- W4385345993 abstract "Novel Ti/Al laminated composite embedded with particles of the high entropy alloy Al0.5CoCrFeNi were produced by vacuum hot press sintering at 650°C. The microstructure of the laminated composite was investigated using XRD, SEM, EDS, TEM and EBSD techniques. It was found that a thin layer of Al3Ti was formed at the Ti/Al interface. There were no obvious defects between the Al0.5CoCrFeNi particles and Al matrix, achieving a good interfacial bond. The tensile properties of the material were tested at room temperature. The results of the tensile test indicated that the material exhibited an elongation to failure of 59% and an average tensile strength of 240 MPa, demonstrating excellent plastic deformation capability. During the tensile process, the expansion of fractures and cracks in Al0.5CoCrFeNi particles can consume energy, which helps to improve the material’s ability to undergo plastic deformation. Based on the morphologies of tensile fracture, it has been observed that the fracture surface of high entropy alloys exhibits a mixed fracture mode consisting of both brittle and plastic fracture. The brittle BCC phase has been identified as the main cause of cracking in HEA. Ultimately, the material fractures due to necking." @default.
- W4385345993 created "2023-07-29" @default.
- W4385345993 creator A5005244980 @default.
- W4385345993 creator A5018679708 @default.
- W4385345993 creator A5030740444 @default.
- W4385345993 creator A5040990429 @default.
- W4385345993 creator A5045602727 @default.
- W4385345993 creator A5064569232 @default.
- W4385345993 creator A5072993972 @default.
- W4385345993 creator A5083983639 @default.
- W4385345993 creator A5023353093 @default.
- W4385345993 date "2023-07-28" @default.
- W4385345993 modified "2023-09-24" @default.
- W4385345993 title "Microstructure and tensile properties of high-entropy alloy Al<sub>0.5</sub>CoCrFeNi particles reinforced Ti/Al laminated composite" @default.
- W4385345993 cites W1966594162 @default.
- W4385345993 cites W1975787260 @default.
- W4385345993 cites W2002730540 @default.
- W4385345993 cites W2010626550 @default.
- W4385345993 cites W2057638952 @default.
- W4385345993 cites W2066675582 @default.
- W4385345993 cites W2070197891 @default.
- W4385345993 cites W2076328975 @default.
- W4385345993 cites W2080821150 @default.
- W4385345993 cites W2085427474 @default.
- W4385345993 cites W2097591653 @default.
- W4385345993 cites W2168686241 @default.
- W4385345993 cites W2174258863 @default.
- W4385345993 cites W2182786315 @default.
- W4385345993 cites W2310157210 @default.
- W4385345993 cites W2532828627 @default.
- W4385345993 cites W2553827735 @default.
- W4385345993 cites W2560349458 @default.
- W4385345993 cites W2560724998 @default.
- W4385345993 cites W2780485163 @default.
- W4385345993 cites W2788391186 @default.
- W4385345993 cites W2802183918 @default.
- W4385345993 cites W2807192081 @default.
- W4385345993 cites W2951535627 @default.
- W4385345993 cites W2972374259 @default.
- W4385345993 cites W3004823109 @default.
- W4385345993 cites W3019842067 @default.
- W4385345993 cites W3046580001 @default.
- W4385345993 cites W3164669417 @default.
- W4385345993 cites W3185576805 @default.
- W4385345993 cites W4200422739 @default.
- W4385345993 cites W4280591147 @default.
- W4385345993 cites W4296220165 @default.
- W4385345993 cites W4296335772 @default.
- W4385345993 cites W4296657970 @default.
- W4385345993 cites W4302027608 @default.
- W4385345993 cites W4361191589 @default.
- W4385345993 cites W4366385161 @default.
- W4385345993 doi "https://doi.org/10.1080/09276440.2023.2240567" @default.
- W4385345993 hasPublicationYear "2023" @default.
- W4385345993 type Work @default.
- W4385345993 citedByCount "0" @default.
- W4385345993 crossrefType "journal-article" @default.
- W4385345993 hasAuthorship W4385345993A5005244980 @default.
- W4385345993 hasAuthorship W4385345993A5018679708 @default.
- W4385345993 hasAuthorship W4385345993A5023353093 @default.
- W4385345993 hasAuthorship W4385345993A5030740444 @default.
- W4385345993 hasAuthorship W4385345993A5040990429 @default.
- W4385345993 hasAuthorship W4385345993A5045602727 @default.
- W4385345993 hasAuthorship W4385345993A5064569232 @default.
- W4385345993 hasAuthorship W4385345993A5072993972 @default.
- W4385345993 hasAuthorship W4385345993A5083983639 @default.
- W4385345993 hasConcept C104779481 @default.
- W4385345993 hasConcept C112950240 @default.
- W4385345993 hasConcept C119001679 @default.
- W4385345993 hasConcept C136478896 @default.
- W4385345993 hasConcept C159985019 @default.
- W4385345993 hasConcept C182508753 @default.
- W4385345993 hasConcept C192562407 @default.
- W4385345993 hasConcept C2780026712 @default.
- W4385345993 hasConcept C87976508 @default.
- W4385345993 hasConceptScore W4385345993C104779481 @default.
- W4385345993 hasConceptScore W4385345993C112950240 @default.
- W4385345993 hasConceptScore W4385345993C119001679 @default.
- W4385345993 hasConceptScore W4385345993C136478896 @default.
- W4385345993 hasConceptScore W4385345993C159985019 @default.
- W4385345993 hasConceptScore W4385345993C182508753 @default.
- W4385345993 hasConceptScore W4385345993C192562407 @default.
- W4385345993 hasConceptScore W4385345993C2780026712 @default.
- W4385345993 hasConceptScore W4385345993C87976508 @default.
- W4385345993 hasFunder F4320321001 @default.
- W4385345993 hasFunder F4320322769 @default.
- W4385345993 hasFunder F4320323085 @default.
- W4385345993 hasLocation W43853459931 @default.
- W4385345993 hasOpenAccess W4385345993 @default.
- W4385345993 hasPrimaryLocation W43853459931 @default.
- W4385345993 hasRelatedWork W1976966962 @default.
- W4385345993 hasRelatedWork W1994380574 @default.
- W4385345993 hasRelatedWork W1994805729 @default.
- W4385345993 hasRelatedWork W2010733322 @default.
- W4385345993 hasRelatedWork W2123155170 @default.
- W4385345993 hasRelatedWork W2358581418 @default.
- W4385345993 hasRelatedWork W2375443292 @default.
- W4385345993 hasRelatedWork W2379855728 @default.