- W4386120489 endingPage "88" @default.
- W4386120489 startingPage "82" @default.
- W4386120489 abstract "The subject of the research is the influence of low-pressure cold spraying process parameters on the adhesive strength of the coatings. The goal is to ensure the maximum values of the adhesive strength of nickel-based coatings deposited by cold spraying by controlling the gas temperature at the nozzle inlet. The task is to investigate the effect of the temperature mode of the DYMET-405 machine on the adhesive strength of the coatings obtained from the Ni+Zn+Al2O3 powder mixture at constant other spraying parameters. Research methods. The experimental study of the adhesive strength was conducted on the tear using adhesive method in accordance with DSTU 2639-94. The metal-matrix composite powder mixture Ni+Zn+Al2O3 was used as powder material. VT3-1 titanium alloy was chosen as substrate material. Coatings were deposited using DYMET-405 low-pressure cold spraying machine. Temperature regulation at the nozzle inlet was performed by turning on the required temperature mode on the equipment control panel. Other spraying parameters remained constant during coating deposition process. The results. It was established that with an increase in the temperature of the gas in the nozzle, an increase in the adhesive strength of coatings is observed, on average from 9.5 MPa to 28.7 MPa. This can be explained by the fact that an increase in gas temperature leads to an increase in the velocity of the gas flow and, accordingly, of the powder particles in this flow. Higher particle impact velocity has a positive effect on the process of their deforming, filling of pores, densifying of coating layers, and finally increasing the adhesive and cohesive strength. The scientific novelty of the obtained results is that the dependence of the gas temperature at the nozzle inlet during low-pressure cold spraying on the adhesive strength of Ni+Zn+Al2O3 powder mixture coatings deposited on VT3-1 titanium alloy substrates was obtained. Conclusions. The practical value of the obtained results is that the obtained dependences of adhesive strength on gas temperature can be used for the development of cold spraying recommendations for the deposition of restorative coatings on parts made of titanium alloys, in particular in aircraft engines to eliminate operational defects." @default.
- W4386120489 created "2023-08-25" @default.
- W4386120489 creator A5037552225 @default.
- W4386120489 creator A5049304871 @default.
- W4386120489 creator A5052264320 @default.
- W4386120489 creator A5067463571 @default.
- W4386120489 date "2023-08-24" @default.
- W4386120489 modified "2023-10-17" @default.
- W4386120489 title "Дослідження впливу температури газу процесу холодного газодинамічного напилювання на адгезійну міцність нікелевмісних покриттів" @default.
- W4386120489 doi "https://doi.org/10.32620/aktt.2023.4sup2.11" @default.
- W4386120489 hasPublicationYear "2023" @default.
- W4386120489 type Work @default.
- W4386120489 citedByCount "0" @default.
- W4386120489 crossrefType "journal-article" @default.
- W4386120489 hasAuthorship W4386120489A5037552225 @default.
- W4386120489 hasAuthorship W4386120489A5049304871 @default.
- W4386120489 hasAuthorship W4386120489A5052264320 @default.
- W4386120489 hasAuthorship W4386120489A5067463571 @default.
- W4386120489 hasBestOaLocation W43861204891 @default.
- W4386120489 hasConcept C104779481 @default.
- W4386120489 hasConcept C121332964 @default.
- W4386120489 hasConcept C147789679 @default.
- W4386120489 hasConcept C151730666 @default.
- W4386120489 hasConcept C159985019 @default.
- W4386120489 hasConcept C185592680 @default.
- W4386120489 hasConcept C187530423 @default.
- W4386120489 hasConcept C191897082 @default.
- W4386120489 hasConcept C192562407 @default.
- W4386120489 hasConcept C202752663 @default.
- W4386120489 hasConcept C2779227376 @default.
- W4386120489 hasConcept C2781448156 @default.
- W4386120489 hasConcept C2816523 @default.
- W4386120489 hasConcept C56200935 @default.
- W4386120489 hasConcept C64297162 @default.
- W4386120489 hasConcept C68928338 @default.
- W4386120489 hasConcept C86803240 @default.
- W4386120489 hasConcept C97355855 @default.
- W4386120489 hasConceptScore W4386120489C104779481 @default.
- W4386120489 hasConceptScore W4386120489C121332964 @default.
- W4386120489 hasConceptScore W4386120489C147789679 @default.
- W4386120489 hasConceptScore W4386120489C151730666 @default.
- W4386120489 hasConceptScore W4386120489C159985019 @default.
- W4386120489 hasConceptScore W4386120489C185592680 @default.
- W4386120489 hasConceptScore W4386120489C187530423 @default.
- W4386120489 hasConceptScore W4386120489C191897082 @default.
- W4386120489 hasConceptScore W4386120489C192562407 @default.
- W4386120489 hasConceptScore W4386120489C202752663 @default.
- W4386120489 hasConceptScore W4386120489C2779227376 @default.
- W4386120489 hasConceptScore W4386120489C2781448156 @default.
- W4386120489 hasConceptScore W4386120489C2816523 @default.
- W4386120489 hasConceptScore W4386120489C56200935 @default.
- W4386120489 hasConceptScore W4386120489C64297162 @default.
- W4386120489 hasConceptScore W4386120489C68928338 @default.
- W4386120489 hasConceptScore W4386120489C86803240 @default.
- W4386120489 hasConceptScore W4386120489C97355855 @default.
- W4386120489 hasIssue "4sup2" @default.
- W4386120489 hasLocation W43861204891 @default.
- W4386120489 hasOpenAccess W4386120489 @default.
- W4386120489 hasPrimaryLocation W43861204891 @default.
- W4386120489 hasRelatedWork W1982945099 @default.
- W4386120489 hasRelatedWork W2001108138 @default.
- W4386120489 hasRelatedWork W2005496670 @default.
- W4386120489 hasRelatedWork W2054113325 @default.
- W4386120489 hasRelatedWork W2134108492 @default.
- W4386120489 hasRelatedWork W2373555045 @default.
- W4386120489 hasRelatedWork W2996028150 @default.
- W4386120489 hasRelatedWork W3048672776 @default.
- W4386120489 hasRelatedWork W4200419002 @default.
- W4386120489 hasRelatedWork W4376873503 @default.
- W4386120489 isParatext "false" @default.
- W4386120489 isRetracted "false" @default.
- W4386120489 workType "article" @default.