- W4385728138 abstract "The microstructure and mechanical properties of Al14Co41Cr15Fe10Ni20 high entropy alloy is investigated in this work. Both the as-cast and homogenized (1200 °C/20 hours) alloys show a dual phase microstructure consisting from a dendritic solid solution FCC phase and an interdendritic B2 (BCC) phase. Aging treatments in the temperature range of 750 °C-1000 °C were applied on samples for 20 hours. Uniform distribution of precipitates in both dendritic and interdendritic regions were observed after performing the aging treatments. It is observed that with increasing the aging temperature from 750 °C to 1000 °C, the size of precipitates increases and the hardness of alloys decreases due to over-aging. The aged alloy with optimized hardness was selected for further room temperature and high temperature tensile tests. The results of mechanical tests indicate that the room temperature mechanical properties of the investigated alloy are comparable to the mechanical properties of commercial Co-based alloys, although the high temperature ductility of the alloy is very poor in comparison with commercial alloys. The obtained results in this work could be used for the further development of high entropy alloys with dual phase FCC/B2 microstructures." @default.
- W4385728138 created "2023-08-11" @default.
- W4385728138 creator A5005395572 @default.
- W4385728138 creator A5038317102 @default.
- W4385728138 creator A5076895919 @default.
- W4385728138 date "2023-09-01" @default.
- W4385728138 modified "2023-10-17" @default.
- W4385728138 title "Effect of heat treatment on the microstructure and mechanical properties of a dual phase Al14Co41Cr15Fe10Ni20 high entropy alloy" @default.
- W4385728138 cites W1970065157 @default.
- W4385728138 cites W2012041268 @default.
- W4385728138 cites W2018913363 @default.
- W4385728138 cites W2071212235 @default.
- W4385728138 cites W2087945533 @default.
- W4385728138 cites W2096553946 @default.
- W4385728138 cites W2097524443 @default.
- W4385728138 cites W2103109670 @default.
- W4385728138 cites W2222866092 @default.
- W4385728138 cites W2303123259 @default.
- W4385728138 cites W2429758906 @default.
- W4385728138 cites W2512171886 @default.
- W4385728138 cites W2534691303 @default.
- W4385728138 cites W2782471633 @default.
- W4385728138 cites W2792320529 @default.
- W4385728138 cites W2792597153 @default.
- W4385728138 cites W2888064467 @default.
- W4385728138 cites W2973685077 @default.
- W4385728138 cites W2977978921 @default.
- W4385728138 cites W2981612485 @default.
- W4385728138 cites W2984017794 @default.
- W4385728138 cites W3010643808 @default.
- W4385728138 cites W3169352931 @default.
- W4385728138 cites W3170308934 @default.
- W4385728138 cites W3194657185 @default.
- W4385728138 cites W4286253162 @default.
- W4385728138 cites W4289638464 @default.
- W4385728138 cites W4291396200 @default.
- W4385728138 cites W4296220165 @default.
- W4385728138 cites W4296335772 @default.
- W4385728138 cites W4296657970 @default.
- W4385728138 cites W4318773715 @default.
- W4385728138 cites W4361191589 @default.
- W4385728138 doi "https://doi.org/10.1016/j.jmrt.2023.08.071" @default.
- W4385728138 hasPublicationYear "2023" @default.
- W4385728138 type Work @default.
- W4385728138 citedByCount "1" @default.
- W4385728138 crossrefType "journal-article" @default.
- W4385728138 hasAuthorship W4385728138A5005395572 @default.
- W4385728138 hasAuthorship W4385728138A5038317102 @default.
- W4385728138 hasAuthorship W4385728138A5076895919 @default.
- W4385728138 hasBestOaLocation W43857281381 @default.
- W4385728138 hasConcept C112950240 @default.
- W4385728138 hasConcept C149912024 @default.
- W4385728138 hasConcept C159985019 @default.
- W4385728138 hasConcept C178790620 @default.
- W4385728138 hasConcept C185592680 @default.
- W4385728138 hasConcept C191897082 @default.
- W4385728138 hasConcept C192562407 @default.
- W4385728138 hasConcept C2776512210 @default.
- W4385728138 hasConcept C2780026712 @default.
- W4385728138 hasConcept C2780299837 @default.
- W4385728138 hasConcept C44280652 @default.
- W4385728138 hasConcept C87976508 @default.
- W4385728138 hasConceptScore W4385728138C112950240 @default.
- W4385728138 hasConceptScore W4385728138C149912024 @default.
- W4385728138 hasConceptScore W4385728138C159985019 @default.
- W4385728138 hasConceptScore W4385728138C178790620 @default.
- W4385728138 hasConceptScore W4385728138C185592680 @default.
- W4385728138 hasConceptScore W4385728138C191897082 @default.
- W4385728138 hasConceptScore W4385728138C192562407 @default.
- W4385728138 hasConceptScore W4385728138C2776512210 @default.
- W4385728138 hasConceptScore W4385728138C2780026712 @default.
- W4385728138 hasConceptScore W4385728138C2780299837 @default.
- W4385728138 hasConceptScore W4385728138C44280652 @default.
- W4385728138 hasConceptScore W4385728138C87976508 @default.
- W4385728138 hasLocation W43857281381 @default.
- W4385728138 hasOpenAccess W4385728138 @default.
- W4385728138 hasPrimaryLocation W43857281381 @default.
- W4385728138 hasRelatedWork W2058940780 @default.
- W4385728138 hasRelatedWork W2090404944 @default.
- W4385728138 hasRelatedWork W2300939370 @default.
- W4385728138 hasRelatedWork W2312532833 @default.
- W4385728138 hasRelatedWork W2354424856 @default.
- W4385728138 hasRelatedWork W2375093060 @default.
- W4385728138 hasRelatedWork W2609598984 @default.
- W4385728138 hasRelatedWork W2968845083 @default.
- W4385728138 hasRelatedWork W3112534208 @default.
- W4385728138 hasRelatedWork W4213247598 @default.
- W4385728138 hasVolume "26" @default.
- W4385728138 isParatext "false" @default.
- W4385728138 isRetracted "false" @default.
- W4385728138 workType "article" @default.