- W4382933712 abstract "The effects of solution time and aging temperature on the microstructure and properties of C17300 beryllium copper alloy wire were studied by means of SEM, XRD, electronic universal tester and resistance tester. The results show that after solution treatment, the deformed twin structure disappears and the distorted crystal grows into equiaxed crystal. The optimum solution time is 90min, and the hardness and resistivity are 115HV and 1.13×10-7Ω·m respectively. The optimum solution time is 90min, and the hardness and resistivity are 115HV and 9.52×10-7Ω·m respectively. When the aging temperature is increased from 260°C to 340°C, the amount of grain boundary reaction is increased from 3.84% to 17.05%, and the precipitated phase changes from point to tumor-like distribution. When the aging temperature rises to 320°C, the mechanical properties are the best, with tensile strength of 1192.86MPa, hardness of 373.81HV and elongation of 5.16%. With the increase of aging temperature, the work hardening rate gradually increases, the number of dimples and micropores on the fracture surface decreases, and the granular precipitates at the bottom of dimples increase. In summary, the differences of microstructure and mechanical properties of beryllium bronze at different solution time and aging temperature are compared, which provides some basis for preparing high strength beryllium copper alloy microwires." @default.
- W4382933712 created "2023-07-04" @default.
- W4382933712 creator A5003358521 @default.
- W4382933712 creator A5005365468 @default.
- W4382933712 creator A5005762426 @default.
- W4382933712 creator A5021214519 @default.
- W4382933712 creator A5033004996 @default.
- W4382933712 creator A5065346031 @default.
- W4382933712 creator A5066432875 @default.
- W4382933712 creator A5072265110 @default.
- W4382933712 creator A5080703712 @default.
- W4382933712 date "2023-07-01" @default.
- W4382933712 modified "2023-09-27" @default.
- W4382933712 title "Study on the effect of heat treatment on the microstructure and properties of C17300 beryllium copper alloy microwires" @default.
- W4382933712 cites W2002122192 @default.
- W4382933712 cites W2008188297 @default.
- W4382933712 cites W2028748176 @default.
- W4382933712 cites W2061746150 @default.
- W4382933712 cites W2123104836 @default.
- W4382933712 cites W2132851640 @default.
- W4382933712 cites W2278268362 @default.
- W4382933712 cites W2462008438 @default.
- W4382933712 cites W2533964396 @default.
- W4382933712 cites W2577700631 @default.
- W4382933712 cites W2745074454 @default.
- W4382933712 cites W2755667888 @default.
- W4382933712 cites W2794431635 @default.
- W4382933712 cites W2903427807 @default.
- W4382933712 cites W2908174097 @default.
- W4382933712 cites W2945507843 @default.
- W4382933712 cites W2979393851 @default.
- W4382933712 cites W2980499137 @default.
- W4382933712 cites W3021063062 @default.
- W4382933712 cites W3035190431 @default.
- W4382933712 cites W3082146168 @default.
- W4382933712 cites W3130493591 @default.
- W4382933712 cites W3131922351 @default.
- W4382933712 cites W3167289291 @default.
- W4382933712 cites W4220973074 @default.
- W4382933712 cites W4221014827 @default.
- W4382933712 cites W4294958192 @default.
- W4382933712 cites W4296929668 @default.
- W4382933712 cites W4297186279 @default.
- W4382933712 cites W4303958985 @default.
- W4382933712 cites W4316467492 @default.
- W4382933712 cites W4324100564 @default.
- W4382933712 cites W4378472199 @default.
- W4382933712 cites W817404048 @default.
- W4382933712 doi "https://doi.org/10.1016/j.jmrt.2023.06.274" @default.
- W4382933712 hasPublicationYear "2023" @default.
- W4382933712 type Work @default.
- W4382933712 citedByCount "0" @default.
- W4382933712 crossrefType "journal-article" @default.
- W4382933712 hasAuthorship W4382933712A5003358521 @default.
- W4382933712 hasAuthorship W4382933712A5005365468 @default.
- W4382933712 hasAuthorship W4382933712A5005762426 @default.
- W4382933712 hasAuthorship W4382933712A5021214519 @default.
- W4382933712 hasAuthorship W4382933712A5033004996 @default.
- W4382933712 hasAuthorship W4382933712A5065346031 @default.
- W4382933712 hasAuthorship W4382933712A5066432875 @default.
- W4382933712 hasAuthorship W4382933712A5072265110 @default.
- W4382933712 hasAuthorship W4382933712A5080703712 @default.
- W4382933712 hasBestOaLocation W43829337121 @default.
- W4382933712 hasConcept C112950240 @default.
- W4382933712 hasConcept C119599485 @default.
- W4382933712 hasConcept C121332964 @default.
- W4382933712 hasConcept C127413603 @default.
- W4382933712 hasConcept C152327431 @default.
- W4382933712 hasConcept C159985019 @default.
- W4382933712 hasConcept C185544564 @default.
- W4382933712 hasConcept C191897082 @default.
- W4382933712 hasConcept C192562407 @default.
- W4382933712 hasConcept C199360897 @default.
- W4382933712 hasConcept C2780026712 @default.
- W4382933712 hasConcept C2781285689 @default.
- W4382933712 hasConcept C33947775 @default.
- W4382933712 hasConcept C41008148 @default.
- W4382933712 hasConcept C506630978 @default.
- W4382933712 hasConcept C544778455 @default.
- W4382933712 hasConcept C69990965 @default.
- W4382933712 hasConcept C81710450 @default.
- W4382933712 hasConcept C87976508 @default.
- W4382933712 hasConceptScore W4382933712C112950240 @default.
- W4382933712 hasConceptScore W4382933712C119599485 @default.
- W4382933712 hasConceptScore W4382933712C121332964 @default.
- W4382933712 hasConceptScore W4382933712C127413603 @default.
- W4382933712 hasConceptScore W4382933712C152327431 @default.
- W4382933712 hasConceptScore W4382933712C159985019 @default.
- W4382933712 hasConceptScore W4382933712C185544564 @default.
- W4382933712 hasConceptScore W4382933712C191897082 @default.
- W4382933712 hasConceptScore W4382933712C192562407 @default.
- W4382933712 hasConceptScore W4382933712C199360897 @default.
- W4382933712 hasConceptScore W4382933712C2780026712 @default.
- W4382933712 hasConceptScore W4382933712C2781285689 @default.
- W4382933712 hasConceptScore W4382933712C33947775 @default.
- W4382933712 hasConceptScore W4382933712C41008148 @default.
- W4382933712 hasConceptScore W4382933712C506630978 @default.
- W4382933712 hasConceptScore W4382933712C544778455 @default.