- W4383371811 abstract "The Ladle Furnace (LF) refining slag resistance of MgAlON–MgO composites synthesized from spent MgOC brick was investigated using the sessile drop technique, manifesting that MgAlON with slag corrosion thickness of 780 μm exhibits the best slag resistance than other composites. MgAlON–MgO composites react with the slag to generate calcium aluminate, spinel, and TiN. Furthermore, MgAlON–MgO composites with different MgO content show different corrosion process. The corrosion process of MgAlON and MgAlON–4.2 wt.%MgO proceeds with wetting, reaction, and infiltration processes, while that of MgAlON–10.5 wt.%MgO and MgAlON–15.7 wt.%MgO only proceeds with wetting and infiltration processes. Compared with MgAlON–10.5 wt.%MgO and MgAlON–15.7 wt.%MgO, MgAlON and MgAlON–4.2 wt.%MgO show low contact angle, presenting good slag wettability. Nevertheless, the viscosity of molten slag decreases with increasing MgO content, and MgAlON–MgO composites with high MgO content (MgAlON–10.5 wt.%MgO and MgAlON–15.7 wt.%MgO) show high porosity, thus aggravating the infiltration of molten slag. Compared with the wetting behaviour between molten slag and MgAlON–MgO composites, the infiltration of slag plays a decisive role in the slag corrosion process. Therefore, MgAlON and MgAlON–4.2 wt.%MgO exhibit better slag resistance, showing the potential application in the ladle furnace." @default.
- W4383371811 created "2023-07-07" @default.
- W4383371811 creator A5015996920 @default.
- W4383371811 creator A5019400621 @default.
- W4383371811 creator A5020147975 @default.
- W4383371811 creator A5022753725 @default.
- W4383371811 creator A5024261526 @default.
- W4383371811 creator A5067871430 @default.
- W4383371811 date "2023-11-01" @default.
- W4383371811 modified "2023-10-03" @default.
- W4383371811 title "Effect of MgO on corrosion mechanism under LF refining slag for MgAlON–MgO composites synthesized from spent MgO–C brick: Wetting behaviour, reaction process and infiltration mechanism" @default.
- W4383371811 cites W2000398507 @default.
- W4383371811 cites W2083607625 @default.
- W4383371811 cites W2084951273 @default.
- W4383371811 cites W2324231385 @default.
- W4383371811 cites W3046451627 @default.
- W4383371811 cites W3195000076 @default.
- W4383371811 cites W3200612695 @default.
- W4383371811 cites W3208303158 @default.
- W4383371811 cites W3208782085 @default.
- W4383371811 cites W4205761875 @default.
- W4383371811 cites W4211008829 @default.
- W4383371811 cites W4220741330 @default.
- W4383371811 cites W4280604401 @default.
- W4383371811 cites W4281708634 @default.
- W4383371811 cites W4283366256 @default.
- W4383371811 cites W4296260613 @default.
- W4383371811 cites W4299287504 @default.
- W4383371811 cites W4308038414 @default.
- W4383371811 cites W4317214449 @default.
- W4383371811 cites W4317655941 @default.
- W4383371811 cites W4362716420 @default.
- W4383371811 cites W4368370457 @default.
- W4383371811 cites W4376869104 @default.
- W4383371811 cites W4377193596 @default.
- W4383371811 cites W4378190070 @default.
- W4383371811 doi "https://doi.org/10.1016/j.jallcom.2023.171278" @default.
- W4383371811 hasPublicationYear "2023" @default.
- W4383371811 type Work @default.
- W4383371811 citedByCount "1" @default.
- W4383371811 countsByYear W43833718112023 @default.
- W4383371811 crossrefType "journal-article" @default.
- W4383371811 hasAuthorship W4383371811A5015996920 @default.
- W4383371811 hasAuthorship W4383371811A5019400621 @default.
- W4383371811 hasAuthorship W4383371811A5020147975 @default.
- W4383371811 hasAuthorship W4383371811A5022753725 @default.
- W4383371811 hasAuthorship W4383371811A5024261526 @default.
- W4383371811 hasAuthorship W4383371811A5067871430 @default.
- W4383371811 hasConcept C134514944 @default.
- W4383371811 hasConcept C159985019 @default.
- W4383371811 hasConcept C191897082 @default.
- W4383371811 hasConcept C192562407 @default.
- W4383371811 hasConcept C20625102 @default.
- W4383371811 hasConcept C2776230739 @default.
- W4383371811 hasConcept C6648577 @default.
- W4383371811 hasConceptScore W4383371811C134514944 @default.
- W4383371811 hasConceptScore W4383371811C159985019 @default.
- W4383371811 hasConceptScore W4383371811C191897082 @default.
- W4383371811 hasConceptScore W4383371811C192562407 @default.
- W4383371811 hasConceptScore W4383371811C20625102 @default.
- W4383371811 hasConceptScore W4383371811C2776230739 @default.
- W4383371811 hasConceptScore W4383371811C6648577 @default.
- W4383371811 hasLocation W43833718111 @default.
- W4383371811 hasOpenAccess W4383371811 @default.
- W4383371811 hasPrimaryLocation W43833718111 @default.
- W4383371811 hasRelatedWork W2121036907 @default.
- W4383371811 hasRelatedWork W2137307547 @default.
- W4383371811 hasRelatedWork W2167517449 @default.
- W4383371811 hasRelatedWork W2380293314 @default.
- W4383371811 hasRelatedWork W2610509641 @default.
- W4383371811 hasRelatedWork W2941595404 @default.
- W4383371811 hasRelatedWork W2943188944 @default.
- W4383371811 hasRelatedWork W3082440218 @default.
- W4383371811 hasRelatedWork W3097783663 @default.
- W4383371811 hasRelatedWork W4366262926 @default.
- W4383371811 hasVolume "963" @default.
- W4383371811 isParatext "false" @default.
- W4383371811 isRetracted "false" @default.
- W4383371811 workType "article" @default.