- W4386003778 abstract "Zn-Mn alloy coatings with small amounts of Mn (Zn-0.19 wt.% Mn, Zn-0.21 wt.% Mn, Zn-0.26 wt.% Mn and Zn-0.34 wt.% Mn) were formed by electrodeposition, onto pre-treated Mg substrates (Mgt) covered with a Zn film (Zn/Mgt). The chemical composition in depth profiles, morphological and structural characteristics of the Zn-Mn coatings on Zn/Mgt (labeled as Zn-Mn/(Zn/Mgt)) were analyzed using Glow Discharge Optical Emission Spectroscopy (GD-OES), Scanning Electron Microscopy/Energy Dispersive X-ray spectroscopy (SEM/EDS), and X-ray diffraction (XRD). When the manganese content was greater than 0.19 wt.%, the results reveal the formation of two Zn-Mn phases: η-ZnMn and ζ-MnZn13; while the formation of the ζ-MnZn13 phase was favored by increasing the Mn content in the alloy. On the other hand, microhardness, wear resistance, and coefficient of friction significantly increase when coating Zn/Mgt substrate with the Zn-Mn alloy. The corrosion performance of this alloy was evaluated by potentiodynamic polarization, and electrochemical impedance spectroscopy (EIS). The degradation rate in Hank's solutions of the pristine Mg substrate (0.29 mm yr-1) decreases due to the Zn-Mn coating. Furthermore, the degradation rate of Zn-Mn was further decreased from 0.051 to 0.022 mm yr-1, by varying the amount of Mn in the Zn-Mn alloy from 0.19 to 0.26 wt.% Mn, respectively. However, the rate of degradation increases up to 0.064 mm yr-1 at higher Mn content, Zn-0.34 wt.% Mn. Therefore, the microhardness, wear volume, and degradation rate of Zn-Mn/(Zn/Mg) in Hank's solution can be modulated by varying the Mn composition in the alloy." @default.
- W4386003778 created "2023-08-20" @default.
- W4386003778 creator A5000346312 @default.
- W4386003778 creator A5007967373 @default.
- W4386003778 creator A5026436801 @default.
- W4386003778 creator A5037208803 @default.
- W4386003778 creator A5040693291 @default.
- W4386003778 creator A5042825894 @default.
- W4386003778 creator A5051203679 @default.
- W4386003778 creator A5056473983 @default.
- W4386003778 creator A5081468877 @default.
- W4386003778 creator A5087900403 @default.
- W4386003778 date "2023-09-01" @default.
- W4386003778 modified "2023-10-18" @default.
- W4386003778 title "Modulating tribological properties and degradation rate in Hank's solution of Zn–Mn alloys electrodeposited on Mg with variable Mn content" @default.
- W4386003778 cites W1966730582 @default.
- W4386003778 cites W1971578189 @default.
- W4386003778 cites W1973602510 @default.
- W4386003778 cites W1981104073 @default.
- W4386003778 cites W1982819273 @default.
- W4386003778 cites W1995743978 @default.
- W4386003778 cites W2007389259 @default.
- W4386003778 cites W2030117018 @default.
- W4386003778 cites W2035783036 @default.
- W4386003778 cites W2047311328 @default.
- W4386003778 cites W2048182182 @default.
- W4386003778 cites W2048890220 @default.
- W4386003778 cites W2050957889 @default.
- W4386003778 cites W2055248506 @default.
- W4386003778 cites W2057197536 @default.
- W4386003778 cites W2072016479 @default.
- W4386003778 cites W2072819674 @default.
- W4386003778 cites W2084498917 @default.
- W4386003778 cites W2094057964 @default.
- W4386003778 cites W2119643055 @default.
- W4386003778 cites W2296360581 @default.
- W4386003778 cites W2307249191 @default.
- W4386003778 cites W2474964860 @default.
- W4386003778 cites W2562927019 @default.
- W4386003778 cites W2585611321 @default.
- W4386003778 cites W2588925600 @default.
- W4386003778 cites W2592963514 @default.
- W4386003778 cites W2604231752 @default.
- W4386003778 cites W2625686903 @default.
- W4386003778 cites W2784282477 @default.
- W4386003778 cites W2789878952 @default.
- W4386003778 cites W2909265295 @default.
- W4386003778 cites W2965676333 @default.
- W4386003778 cites W2999110053 @default.
- W4386003778 cites W3083620031 @default.
- W4386003778 cites W3091589887 @default.
- W4386003778 cites W3102991811 @default.
- W4386003778 cites W3205280089 @default.
- W4386003778 cites W3205909877 @default.
- W4386003778 cites W3208409543 @default.
- W4386003778 cites W3209529515 @default.
- W4386003778 cites W4224771892 @default.
- W4386003778 cites W4286509937 @default.
- W4386003778 cites W4311423197 @default.
- W4386003778 cites W4311692848 @default.
- W4386003778 cites W4328121688 @default.
- W4386003778 cites W882164914 @default.
- W4386003778 doi "https://doi.org/10.1016/j.jmrt.2023.08.147" @default.
- W4386003778 hasPublicationYear "2023" @default.
- W4386003778 type Work @default.
- W4386003778 citedByCount "0" @default.
- W4386003778 crossrefType "journal-article" @default.
- W4386003778 hasAuthorship W4386003778A5000346312 @default.
- W4386003778 hasAuthorship W4386003778A5007967373 @default.
- W4386003778 hasAuthorship W4386003778A5026436801 @default.
- W4386003778 hasAuthorship W4386003778A5037208803 @default.
- W4386003778 hasAuthorship W4386003778A5040693291 @default.
- W4386003778 hasAuthorship W4386003778A5042825894 @default.
- W4386003778 hasAuthorship W4386003778A5051203679 @default.
- W4386003778 hasAuthorship W4386003778A5056473983 @default.
- W4386003778 hasAuthorship W4386003778A5081468877 @default.
- W4386003778 hasAuthorship W4386003778A5087900403 @default.
- W4386003778 hasBestOaLocation W43860037781 @default.
- W4386003778 hasConcept C111368507 @default.
- W4386003778 hasConcept C113196181 @default.
- W4386003778 hasConcept C121332964 @default.
- W4386003778 hasConcept C127313418 @default.
- W4386003778 hasConcept C127413603 @default.
- W4386003778 hasConcept C13965031 @default.
- W4386003778 hasConcept C147438087 @default.
- W4386003778 hasConcept C147789679 @default.
- W4386003778 hasConcept C159985019 @default.
- W4386003778 hasConcept C165720898 @default.
- W4386003778 hasConcept C17525397 @default.
- W4386003778 hasConcept C175708663 @default.
- W4386003778 hasConcept C185592680 @default.
- W4386003778 hasConcept C191897082 @default.
- W4386003778 hasConcept C192562407 @default.
- W4386003778 hasConcept C20625102 @default.
- W4386003778 hasConcept C26771246 @default.
- W4386003778 hasConcept C2777289219 @default.
- W4386003778 hasConcept C2780026712 @default.
- W4386003778 hasConcept C2781448156 @default.