- W4385652178 abstract "Acquiring high-performance calcium phosphate (CaP) ceramics via 3D printing is critical for their applications in bone regenerative repair. In current study, a complete process study of 3D printed CaP ceramics based on digital light processing (DLP) technology was performed to get the ideal implant for the regenerative repair of calvarial defects. The smaller particle size of initial powder would be more favorable to getting slurry with high solid content and low viscosity. CaP green body with high precision and high curing rate could be fabricated at the exposure energy density and exposure time of 6.20 mJ cm−2 and 2 s, respectively. Moreover, the post-curing treatment could eliminate the interlayer cracks and increase the curing rate from 69.78% to 93.91% of green body. After that, the mechanical strength of CaP ceramics increased by 46.34%. In-vitro cellular experiments showed that 3D printed CaP ceramics had good biocompatibility, and could promote the osteoblastic differentiation of BMSCs. In-vivo rat cranial defect implantation revealed 3D printed CaP ceramics exhibited better osteogenic ability than the commercial ones (BAM®), reaching the close level with the autografts. Overall, this study could provide a closed-loop solution for 3D printed CaP ceramics with high-precision and low-defect to induce bone regeneration." @default.
- W4385652178 created "2023-08-09" @default.
- W4385652178 creator A5025405141 @default.
- W4385652178 creator A5032313846 @default.
- W4385652178 creator A5033667355 @default.
- W4385652178 creator A5050407938 @default.
- W4385652178 creator A5067003794 @default.
- W4385652178 creator A5076340145 @default.
- W4385652178 creator A5079170742 @default.
- W4385652178 creator A5089236349 @default.
- W4385652178 creator A5091791565 @default.
- W4385652178 date "2023-09-01" @default.
- W4385652178 modified "2023-10-17" @default.
- W4385652178 title "Optimized fabrication of DLP-based 3D printing calcium phosphate ceramics with high-precision and low-defect to induce calvarial defect regeneration" @default.
- W4385652178 cites W1969224318 @default.
- W4385652178 cites W1974542383 @default.
- W4385652178 cites W2008277897 @default.
- W4385652178 cites W2029253255 @default.
- W4385652178 cites W2052986265 @default.
- W4385652178 cites W2085765714 @default.
- W4385652178 cites W2142508865 @default.
- W4385652178 cites W2165077305 @default.
- W4385652178 cites W2339169747 @default.
- W4385652178 cites W2521867133 @default.
- W4385652178 cites W2562843154 @default.
- W4385652178 cites W2639701622 @default.
- W4385652178 cites W2680926619 @default.
- W4385652178 cites W2753782603 @default.
- W4385652178 cites W2794041576 @default.
- W4385652178 cites W2801083616 @default.
- W4385652178 cites W2888566393 @default.
- W4385652178 cites W2892208067 @default.
- W4385652178 cites W2895936594 @default.
- W4385652178 cites W2898525848 @default.
- W4385652178 cites W2905174742 @default.
- W4385652178 cites W2953743301 @default.
- W4385652178 cites W2975186898 @default.
- W4385652178 cites W2981847431 @default.
- W4385652178 cites W2996856075 @default.
- W4385652178 cites W3025284451 @default.
- W4385652178 cites W3033458991 @default.
- W4385652178 cites W3034153390 @default.
- W4385652178 cites W3041151187 @default.
- W4385652178 cites W3048944495 @default.
- W4385652178 cites W3090026992 @default.
- W4385652178 cites W3092410316 @default.
- W4385652178 cites W3108055321 @default.
- W4385652178 cites W3113898787 @default.
- W4385652178 cites W3150592967 @default.
- W4385652178 cites W3154772949 @default.
- W4385652178 cites W3155597318 @default.
- W4385652178 cites W3179832019 @default.
- W4385652178 cites W3193918535 @default.
- W4385652178 cites W3194048522 @default.
- W4385652178 cites W3199037531 @default.
- W4385652178 cites W3204982151 @default.
- W4385652178 cites W3216149905 @default.
- W4385652178 cites W3217369645 @default.
- W4385652178 cites W4210510898 @default.
- W4385652178 cites W4210772982 @default.
- W4385652178 cites W4214642637 @default.
- W4385652178 cites W4221088651 @default.
- W4385652178 cites W4280549287 @default.
- W4385652178 cites W4281684497 @default.
- W4385652178 cites W4281701862 @default.
- W4385652178 cites W4282929788 @default.
- W4385652178 cites W4282939336 @default.
- W4385652178 cites W4282984254 @default.
- W4385652178 cites W4283517465 @default.
- W4385652178 cites W4291158182 @default.
- W4385652178 doi "https://doi.org/10.1016/j.matdes.2023.112230" @default.
- W4385652178 hasPublicationYear "2023" @default.
- W4385652178 type Work @default.
- W4385652178 citedByCount "0" @default.
- W4385652178 crossrefType "journal-article" @default.
- W4385652178 hasAuthorship W4385652178A5025405141 @default.
- W4385652178 hasAuthorship W4385652178A5032313846 @default.
- W4385652178 hasAuthorship W4385652178A5033667355 @default.
- W4385652178 hasAuthorship W4385652178A5050407938 @default.
- W4385652178 hasAuthorship W4385652178A5067003794 @default.
- W4385652178 hasAuthorship W4385652178A5076340145 @default.
- W4385652178 hasAuthorship W4385652178A5079170742 @default.
- W4385652178 hasAuthorship W4385652178A5089236349 @default.
- W4385652178 hasAuthorship W4385652178A5091791565 @default.
- W4385652178 hasBestOaLocation W43856521781 @default.
- W4385652178 hasConcept C132976073 @default.
- W4385652178 hasConcept C134132462 @default.
- W4385652178 hasConcept C136229726 @default.
- W4385652178 hasConcept C136525101 @default.
- W4385652178 hasConcept C142724271 @default.
- W4385652178 hasConcept C159985019 @default.
- W4385652178 hasConcept C191897082 @default.
- W4385652178 hasConcept C192562407 @default.
- W4385652178 hasConcept C204787440 @default.
- W4385652178 hasConcept C2776865275 @default.
- W4385652178 hasConcept C2777230088 @default.
- W4385652178 hasConcept C3019308078 @default.
- W4385652178 hasConcept C31972630 @default.