
- W4382139417 hasConceptScore W4382139417C2779227376 @default.
- W4382139417 hasConceptScore W4382139417C2779851234 @default.
- W4382139417 hasConceptScore W4382139417C535196362 @default.
- W4382139417 hasConceptScore W4382139417C6648577 @default.
- W4382139417 hasConceptScore W4382139417C8846229 @default.
- W4382139417 hasIssue "6" @default.
- W4382139417 hasLocation W43821394171 @default.
- W4382139417 hasOpenAccess W4382139417 @default.
- W4382139417 hasPrimaryLocation W43821394171 @default.
- W4382139417 hasRelatedWork W1976931754 @default.
- W4382139417 hasRelatedWork W1985488129 @default.
- W4382139417 hasRelatedWork W1987386141 @default.
- W4382139417 hasRelatedWork W2057596709 @default.
- W4382139417 hasRelatedWork W2383046826 @default.
- W4382139417 hasRelatedWork W2778524441 @default.
- W4382139417 hasRelatedWork W2779521655 @default.
- W4382139417 hasRelatedWork W3124786062 @default.
- W4382139417 hasRelatedWork W4205446455 @default.
- W4382139417 hasRelatedWork W4310217081 @default.
- W4382139417 hasVolume "10" @default.
- W4382139417 isParatext "false" @default.
- W4382139417 isRetracted "false" @default.
- W4382139417 workType "article" @default.