• W4386018830 abstract "Cement-stabilized coral aggregate (CSCA) can be used as a base material for roads and airports, and it is a future direction for island engineering. In this study, four-point bending tests were conducted on notched CSCA beams with different notch depth ratios, and the specimens were monitored using acoustic emission (AE) technology. The ringing count, amplitude, RA value, frequency, and b-value were used to study the bending fracture characteristics of the CSCA material. The results of the study showed that the 28d flexural tensile strength of the CSCA beam was 0.922 MPa when the test loading rate was 0.1 mm/min. The CSCA materials exhibited brittleness during the bending fracture process. The CSCA originally had defects, internal pores, and large-diameter irregular coral aggregates, which caused beam fractures from the weak surface near the loading point. At the stage where the peak force was reduced to approximately 0.2 times the peak force, many cracks in the CSCA formed, extended, and connected, and the beams experienced dense damage. The damage to the CSCA material was dominated by tensile cracks. In the CSCA material, the combined effect of the aggregate and cement paste was enhanced, the strength of the interfacial transition zone was increased, and the strength of the aggregate was weakened compared with that of cement-stabilized macadam material. The fracture process of the CSCA material was accompanied by the destruction of the interface and fracture of the aggregate particles." @default.
• W4386018830 created "2023-08-22" @default.
• W4386018830 creator A5009734634 @default.
• W4386018830 creator A5035543428 @default.
• W4386018830 creator A5042954417 @default.
• W4386018830 creator A5049111889 @default.
• W4386018830 creator A5057239216 @default.
• W4386018830 creator A5074881336 @default.
• W4386018830 creator A5085310269 @default.
• W4386018830 creator A5086770241 @default.
• W4386018830 date "2023-10-01" @default.
• W4386018830 modified "2023-10-02" @default.
• W4386018830 title "Identification of bending fracture characteristics of cement-stabilized coral aggregate in four-point bending tests based on acoustic emission" @default.
• W4386018830 cites W2035216734 @default.
• W4386018830 cites W2079135474 @default.
• W4386018830 cites W2088256487 @default.
• W4386018830 cites W2092811014 @default.
• W4386018830 cites W2093396074 @default.
• W4386018830 cites W2310111665 @default.
• W4386018830 cites W2475173732 @default.
• W4386018830 cites W2600030842 @default.
• W4386018830 cites W2738687897 @default.
• W4386018830 cites W2739548870 @default.
• W4386018830 cites W2886777772 @default.
• W4386018830 cites W2919002275 @default.
• W4386018830 cites W2958413160 @default.
• W4386018830 cites W2958437613 @default.
• W4386018830 cites W2981106442 @default.
• W4386018830 cites W2981800040 @default.
• W4386018830 cites W2990455797 @default.
• W4386018830 cites W3047574255 @default.
• W4386018830 cites W3083633332 @default.
• W4386018830 cites W3085164611 @default.
• W4386018830 cites W3111048459 @default.
• W4386018830 cites W3114119573 @default.
• W4386018830 cites W3118205326 @default.
• W4386018830 cites W3124547747 @default.
• W4386018830 cites W3128017409 @default.
• W4386018830 cites W3157708595 @default.
• W4386018830 cites W3176332802 @default.
• W4386018830 cites W3187565486 @default.
• W4386018830 cites W3205452777 @default.
• W4386018830 cites W3213625505 @default.
• W4386018830 cites W4200423725 @default.
• W4386018830 cites W4206999357 @default.
• W4386018830 cites W4213152373 @default.
• W4386018830 cites W4225015816 @default.
• W4386018830 cites W4246324802 @default.
• W4386018830 cites W4280544474 @default.
• W4386018830 cites W4293412472 @default.
• W4386018830 cites W4307957984 @default.
• W4386018830 cites W4318465470 @default.
• W4386018830 cites W4318996905 @default.
• W4386018830 doi "https://doi.org/10.1016/j.conbuildmat.2023.132999" @default.
• W4386018830 hasPublicationYear "2023" @default.
• W4386018830 type Work @default.
• W4386018830 citedByCount "0" @default.
• W4386018830 crossrefType "journal-article" @default.
• W4386018830 hasAuthorship W4386018830A5009734634 @default.
• W4386018830 hasAuthorship W4386018830A5035543428 @default.
• W4386018830 hasAuthorship W4386018830A5042954417 @default.
• W4386018830 hasAuthorship W4386018830A5049111889 @default.
• W4386018830 hasAuthorship W4386018830A5057239216 @default.
• W4386018830 hasAuthorship W4386018830A5074881336 @default.
• W4386018830 hasAuthorship W4386018830A5085310269 @default.
• W4386018830 hasAuthorship W4386018830A5086770241 @default.
• W4386018830 hasConcept C112950240 @default.
• W4386018830 hasConcept C127413603 @default.
• W4386018830 hasConcept C136478896 @default.
• W4386018830 hasConcept C159985019 @default.
• W4386018830 hasConcept C168834538 @default.
• W4386018830 hasConcept C178405089 @default.
• W4386018830 hasConcept C192562407 @default.
• W4386018830 hasConcept C43369102 @default.
• W4386018830 hasConcept C4679612 @default.
• W4386018830 hasConcept C523993062 @default.
• W4386018830 hasConcept C66938386 @default.
• W4386018830 hasConcept C86060186 @default.
• W4386018830 hasConcept C87210426 @default.
• W4386018830 hasConceptScore W4386018830C112950240 @default.
• W4386018830 hasConceptScore W4386018830C127413603 @default.
• W4386018830 hasConceptScore W4386018830C136478896 @default.
• W4386018830 hasConceptScore W4386018830C159985019 @default.
• W4386018830 hasConceptScore W4386018830C168834538 @default.
• W4386018830 hasConceptScore W4386018830C178405089 @default.
• W4386018830 hasConceptScore W4386018830C192562407 @default.
• W4386018830 hasConceptScore W4386018830C43369102 @default.
• W4386018830 hasConceptScore W4386018830C4679612 @default.
• W4386018830 hasConceptScore W4386018830C523993062 @default.
• W4386018830 hasConceptScore W4386018830C66938386 @default.
• W4386018830 hasConceptScore W4386018830C86060186 @default.
• W4386018830 hasConceptScore W4386018830C87210426 @default.
• W4386018830 hasFunder F4320321540 @default.
• W4386018830 hasFunder F4320335777 @default.
• W4386018830 hasLocation W43860188301 @default.
• W4386018830 hasOpenAccess W4386018830 @default.
• W4386018830 hasPrimaryLocation W43860188301 @default.
• W4386018830 hasRelatedWork W2056068419 @default.

• next