• W4382795087 abstract "The weldability of twin-induced plasticity (TWIP) steel with ultra-high strength via friction stir welding (FSW) technique was investigated, and microstructural evolution and deformation behavior of whole and micro-zones of FSW TWIP joint were studied for the first time. The results showed that the content of recrystallized grains in the stir zone (SZ) increased from 10.5% of basal material (BM) to 14.2%, and that of heat affected zone (HAZ) increased to 78.6%. The percentage of annealing twins decreased from 26.8% in BM to 11% in SZ, while increased to 35% in HAZ. Compared with the BM, the ultimate tensile strength and yield strength of the FSW joint increased to 1036 MPa and 550 MPa, respectively, reaching 106.7% and 110.9% of BM, respectively. The elongation of the entire joint was 50.5%, which was lower than that of BM due to the nonuniform deformation during the tensile test. The engineering strain was mainly concentrated in BM and SZ and transferred to each other during the tensile test, while the engineering strain in HAZ was always the lowest. Finally, the tensile fracture occurred in the SZ. The order of ultimate tensile strength of micro-zones in the FSW joint was as follows: HAZ > BM ≈ SZ. The order of yield strength was as follows: HAZ > BM > SZ." @default.
• W4382795087 created "2023-07-02" @default.
• W4382795087 creator A5017239072 @default.
• W4382795087 creator A5037403472 @default.
• W4382795087 creator A5049242358 @default.
• W4382795087 creator A5054124734 @default.
• W4382795087 creator A5058924447 @default.
• W4382795087 creator A5062646279 @default.
• W4382795087 creator A5064436064 @default.
• W4382795087 creator A5074667554 @default.
• W4382795087 creator A5074940051 @default.
• W4382795087 date "2024-01-01" @default.
• W4382795087 modified "2023-09-23" @default.
• W4382795087 title "Microstructural evolution and deformation behavior of friction stir welded twin-induced plasticity steel" @default.
• W4382795087 cites W1274703628 @default.
• W4382795087 cites W1982606398 @default.
• W4382795087 cites W1984233617 @default.
• W4382795087 cites W1985986406 @default.
• W4382795087 cites W1989773011 @default.
• W4382795087 cites W1991334661 @default.
• W4382795087 cites W1999957100 @default.
• W4382795087 cites W2003129646 @default.
• W4382795087 cites W2011908431 @default.
• W4382795087 cites W2026199268 @default.
• W4382795087 cites W2031920866 @default.
• W4382795087 cites W2058520447 @default.
• W4382795087 cites W2068222912 @default.
• W4382795087 cites W2069416742 @default.
• W4382795087 cites W2123294155 @default.
• W4382795087 cites W2470395051 @default.
• W4382795087 cites W2554674036 @default.
• W4382795087 cites W2608051935 @default.
• W4382795087 cites W2736831392 @default.
• W4382795087 cites W2750516224 @default.
• W4382795087 cites W2770131335 @default.
• W4382795087 cites W2791785776 @default.
• W4382795087 cites W2900591433 @default.
• W4382795087 cites W2908716127 @default.
• W4382795087 cites W2912043582 @default.
• W4382795087 cites W2958948796 @default.
• W4382795087 cites W2971941398 @default.
• W4382795087 cites W2994323946 @default.
• W4382795087 cites W3031020006 @default.
• W4382795087 cites W3110900905 @default.
• W4382795087 cites W4213122434 @default.
• W4382795087 cites W4283079037 @default.
• W4382795087 cites W4306247403 @default.
• W4382795087 cites W753645979 @default.
• W4382795087 doi "https://doi.org/10.1016/j.jmst.2023.05.053" @default.
• W4382795087 hasPublicationYear "2024" @default.
• W4382795087 type Work @default.
• W4382795087 citedByCount "0" @default.
• W4382795087 crossrefType "journal-article" @default.
• W4382795087 hasAuthorship W4382795087A5017239072 @default.
• W4382795087 hasAuthorship W4382795087A5037403472 @default.
• W4382795087 hasAuthorship W4382795087A5049242358 @default.
• W4382795087 hasAuthorship W4382795087A5054124734 @default.
• W4382795087 hasAuthorship W4382795087A5058924447 @default.
• W4382795087 hasAuthorship W4382795087A5062646279 @default.
• W4382795087 hasAuthorship W4382795087A5064436064 @default.
• W4382795087 hasAuthorship W4382795087A5074667554 @default.
• W4382795087 hasAuthorship W4382795087A5074940051 @default.
• W4382795087 hasConcept C112950240 @default.
• W4382795087 hasConcept C159985019 @default.
• W4382795087 hasConcept C182508753 @default.
• W4382795087 hasConcept C191897082 @default.
• W4382795087 hasConcept C192562407 @default.
• W4382795087 hasConcept C19474535 @default.
• W4382795087 hasConcept C204366326 @default.
• W4382795087 hasConcept C2777855556 @default.
• W4382795087 hasConcept C2779863471 @default.
• W4382795087 hasConcept C40367268 @default.
• W4382795087 hasConcept C6840138 @default.
• W4382795087 hasConcept C79186407 @default.
• W4382795087 hasConcept C87976508 @default.
• W4382795087 hasConcept C88504338 @default.
• W4382795087 hasConceptScore W4382795087C112950240 @default.
• W4382795087 hasConceptScore W4382795087C159985019 @default.
• W4382795087 hasConceptScore W4382795087C182508753 @default.
• W4382795087 hasConceptScore W4382795087C191897082 @default.
• W4382795087 hasConceptScore W4382795087C192562407 @default.
• W4382795087 hasConceptScore W4382795087C19474535 @default.
• W4382795087 hasConceptScore W4382795087C204366326 @default.
• W4382795087 hasConceptScore W4382795087C2777855556 @default.
• W4382795087 hasConceptScore W4382795087C2779863471 @default.
• W4382795087 hasConceptScore W4382795087C40367268 @default.
• W4382795087 hasConceptScore W4382795087C6840138 @default.
• W4382795087 hasConceptScore W4382795087C79186407 @default.
• W4382795087 hasConceptScore W4382795087C87976508 @default.
• W4382795087 hasConceptScore W4382795087C88504338 @default.
• W4382795087 hasLocation W43827950871 @default.
• W4382795087 hasOpenAccess W4382795087 @default.
• W4382795087 hasPrimaryLocation W43827950871 @default.
• W4382795087 hasRelatedWork W2001513542 @default.
• W4382795087 hasRelatedWork W2089085266 @default.
• W4382795087 hasRelatedWork W2152746450 @default.
• W4382795087 hasRelatedWork W2729932191 @default.
• W4382795087 hasRelatedWork W2795554382 @default.

• next